Abstract: Strained layer single or multiple quantum well lasers include an InP substrate, a pair of lattice-matched InGaAsP quarternary layers epitaxially grown on the substrate surrounding a pair of lattice matched In.sub.0.53 Ga.sub.0.47 As ternary layers surrounding one or more strained active layers of epitaxially grown, lattice-mismatched In.sub.0.75 Ga.sub.0.25 As. The level of strain is selected to control the bandgap energy to produce laser output having a wavelength in the range of 1.6 to 2.5 .mu.m. The multiple quantum well structure uses between each active layer. Diethyl zinc is used for p-type dopant in an InP cladding layer at a concentration level in the range of about 5.times.10.sup.17 /cm.sup.3 to about 2.times.10.sup.18 /cm.sup.3.