Abstract: The invention relates to a two-part dual cure dental composition with improved stability toward discoloration and premature polymerization. The dental composition comprises a Base Part and a Catalyst Part, the Base Part comprising polymerizable component(s) without an acidic moiety, optionally polymerizable component(s) with an acidic moiety, filler(s), transition metal component(s), peroxide component(s), stabilizer component(s) comprising a free-radical moiety, the Catalyst Part comprising polymerizable component(s) without an acidic moiety, filler(s), ascorbic acid component, photo-initiator system, stabilizer component(s) comprising a phosphite or sulfite moiety. The dental composition is in particular useful as bulk fill dental composite, dental resin cement, core build-up dental material or self- and dual cure dental adhesive. The invention further relates to an initiator system and the use of a stabilizer comprising a free-radical moiety.

Abstract: The present invention relates to a kit of parts comprising Part A and Part B, Part A comprising: ascorbic acid, component(s) comprising an ascorbic acid moiety or derivative(s) thereof, optionally polymerizable component(s) without acidic moieties, optionally polymerizable component(s) with acidic moieties, and optionally filler(s), Part B comprising polymerizable component(s) without acidic moieties, polymerizable component(s) with acidic moieties, transition metal component(s), organic peroxide(s), and optionally filler(s), The invention is also directed to a redox initiator system comprising ascorbic acid, component(s) comprising an ascorbic acid moiety or derivative(s) thereof, transition metal component(s), preferably comprising a copper or iron ion containing salt, organic peroxide(s), preferably comprising a hydroperoxide or di-peroxide. The kit of parts and redox initiator system are particularly useful in the dental field.

Abstract: The present invention relates to a kit of parts comprising Part A and Part B, Part A comprising: ascorbic acid, component(s) comprising an ascorbic acid moiety or derivative(s) thereof, optionally polymerizable component(s) without acidic moieties, optionally polymerizable component(s) with acidic moieties, and optionally filler(s), Part B comprising polymerizable component(s) without acidic moieties, polymerizable component(s) with acidic moieties, transition metal component(s), organic peroxide(s), and optionally filler(s), The invention is also directed to a redox initiator system comprising ascorbic acid, component(s) comprising an ascorbic acid moiety or derivative(s) thereof, transition metal component(s), preferably comprising a copper or iron ion containing salt, organic peroxide(s), preferably comprising a hydroperoxide or di-peroxide. The kit of parts and redox initiator system are particularly useful in the dental field.

Abstract: The invention relates to a one-component self-adhesive composition for dental use comprising radically polymerizable component(s) with an acidic moiety as component A, radically polymerizable component(s) without an acidic moiety as component (B), an oxidizing agent comprising persulfate(s) as component (C), transition metal component(s) as component (D), photoinitiator system(s) as component (E), optionally non acid-reactive filler(s) as component (F), and optionally additive(s) as component (G).

Abstract: The invention relates to a one-component self-adhesive composition for dental use comprising radically polymerizable component(s) with an acidic moiety as component A, radically polymerizable component(s) without an acidic moiety as component (B), an oxidizing agent comprising persulfate(s) as component (C), transition metal component(s) as component (D), photoinitiator system(s) as component (E), optionally non acid-reactive filler(s) as component (F), and optionally additive(s) as component (G).

Abstract: The present invention relates to a glass filler material with an average particle size of 0.1-20 ?m. It further relates to a method for producing a glass filler material. The glass filler material comprises 65-99.95 mol % silicon dioxide (SiO2), 0-15 mol % aluminum and/or boron oxide (Al2O3, B2O3), 0-30 mol % zirconium and/or titanium and/or hafnium oxide (ZrO2, TIO2, HfO2), Y2O3 and/or Sc2O3 and/or La2O3 and/or CeO2 and/or other lanthanide oxides, 0.05-4 mol % alkali metal oxides (Na2O, Li2O, K2O, Rb2O, Cs2O), 0-25 mol % earth alkali metal oxides (MgO, CaO, SrO, BaO). The glass filler material shows a low concentration of alkali ions and is used for composites with cationically curing properties and for dental composites and dental restoration materials.

Abstract: The invention relates to a polymerizable dental material containing: (a) 3 to 80 wt. % of one or more cationically curable monomers; (b) 3 to 90 wt. % of one or more radio-opaque fillers; (c) 0.01 to 25 wt. % of initiators, retarders and/or accelerators, and; (d) 0 to 25 wt. % of auxiliary agents, whereby the cited percentages each refer to the total weight of the material. Filler (b) is produced by means of a melting method and is selected so that it has a refractive index of nD=1.49–1.54, so that the viscosity of the polymerizable dental material, after a period of at least 9 months during which it was stored at a temperature ranging from 20 to 25° C., has a value of +/?50 % of the initial value measured 24 hours after the polymerizable dental material was produced, and so that the polymerizable dental material has a reactivity of the type that, once polymerization is initiated, the amount of the maximum heat flux generated by the dental material equals at least 0.

Abstract: The invention relates to a polymerizable dental material containing: (a) 3 to 80 wt. % of one or more cationically curable monomers; (b) 3 to 90 wt. % of one or more radio-opaque fillers; (c) 0.01 to 25 wt. % of initiators, retarders and/or accelerators, and; (d) 0 to 25 wt. % of auxiliary agents, whereby the cited percentages each refer to the total weight of the material. Filler (b) is produced by means of a melting method and is selected so that it has a refractive index of nD=1.49 1.54, so that the viscosity of the polymerizable dental material, after a period of at least 9 months during which it was stored at a temperature ranging from 20 to 25° C., has a value of +/−50% of the initial value measured 24 hours after the polymerizable dental material was produced, and so that the polymerizable dental material has a reactivity of the type that, once polymerization is initiated, the amount of the maximum heat flux generated by the dental material equals at least 0.