Abstract: Tungsten-titanium-phosphate materials and methods of making and using the same.

Abstract: A fused silica glass having a refractive index homogeneity of less or equal to about 5 ppm over an aperture area of at least about 50 cm2. The fused silica glass is also substantially free of halogens and has an adsorption edge of less than about 160 nm. The glass is dried by exposing a silica soot blank to carbon monoxide before consolidation, reducing the combined concentration of hydroxyl (i.e., OH, where H is protium (11H) and deuteroxyl (OD), where D is deuterium (12H)) of less than about 20 ppm by weight in one embodiment, less than about 5 ppm by weight in another embodiment, and less than about 1 ppm by weight in a third embodiment.

Abstract: This disclosure describes a process for strengthening, by ion-exchange, the edges of an article separated from a large glass sheet after the sheet has been ion-exchanged to strengthen by exposing only the one or a plurality of the edges of the separated article to an ion-exchange medium (for example without limitation, a salt, paste, frit, glass) while the glass surface is maintained at temperatures less than 200° C.

Abstract: Strengthened glass substrate sheets and methods of fabricating glass panels from glass substrate sheets are disclosed. In one embodiment, a method includes forming at least one series of holes through a thickness of the glass substrate sheet, wherein the at least one series of holes defines a perimeter of the glass panel to be separated from the glass substrate sheet. The method further includes strengthening the glass substrate sheet by a strengthening process, and separating the glass panel from the glass substrate sheet along the at least one series of holes. At least a portion of one or more edges of the glass panel has an associated edge compressive layer. In another embodiment, a strengthened glass substrate sheet includes at least one series of holes that defines a perimeter of one or more glass panels to be separated from the strengthened glass substrate sheet.

Abstract: A method of cutting an article (172) from a chemically strengthened glass substrate (110) includes generating a pulsed laser beam (108) from a laser source (106). The pulsed laser beam (108) may have a pulse duration of less than about 1000 fs and an output wavelength such that the chemically strengthened glass substrate (110) is substantially transparent to the pulsed laser beam (108). The pulsed laser beam (108) may be focused to form a beam waist (109) that is positioned in the same horizontal plane as an inner tensile region (124) of the chemically strengthened glass substrate (110). The beam waist (109) may be translated in a first pass along a cut line (116), wherein the beam waist (109) traverses an edge (111) of the chemically strengthened glass substrate. The beam waist (113) may then be translated in a second pass along the cut line (116) such that a crack (119) propagates from the edge (113) along the cut line (116) ahead of the translated beam waist (109) during the second pass.

Abstract: Methods for separating strengthened glass articles from glass substrate sheets and strengthened glass substrate sheets are described herein. In one embodiment, a method of separating a glass article from a glass substrate sheet includes forming at least one groove on at least one surface of the glass substrate sheet. The at least one groove continuously extends around a perimeter of the glass article and extends partially through a thickness of the glass substrate sheet. The method further includes strengthening the glass substrate sheet by a strengthening process and separating the glass article from the glass substrate sheet along the at least one groove such that one or more edges of the glass article are under compressive stress. In another embodiment, a strengthened glass substrate sheet includes an ion exchanged glass having one or more grooves in one or more strengthened surface layers, the one or more grooves defining glass articles.

Abstract: Glass interposer panels and methods for forming the same are described herein. The interposer panels include a glass substrate core formed from an ion-exchangeable glass. A first layer of compressive stress may extend from a first surface of the glass substrate into the thickness T of the glass substrate core to a first depth of layer D1. A second layer of compressive stress may be spaced apart from the first layer of compressive stress and extending from a second surface of the glass substrate core into the thickness T of the glass substrate core to a second depth of layer D2. A plurality of through-vias may extend through the thickness T of the glass substrate core. Each through-via is surrounded by an intermediate zone of compressive stress that extends from the first layer of compressive stress to the second layer of compressive stress adjacent to a sidewall of each through-via.

Abstract: A method for producing a fused silica glass containing titania includes synthesizing particles of silica and titania by delivering a mixture of a silica precursor and a titania precursor to a burner, growing a porous preform by successively depositing the particles on a deposition surface while rotating and translating the deposition surface relative to the burner, and consolidating the porous preform into a dense glass.

Abstract: An F-doped silica glass, a process for making the glass, an optical member comprising the glass, and an optical system comprising such optical member. The glass material comprises 0.1-5000 ppm by weight of fluorine. The glass material according to certain embodiments of the present invention has low polarization-induced birefringence, low LIWFD and low induced absorption at 193 nm.

Abstract: Disclosed in the application are a synthetic silica glass having low fluence-dependent transmission, particularly at about 193 nm, and a process for making the same. The glass may desirably exhibit a low level of fluorescence at 290 and 390 nm when activated at about 248 nm. The glass may desirably exhibit low level of LIWFD, [SiH*] and/or [ODC].

