Abstract: In a first aspect, the present disclosure provides a method for making an inorganic thermoset resin, the method comprising: (a) mixing SiO2, H2O and a metallic hydroxide for generating an alkaline aqueous solution with pH from 10 to 14 comprising a metallic silicate, wherein said metallic hydroxide generates a first metallic oxide in the aqueous solution, (b) adding aluminum oxide (Al2O3) and silicon oxide (SiO2) to the alkaline aqueous solution comprising a metallic silicate generated in step (a) and (c) adding halloysite nanotubes (Al2Si2O5(OH)4) to the solution generated in step (b). The present disclosure further provides an inorganic thermoset resin obtainable by the method as defined in the first aspect of the disclosure.

Abstract: A method for a curing cycle of an inorganic thermoset resin, the method comprising: (a) adding a hardener in a concentration from 18 to 30% by weight of the resin to said inorganic thermoset resin and (b) curing the resin at a temperature from 110 to 120° C. An inorganic thermoset resin, comprising a hardener in a concentration from 18 to 30% by weight of the resin. A vehicle interior panel, comprising a composite comprising a composite matrix of a natural fibre set within an inorganic thermoset resin.

Abstract: In a first aspect, the present disclosure provides a method for making an inorganic thermoset resin, the method comprising: (a) mixing SiO2, H2O and a metallic hydroxide for generating an alkaline aqueous solution with pH from 10 to 14 comprising a metallic silicate, wherein said metallic hydroxide generates a first metallic oxide in the aqueous solution, (b) adding aluminum oxide (Al2O3) and silicon oxide (SiO2) to the alkaline aqueous solution comprising a metallic silicate generated in step (a) and (c) adding halloysite nanotubes (Al2Si2O5(OH)4) to the solution generated in step (b). The present disclosure further provides an inorganic thermoset resin obtainable by the method as defined in the first aspect of the disclosure.

Abstract: In a first aspect, the present disclosure provides a method for making an inorganic thermoset resin, the method comprising: (a) mixing SiO2, H2O and a metallic hydroxide for generating an alkaline aqueous solution with pH from 10 to 14 comprising a metallic silicate, wherein said metallic hydroxide generates a first metallic oxide in the aqueous solution, (b) adding aluminum oxide (Al2O3) and silicon oxide (SiO2) to the alkaline aqueous solution comprising a metallic silicate generated in step (a) and (c) adding halloysite nanotubes (Al2Si2O5(OH)4) to the solution generated in step (b). The present disclosure further provides an inorganic thermoset resin obtainable by the method as defined in the first aspect of the disclosure.

Abstract: A method for a curing cycle of an inorganic thermoset resin, the method comprising: (a) adding a hardener in a concentration from 18 to 30% by weight of the resin to said inorganic thermoset resin and (b) curing the resin at a temperature from 110 to 120° C. An inorganic thermoset resin, comprising a hardener in a concentration from 18 to 30% by weight of the resin. A vehicle interior panel, comprising a composite comprising a composite matrix of a natural fibre set within an inorganic thermoset resin.

Abstract: In a first aspect, the present disclosure provides a method for making an inorganic thermoset resin, the method comprising: (a) mixing SiO2, H2O and a metallic hydroxide for generating an alkaline aqueous solution with pH from 10 to 14 comprising a metallic silicate, wherein said metallic hydroxide generates a first metallic oxide in the aqueous solution, (b) adding aluminum oxide (Al2O3) and silicon oxide (SiO2) to the alkaline aqueous solution comprising a metallic silicate generated in step (a) and (c) adding halloysite nanotubes (Al2Si2O5(OH)4) to the solution generated in step (b). The present disclosure further provides an inorganic thermoset resin obtainable by the method as defined in the first aspect of the disclosure.