Abstract: A nuclear fuel includes uranium(IV) oxide (UO2) and manganese (Mn) as a dopant. The Mn dopant may be present in the fuel in an amount up to the solubility limit for Mn under a given set of conditions, for example, about 0.01 wt % to about 1 wt %. The nuclear fuel is substantially free of aluminum (Al). The nuclear fuel exhibits enhanced grain size development during sintering temperatures as low at 1400 K due to an increase in uranium sub-lattice vacancies induced by dissolution of the Mn dopant at interstitial defect sites. The Mn-doped nuclear fuel exhibits improved grain sizes at lower temperatures compared to Cr-, Al-, and undoped UO2, and therefore desirably exhibits lower fission gas release and higher plasticity, reducing the chances of fuel rod failure.