Abstract: A sintered cemented carbide insert for mining or cutting applications includes a mean WC grain size of between 0.8-18 ?m, a binder phase in a weight between 4-18 wt %, a gamma phase with the cubic gamma phase precursors in a weight of between 0.8-10 wt %, and any unavoidable impurities and a balance of WC. A difference between the hardness at any point 0.3 mm from the surface of the insert and the hardness of the bulk is at least 25 HV3, wherein hardness is measured according to ISO EN6507. A method of producing the cemented carbide is also provided.

Abstract: A rock drill button having a body of sintered cemented carbide that has hard constituents of tungsten carbide (WC) in a binder phase of Co, wherein the cemented carbide has 4-12 mass % Co and balance WC and unavoidable impurities. The cemented carbide also has Cr in such an amount that the Cr/Co ratio is within the range of 0.043-0.19, and that the WC grain size mean value is above 1.75 ?m.

Abstract: A rock drill button having a body of sintered cemented carbide that has hard constituents of tungsten carbide (WC) in a binder phase of Co, wherein the cemented carbide has 4-12 mass % Co and balance WC and unavoidable impurities. The cemented carbide also has Cr in such an amount that the Cr/Co ratio is within the range of 0.043-0.19, and that the WC grain size mean value is above 1.75 ?m.

Abstract: The present invention relates to a cutting tool insert for parting, grooving and threading in steel and stainless steels comprising a substrate and a coating. The substrate comprises WC, from about 7.5 to about 10.5 wt-% Co, from about 0.7 to about 1.1 wt-% Cr and from about 100 to about 300 ppm Ti. Ti may partly be replaced by Ta to a weight ratio Ti/Ta of equal to or more than about 0.8. The coating comprises two (Ti,Al)N-layers with different Al/Ti-ratios: an inner AlyTi1-yN-layer with y equals from about 0.4 to about 0.67 with a thickness of from about 0.3 to about 2.5 ?m and an outer AlwT1-wN layer with w equals from about 0.15 to about 0.35 with a thickness of from about 0.5 to about 5.0 ?m.

Abstract: The present invention relates to a cutting insert particularly useful for turning in heat resistant super alloys and stainless steels comprising a substrate and a coating. The substrate comprises WC from about 5 to about 7 wt-% Co and from about 0.15 to about 0.60 wt-% TaC and from about 0.10 to about 0.50 wt-% NbC and balance WC, has a coercivity of from about 19.5 to about 24.5 kA/m and a CW-ratio between from about 0.85 to about 1.00. The coating comprises a homogeneous AlxTi1-xN-layer with x=from about 0.6 to about 0.7 and a thickness of greater than about 1 ?m but less than about 3.8 ?m.

Abstract: The present invention relates to a cutting tool insert particularly for turning of steel comprising a cemented carbide body, a coating with a post treatment with a first, innermost layer system of one or several layers of TiCxNyOz with x+y+z?1 with a total thickness of 0.7–4.5 ?m a second multilayer system consisting of a totally 5–31 alternating Al2O3 and TiCxNyOz (x+y+z?1), preferably ?-Al2O3 and TiN, the Al2O3-layers having an individual layer thickness of <0.5 ?m and the TiCxNyOz-layers 0.01–0.2 ?m with a total thickness of the multilayer of 1.0–4.0 ?m. The multilayer is exposed along the edge line and into the rake and flank face, at least 0.02 mm, from the edge line on the rake face, preferably the contact length of the chip at most 0.9 mm, and 0.02–0.20 mm on the flank face.

Abstract: The present invention relates to a cutting tool insert particularly for turning of steel comprising a cemented carbide body, a coating with a post treatment with

Abstract: Coated milling insert has a WC—Co cemented carbide with a low content of cubic carbides and a highly W-alloyed binder phase and a coating including an inner layer of TiCxNy with columnar grains followed by a layer of &kgr;-Al2O3 and a top layer of TiN. The coated milling insert is particularly useful for milling of grey cast iron with or without cast skin under wet conditions at low and moderate cutting speeds and milling of nodular cast iron and compacted graphite iron with or without cast skin under wet conditions at moderate cutting speeds.

Abstract: Coated milling insert has a WC-Co cemented carbide with a low content of cubic carbides and a highly W-alloyed binder phase and a coating including an inner layer of TiCxNy with columnar grains followed by a layer of &kgr;-Al2O3 and a top layer of TiN. The coated milling insert is particularly useful for milling of grey cast iron with or without cast skin under wet conditions at low and moderate cutting speeds and milling of nodular cast iron and compacted graphite iron with or without cast skin under wet conditions at moderate cutting speeds.

Abstract: Coated milling insert has a WC-Co cemented carbide with a low content of cubic carbides and a highly W-alloyed binder phase and a coating including an inner layer of TiCxNy with columnar grains followed by a layer of &kgr;-Al2O3 and a top layer of TiN. The coated milling insert is particularly useful for milling of grey cast iron with or without cast skin under wet conditions at low and moderate cutting speeds and milling of nodular cast iron and compacted graphite iron with or without cast skin under wet conditions at moderate cutting speeds.

Abstract: A method of preserving bodily protein stores such as skeletal muscle mass in a catabolic patient involves the concomitant administration (a) &agr;-KG and/or &agr;-KGA and (b) ammonium in amounts effective to preserving skeletal muscle. Also disclosed is the combination of a first pharmaceutical composition comprising &agr;-KG and/or &agr;-KGA in a pharmaceutically acceptable carrier and a second pharmaceutical composition comprising ammonium in a pharmaceutically acceptable carrier, in amounts effective to preserving skeletal muscle.

Abstract: Coated milling insert has a WC-Co cemented carbide with a low content of cubic carbides and a highly W-alloyed binder phase and a coating including an inner layer of TiCxNy with columnar grains followed by a layer of &kgr;-Al2O3 and a top layer of TiN. The coated milling insert is particularly useful for milling of grey cast iron with or without cast skin under wet conditions at low and moderate cutting speeds and milling of nodular cast iron and compacted graphite iron with or without cast skin under wet conditions at moderate cutting speeds.

Abstract: The present invention discloses an HSS tool with a PVD coating and with at least one cutting edge. The cutting edge has a radius of 15-25 &mgr;m and the carbides in the HSS are in contact with the coating. The present invention also relates to a method of making an HSS tool provided with a PVD coating with improved wear resistance. The improvement is obtained by subjecting the tool prior to the deposition of the coating to an electropolishing treatment such that a cutting edge radius of 15-25 &mgr;m is obtained and that the carbides in the HSS are revealed.

Abstract: Coated milling insert has a WC-Co cemented carbide with a low content of cubic carbides and a highly W-alloyed binder phase and a coating including an inner layer of TiCxNy with columnar grains followed by a layer of ?-Al2O3 and a top layer of TiN. The coated milling insert is particularly useful for milling of grey cast iron with or without cast skin under wet conditions at low and moderate cutting speeds and milling of nodular cast iron and compacted graphite iron with or without cast skin under wet conditions at moderate cutting speeds.

Abstract: Coated milling insert has a WC—Co cemented carbide with a low content of cubic carbides and a highly W-alloyed binder phase and a coating including an inner layer of TiCxNy with columnar grains followed by a layer of ?-Al2O3 and a top layer of TiN. The coated milling insert is particularly useful for milling of grey cast iron with or without cast skin under wet conditions at low and moderate cutting speeds and milling of nodular cast iron and compacted graphite iron with or without cast skin under wet conditions at moderate cutting speeds.