Abstract: A method for cutting a glass article from a strengthened glass substrate having a surface compression layer and a tensile layer includes forming an edge defect in the surface compression layer on a first edge of the strengthened glass substrate. The method further includes propagating a through vent through the surface compression and tensile layers at the edge defect. The through vent precedes a region of separation along a cut line between the glass article and the strengthened glass substrate.

Abstract: The invention relates to a composition suitable for inducing a T cell mediated immune response against an influenza virus in a vertebrate, said composition comprising nucleic acid encoding one or more epitopes of one or more internal proteins of influenza virus, wherein said composition comprises nucleic acid encoding at least two said epitopes, at least one epitope being from each of two or more internal proteins of influenza virus. The invention also relates to uses of same and to methods involving same.

Abstract: An optical member comprising OD-doped silica glass, optionally doped with fluorine. The optical member is particularly advantageous for use in connection with radiation having a wavelength shorter than about 248 nm. In certain embodiments the optical member can be advantageously used for wavelength as short as about 157 nm.

Abstract: Disclosed is a synthetic silica glass optical material having high resistance to optical damage by ultraviolet radiation in the ultraviolet wavelength range, particularly in the wavelength less than about 250 nm and particularly, exhibiting a low laser induced wavefront distortion; specifically a laser induced wavefront distortion, measured at 633 nm, of between about ?1.0 and 1.0 nm/cm when subjected to 10 billion pulses of a laser operating at approximately 193 nm and at a fluence of approximately 70 ?J/cm2. The synthetic silica glass optical material of the present invention comprises OH concentration levels of less than about 600 ppm, preferably less than 200 ppm, and H2 concentration levels less than about 5.0×1017 molecules/cm3? and preferably less than about 2.0×1017 molecules/cm3.

Abstract: A fused silica glass having a refractive index homogeneity of less or equal to about 5 ppm over an aperture area of at least about 50 cm2. The fused silica glass is also substantially free of halogens and has an adsorption edge of less than about 160 nm. The glass is dried by exposing a silica soot blank to carbon monoxide before consolidation, reducing the combined concentration of hydroxyl (i.e., OH, where H is protium (11H) and deuteroxyl (OD), where D is deuterium (12H)) of less than about 20 ppm by weight in one embodiment, less than about 5 ppm by weight in another embodiment, and less than about 1 ppm by weight in a third embodiment.

Abstract: Disclosed is a synthetic silica glass optical material having high resistance to optical damage by ultraviolet radiation in the ultraviolet wavelength range, particularly in the wavelength less than about 250 nm and particularly, exhibiting a low laser induced wavefront distortion; specifically a laser induced wavefront distortion, measured at 633 nm, of between about ?1.0 and 1.0 nm/cm when subjected to 10 billion pulses of a laser operating at approximately 193 nm and at a fluence of approximately 70 ?J/cm2. The synthetic silica glass optical material of the present invention comprises OH concentration levels of less than about 600 ppm, preferably less than 200 ppm, and H2 concentration levels less than about 5.0×1017 molecules/cm3,and preferably less than about 2.0×1017 molecules/cm3.

Abstract: Disclosed are high purity synthetic silica material having an internal transmission at 193 nm of at least 99.65%/cm and method of preparing such material. The material is also featured by a high compositional homogeneity in a plane transverse to the intended optical axis. The soot-to-glass process for making the material includes a step of consolidating the soot preform in the presence of H2O and/or O2.

Abstract: An optical member comprising OD-doped silica glass, optionally doped with fluorine. The optical member is particularly advantageous for use in connection with radiation having a wavelength shorter than about 248 nm. In certain embodiments the optical member can be advantageously used for wavelength as short as about 157 nm.

Abstract: An F-doped silica glass, a process for making the glass, an optical member comprising the glass, and an optical system comprising such optical member. The glass material comprises 0.1-5000 ppm by weight of fluorine. The glass material according to certain embodiments of the present invention has low polarization-induced birefringence, low LIWFD and low induced absorption at 193 nm.

Abstract: The present invention is a method of making a lithography photomask and photomask blank. The method of making the lithography photomask and photomask blank includes providing a silicon oxyfluoride glass tube having an OH content less than 50 ppm. The method further includes cutting the silicon oxyfluoride glass tube, flattening the silicon oxyfluoride glass tube, and forming the flattened cut silicon oxyfluoride glass tube into a photomask blank having a planar surface. The present invention includes a glass lithography mask preform. The glass lithography mask preform is a longitudinal silicon oxyfluoride glass tube that has an OH content ?10 ppm, a F wt. % concentration ?0.5 wt. %.