Abstract: An apparatus and continuous stable process for producing multicrystalline silicon ingots with large cross-sections by an induction method, by maintaining surface temperature of the ingot at the output of the crucible within the range of 900-1150° C., and by heating the ingot at the output of the upper zone of the controlled cooling compartment to a temperature of 1200-1250° C., followed by cooling of the ingot at a rate of no more than 10° C./cm.

Abstract: A process for the production of multicrystalline silicon ingots by the induction method comprises charging a silicon raw material into the melting chamber of a cooled crucible enveloped by an inductor, forming a melt surface, and melting, wherein the mass rate of charging the silicon raw material and the speed of pulling the ingot are set such that provide for the melt surface position below the upper plane of the inductor but not lower than ? of the height thereof and the melt surface is kept at the same level. In doing this the melt surface position is kept at the same level by maintaining one of the output parameters of the inductor feed within a predetermined range. The process provides for casting multicrystalline silicon ingots suitable for solar cell fabrication and it is notable for higher efficiency and lower specific energy consumption.

Abstract: An apparatus and continuous stable process for producing multicrystalline silicon ingots with large cross-sections by an induction method, by maintaining surface temperature of the ingot at the output of the crucible within the range of 900-1150° C., and by heating the ingot at the output of the upper zone of the controlled cooling compartment to a temperature of 1200-1250° C., followed by cooling of the ingot at a rate of no more than 10° C./cm.

Abstract: A process for the production of multicrystalline silicon ingots by the induction method comprises charging a silicon raw material into the melting chamber of a cooled crucible enveloped by an inductor, forming a melt surface, and melting, wherein the mass rate of charging the silicon raw material and the speed of pulling the ingot are set such that provide for the melt surface position below the upper plane of the inductor but not lower than ? of the height thereof and the melt surface is kept at the same level. In doing this the melt surface position is kept at the same level by maintaining one of the output parameters of the inductor feed within a predetermined range. The process provides for casting multicrystalline silicon ingots suitable for solar cell fabrication and it is notable for higher efficiency and lower specific energy consumption.

Abstract: This invention is related to obtaining multicrystalline silicon using induction method. The method comprises melting and casting of a pool in the form of a melting space, crystallization of a multicrystalline silicon ingot, and its controlled cooling by means of a heating equipment set. After the pool melting and casting is terminated, crystallization of the remaining part of the multicrystalline silicon ingot is finished along with the controlled cooling of the whole ingot; the ingot is then removed together with a movable bottom and the heating equipment set; and its controlled cooling continues. At the same time, another heating equipment set is supplied to the vacated place with another movable bottom; then the new movable bottom is moved into the water-cooled crucible; and the process steps are repeated in order to produce the next ingot. The method is implemented using an apparatus that additionally includes a platform installed in the controlled cooling compartment and designed to revolve on its axis.