Abstract: A method of producing a metal superalloy may include: providing a charge of metal materials; melting the charge of metal materials in an electric-arc furnace to obtain a first melt of the charge of metal materials; performing Argon Oxygen Decarburization (A.O.D.) treatment on the first melt to obtain a decarburized and refined first melt; solidifying the decarburized and refined first melt to obtain first ingots; melting the first ingots in a Vacuum Induction Degassing and Pouring (V.I.D.P.) furnace to obtain a second melt; solidifying the second melt to obtain second ingots; melting the second ingots in a Vacuum Arc Remelting (V.A.R.) furnace to obtain a third melt; and solidifying the third melt to obtain the metal superalloy. The charge of metal materials may have a weight greater than or equal to forty tons and less than or equal to sixty tons.

Abstract: The present invention relates to a method (1) of producing a metal superalloy (10) comprising the steps of providing a charge of metal materials (2); melting said charge of metal materials (2) in an electric-arc furnace (3) to obtain a first melt (3A) of said charge of metal materials (2); solidifying (5) said first melt (3A) to obtain first ingots (5A); melting said first ingots (5A) in a V.I.D.P. furnace (6) to obtain a second melt (6A); solidifying (7) said second melt (6A) to obtain second ingots (7A); melting said second ingots (7A) in a V.A.R. furnace (8) to obtain a third melt (8A); solidifying (9) said third melt (8A) to obtain a metal superalloy (10). The method (1) is characterized in that the charge of metal materials (2) has a weight amount ranging from forty to sixty tons, and it includes a step of carrying out an A.O.D. treatment (4) on said first melt (3A) to obtain a decarburized and refined first melt (4A); said melting in the V.I.D.P. furnace (6) and said melting in the V.A.R.