Abstract: A method of generating a patterned alignment direction on an alignment surface for a liquid crystal display cell is described. The cell is formed by forming a first alignment direction on an alignment surface, such as a polyimide surface of the cell. A second alignment direction is formed on the alignment surface. The first and second alignment directions are formed by a variety of sequences of treatments. An example of a first sequence is a first step of rubbing the alignment surface and thereafter a second step of selectively exposing (preferably using a mask) the alignment surface to a treatment selected from the group of exposure to electromagnetic radiation and exposure to a particle beam. Another example of a sequence is a first step of exposing the alignment surface to a treatment selected from the group of electromagnetic radiation and a particle beam thereafter selectively exposing (preferably through a mask) the alignment surface to another particle beam.

Abstract: Bombardment of the surface of a substrate with a film layer is used to create alignment layers for liquid crystal displays. By using bombardment of the surface at an angle, both direct creation of the alignment layer or indirect deposition of the alignment layer material onto a glass plate can be achieved.

Abstract: The present invention is a method for forming a liquid-crystal cell of a liquid-crystal display. Initially, a dry processed alignment film is deposited onto a first transparent substrate using a dry processing technique, such as plasma enhanced chemical vapor deposition (PECVD). The dry processed alignment film is then irradiated with a beam of atoms to arrange the atomic structure of the alignment film in at least one desired direction in order to orient the liquid-crystal molecules. Another dry processed alignment film is deposited on a second substrate using a dry processing technique and, likewise, irradiated with a beam of atoms. The first transparent substrate and the second substrate are then sandwiched together with their respective alignment films spaced adjacent to each other. The space between the films is then filled with a liquid-crystal material.

Abstract: Superconducting transition metal oxide films are provided which exhibit very high onsets of superconductivity and superconductivity at temperatures in excess of 40.degree. K. These films are produced by vapor deposition processes using pure metal sources for the metals in the superconducting compositions, where the metals include multi-valent nonmagnetic transition metals, rare earth elements and/or rare earth-like elements and alkaline earth elements. The substrate is exposed to oxygen during vapor deposition, and, after formation of the film, there is at least one annealing step in an oxygen ambient and slow cooling over several hours to room temperature. The substrates chosen are not critical as long as they are not adversely reactive with the superconducting oxide film. Transition metals include Cu, Ni, Ti and V, while the rare earth-like elements include Y, Sc and La. The alkaline earth elements include Ca, Ba and Sr.

Abstract: We have found that liquid crystals can be aligned on a polyimide surface exposed to a low energy and neutral Argon ion beam. The energy of the incident ions were varied between 75 and 500 eV, the integrated current density from 100 .mu.A/cm.sup.2 to 500 mA/cm.sup.2, and the angle of incidence over which alignment was measured was between 10 and 20 degrees. The pretilt angle of the liquid crystals could be varied between 0 and 8 degrees, by controlling the processing conditions. Degradation of the polyimide, which leads to charge migration, can be avoided by operating at low accelerating voltages.