Abstract: Methods of preparing a dry powder blend co-coagulating conductive carbon black particles and fibrillizable polytetrafluoroethylene particles from an aqueous dispersion and drying the co-coagulate are described. Dry powders prepared by such methods and electrodes prepared from such powders are also described.

Abstract: Described herein is a process for making PTFE having a standard specific gravity of less than 2.160 g/cm3 comprising: polymerizing a tetrafluoroethylene monomer in an aqueous medium comprising an emulsifier and an initiator in a reaction vessel and contacting the aqueous medium with a fluorinated polyether. Also described herein are the polymerizable compositions and articles thereof.

Abstract: Fluoropolymers containing one or more azide group wherein the azide group is not a sulfonyl-azide group and processes of preparing them.

Abstract: Described herein is a method of purifying a product and recycling water comprising the following steps: (i) providing a crude product comprising at least one low molecular weight fluoroorganic compounds wherein the low molecular weight fluoroorganic compounds is partially fluorinated and comprises a polar group and/or a reactive group; (ii) extracting the impurity from the product using water to form an extract, (iii) contacting the extract with a radical-forming process to degrade the low molecular weight fluoroorganic compounds into carbon dioxide, water, fluorine ions, and optionally cations; and (iv) using the water from step (iii) in step (ii)

Abstract: Described herein is a method of purifying a product and recycling water comprising the following steps: (i) providing a crude product comprising at least one low molecular weight fluoroorganic compounds wherein the low molecular weight fluoroorganic compounds is partially fluorinated and comprises a polar group and/or a reactive group; (ii) extracting the impurity from the product using water to form an extract, (iii) contacting the extract with a radical-forming process to degrade the low molecular weight fluoroorganic compounds into carbon dioxide, water, fluorine ions, and optionally cations; and (iv) using the water from step (iii) in step (ii)

Abstract: Fluoropolymers containing one or more azide group wherein the azide group is not a sulfonyl-azide group and processes of preparing them.

Abstract: Described herein is a composition comprising an aqueous polymerization reaction product of fluorinated monomers and wherein the polymerization is initiated (i) in the absence of a fluorinated emulsifier and whereby no fluorinated emulsifier is added during polymerization or (ii) in the presence of an fluorinated emulsifier selected from: [Rf—O-L-COO-]i Xi+ (I) wherein L represents a linear or branched, non-fluorinated, partially fluorinated, or fully fluorinated alkylene group, Rf represents a linear or branched partially or fully fluorinated aliphatic group or a linear or branched partially or fully fluorinated aliphatic group interrupted with at least one oxygen atom, Xi+ represents a cation having the valence i and i is 1, 2 or 3; wherein the reaction product and/or the resulting aqueous phase are substantially free of di- and tri-alkylamines and substantially free of low molecular weight fluoroorganic compounds and methods thereof.

Abstract: There is provided an article prepared from a fluoroelastomer, the fluoroelastomer being derived from an emulsion, the emulsion comprising a fluorinated emulsifier represented by the formula F—(CF2)t—[O(CF2)n]m—O—(CHF)o—(CF2)p—X.

Abstract: Fluoropolymers containing one or more azide group wherein the azide group is not a sulfonyl-azide group and processes of preparing them.

Abstract: A process is described of pyrolyzing at least one perfluorinated hydrocarbon, or a material containing at least one perfluorinated hydrocarbon, in the presence of hydrogen, to yield a reaction mixture containing difluorocarbene.

Abstract: Fluoropolymers containing one or more azide group wherein the azide group is not a sulfonyl-azide group and processes of preparing them.

Abstract: There is provided an article prepared from a fluoroelastomer, the fluoroelastomer being derived from an emulsion, the emulsion comprising a fluorinated emulsifier represented by the formula F—(CF2)t—[O(CF2)n]m—O—(CHF)o—(CF2)p—X.

Abstract: Fluoropolymers containing one or more azide group wherein the azide group is not a sulfonyl-azide group and processes of preparing them.

Abstract: Method of making fluoropolymers by emulsion polymerization of one or more fluorinated monomers in an aqueous phase in the presence of a fluorinated emulsifier, said method comprises adding a doping agent in a weight ratio with respect to the emulsifier of from about 1:2 to about 1:20, said doping agent has a melting point of equal or less than 30° C. and a boiling point of at least about 100° C. and is selected from the group consisting of fluorinated cyclic hydrocarbons, fluorinated polyoxyalkenes, fluorinated alkenes and fluorinated polyoxyalkenes.

Abstract: Described herein is a composition comprising an aqueous polymerization reaction product of fluorinated monomers and wherein the polymerization is initiated (i) in the absence of a fluorinated emulsifier and whereby no fluorinated emulsifier is added during polymerization or (ii) in the presence of an fluorinated emulsifier selected from: [Rf—O-L-COO-]i Xi+ (I) wherein L represents a linear or branched, non-fluorinated, partially fluorinated, or fully fluorinated alkylene group, Rf represents a linear or branched partially or fully fluorinated aliphatic group or a linear or branched partially or fully fluorinated aliphatic group interrupted with at least one oxygen atom, Xi+ represents a cation having the valence i and i is 1, 2 or 3; wherein the reaction product and/or the resulting aqueous phase are substantially free of di- and tri-alkylamines and substantially free of low molecular weight fluoroorganic compounds and methods thereof.

Abstract: There is provided a fluoroelastomer characterized by containing one type or more types of fluorinated emulsifiers represented by the formula: F—(CF2)t-[O(CF2)n]m-O—(CHF)o-(CF2)p-X where m=0 to 3; n=1 to 5; o=0 to 1; p=1 to 3; t=1 to 10; and where when t=2 than o?0; and further where X is selected from a group consisting of a carboxyl acid group and a salt of a carboxylic acid group. A method for preparing fluoroelastomers by using such fluorinated emulsifiers in emulsion polymerization of fluoromonomers and articles containing such fluoroelastomers are also provided. A fluorinated elastomer dispersion including an aqueous mixture of a crosslinkable fluorinated elastomer and such fluorinated emulsifiers are also provided. The fluoroelastomers created with such fluorinated emulsifiers are essentially free of cations other than NH4+ and H+ and have a low glass transition temperature.

Abstract: A process is described of pyrolyzing at least one perfluorinated hydrocarbon, or a material containing at least one perfluorinated hydrocarbon, in the presence of hydrogen, to yield a reaction mixture containing difluorocarbene.

Abstract: Described herein is a process for making PTFE having a standard specific gravity of less than 2.160 g/cm3 comprising: polymerizing a tetrafluoroethylene monomer in an aqueous medium comprising an emulsifier and an initiator in a reaction vessel and contacting the aqueous medium with a fluorinated polyether. Also described herein are the polymerizable compositions and articles thereof.

Abstract: Method of making fluoropolymers by emulsion polymerization of one or more fluorinated monomers in an aqueous phase in the presence of a fluorinated emulsifier, said method comprises adding a doping agent in a weight ratio with respect to the emulsifier of from about 1:2 to about 1:20, said doping agent has a melting point of equal or less than 30° C. and a boiling point of at least about 100° C. and is selected from the group consisting of fluorinated cyclic hydrocarbons, fluorinated polyoxyalkenes, fluorinated alkenes and fluorinated polyoxyalkenes.

Abstract: Fluoropolymers containing one or more azide group wherein the azide group is not a sulfonyl-azide group and processes of preparing them.