Abstract: Liquid admixtures for cement-based products may include one or more of calcium-silicate-hydrates (C-S-H), calcium-aluminum-silicate-hydrates (C-A-S-H), 3-dimensional graphene carbons (3DG carbons) and water. Liquid admixtures for cement-based products may include one or more of zinc modulated C-S-H, C-A-S-H, 3DG carbons and water. The 3DG carbons may include flaky graphene and nodular graphene. High performance concrete (HPC) formulations free of silica fume and including slag, calcium-silicate-hydrates (C-S-H), calcium-aluminum-silicate-hydrates (C-A-S-H), 3-dimensional graphene carbons (3DG carbons) at a silica fume replacement level of approximately 8 wt %.

Abstract: Cement compositions including ordinary Portland cement, a secondary cementitious material (SCM) including one or more of pozzolan, metakaolin, limestone, or gypsum in an amount of up to approximately 70% of a replacement level of ordinary Portland cement, and between approximately 0.05% by weight of cement (bwoc) and 2% bwoc of aggregates of mesoporous carbon nanoparticles (3DG) carbons. The cement compositions regulate nucleation and time-lapsed growth of calcium silica hydrates during initial hydration. The 3DG carbons include aggregates of mesoporous carbon nanoparticles, which include one or more interconnected bundles of electrically conductive graphene layers. The 3DG carbons include oxygen containing functional groups disposed on one or more of the surfaces of the 3DG carbons or within the 3DG carbons.

Abstract: The invention is directed to carbon fibers having high tensile strength. The invention also provides a method and apparatus for making the carbon fibers. The method comprises advancing a precursor fiber through a plurality of passes through an oxidation oven, where stretching during the initial passes is minimized or eliminated entirely, or made negative, followed by controlled stretching over a series of passes, using rollers of increasing speed.

Abstract: Cement compositions including ordinary Portland cement, a secondary cementitious material (SCM) including one or more of pozzolan, metakaolin, limestone, or gypsum in an amount of up to approximately 70% of a replacement level of ordinary Portland cement, and between approximately 0.05% by weight of cement (bwoc) and 2% bwoc of aggregates of mesoporous carbon nanoparticles (3DG) carbons. The cement compositions regulate nucleation and time-lapsed growth of calcium silica hydrates during initial hydration. The 3DG carbons include aggregates of mesoporous carbon nanoparticles, which include one or more interconnected bundles of electrically conductive graphene layers. The 3DG carbons include oxygen containing functional groups disposed on one or more of the surfaces of the 3DG carbons or within the 3DG carbons.