Abstract: The present invention relates to a polyethylene composition comprising, a base resin (A) comprising a copolymer of ethylene and at least one comonomer selected from alpha-olefins having from three to twelve carbon atoms, wherein the ethylene copolymer comprises a low molecular weight component (A-1) and a high molecular weight component (A-2) with the low molecular weight component (A-1) having a lower weight average molecular weight than the high molecular weight component (A-2), (B) carbon black in an amount of 1.0 to 10 wt % based on the total amount of the polyethylene composition, and (C) optional further additives other than carbon black; wherein the low molecular weight component (A-1) has a melt flow rate MFR2 (190° C., 2.

Abstract: The present invention relates to a polyethylene composition comprising —a base resin comprising (A) a first ethylene homo- or copolymer component having a melt flow rate MFR2 (2.16 kg, 190° C.) of equal to or more than 130 g/10 min to equal to or less than 300 g/10 min, determined according to ISO 1133, and (B) a second ethylene homo- or copolymer component, —optional carbon black, —optional further polymer component(s) different to the first ethylene homo- or copolymer components (A) and (B), and —optional additive(s); wherein the first ethylene homo- or copolymer component (A) has a lower weight average molecular weight as the second ethylene homo- or copolymer component (B); the polyethylene composition has a melt flow rate MFR5 (5 kg, 190° C.) of more than 0.60 g/10 min to less than 1.00 g/10 min, determined according to ISO 1133, and a shear thinning index SHI2.7/210 of equal to or more than 10 to equal to or less than 27.