Abstract: Self-adhesive dental restorative composition comprising (i) 10 to 40 percent by weight based on the total weight of the composition of a mixture of hydrolysis-stable polymerizable monomers of the following formula (I): wherein R is a m+n valent organic group having 1 to 20 carbon atoms and optionally 1 to 5 atoms selected from the group of nitrogen, oxygen and sulfur atoms; A independently represents a moiety of the following formula (II): wherein L is a hydrogen atom, a C1-6 alkyl group, a C3-8 cycloalkyl group, a C6-14 aryl group or a group of the following formula (III) wherein R? is a hydrogen atom, a C1-6 alkyl group, a C3-8 cycloalkyl group, or a C6-14 aryl group; X is O, S, NH or NR? wherein R? is a C1-6 alkyl group, a C3-8 cycloalkyl group, a C6-14 aryl group; a is 0 or 1; M is a group of the following formula (IV) wherein Y is O, S, NH or NR?? wherein R?? is a C1-6 alkyl group, a C3-8 cycloalkyl group, a C6-14 aryl group; b is an integer of from O to 3; c is O or 1; d is an integer of from O to 3; pr

Abstract: Dental obturator point having an obturation body containing a composite material comprising (a) a polymer and b) a particulate filler, whereby the obturation body has a radio opacity of at least 3 mm/mm Al, characterized in that the composite material has (i) a tensile strength of from 5 to 70 MPA1 (ii) a flexural strength of from 5 to 90 MPA, (iii) a flexural module of from 0.1 to 2.5 GPa, and which has (iv) a 300 rpm drilling coefficient at 37° C. in the range of from ?1 to 7.00.

Abstract: Dental obturator point having an obturation body containing a composite material comprising (a) a polymer and b) a particulate filler, whereby the obturation body has a radio opacity of at least 3 mm/mm Al, characterized in that the composite material has (i) a tensile strength of from 5 to 70 MPAl (ii) a flexural strength of from 5 to 90 MPA, (iii) a flexural module of from 0.1 to 2.5 GPa, and which has (iv) a 300 rpm drilling coefficient at 37° C. in the range of from ?1 to 7.00.

Abstract: Self-adhesive dental restorative composition comprising (i) 10 to 40 percent by weight based on the total weight of the composition of a mixture of hydrolysis-stable polymerizable monomers of the following formula (I): wherein R is a m+n valent organic group having 1 to 20 carbon atoms and optionally 1 to 5 atoms selected from the group of nitrogen, oxygen and sulfur atoms; A independently represents a moiety of the following formula (II): wherein L is a hydrogen atom, a C1-6 alkyl group, a C3-8 cycloalkyl group, a C6-14 aryl group or a group of the following formula (III) wherein R? is a hydrogen atom, a C1-6 alkyl group, a C3-8 cycloalkyl group, or a C6-14 aryl group; X is O, S, NH or NR? wherein R? is a C1-6 alkyl group, a C3-8 cycloalkyl group, a C6-14 aryl group; a is 0 or 1; M is a group of the following formula (IV) wherein Y is O, S, NH or NR?? wherein R?? is a C1-6 alkyl group, a C3-8 cycloalkyl group, a C6-14 aryl group; b is an integer of from O to 3; c is O or 1; d is an integer of from O to 3; pr