Abstract: A process for stabilizing hypophosphite salt is provided, which comprises the following steps: a) washing the hypophosphite salt at least one time under a controlled pH value of 4-11, preferably 5-8, as the said hypophosphite salt in an aqueous solution and/or in a solid state; and b) drying the said hypophosphite salt under reduced pressure to remove the volatiles. The process can prevent or minimize the formation of a dangerous quantity of phosphine from hypophosphite salts, more particularly in the flame retardant of the application. The flame retardant polymer composition is also provided, which comprises a polymer and the hypophosphite salt stabilized by the above process.

Abstract: The current invention relates to a process for stabilizing a hypophosphite salt, comprising the step of heating the hypophosphite salt at a temperature of between 150 and 370° C. during a sufficient period of time to prevent the formation of a dangerous quantity of phosphine in their application as FR in polymers and a flame retardant polymer composition comprising a polymer and 0.1 to 30 weight percent based on the total weight of the composition of the hypophosphite salt thermally stabilized by the above process.

Abstract: A flame retardant polymer composition is described. The composition can include at least one polymer and a hypophosphite salt, wherein the hypophosphite salt is heat stabilized so that when it is heated for 3 hours at 298° C. under a flow of argon flushing at rate 58 mL/min, it generates less than 0.5 mL of phosphine per gram of hypophosphite salt. The polymer can be an epoxy resin, a phenolic resin, an acrylonitrile-butadiene-styrene resin, a styrene-acrylonitrile resin, a mixture of high impact polystyrene and polyphenylene oxides, a styrene-butadiene rubber, a polylactic acid or a polyvinyl chloride.

Abstract: A flame retardant polymer composition is described. The composition includes at least one polymer and a hypophosphite salt, wherein the hypophosphite salt is heat stabilized so that when it is heated for 3 hours at 298° C. under a flow of argon flushing at rate 58 mL/min, it generates less than 0.5 mL of phosphine per gram of hypophosphite salt. The flame retardant polymer composition can also include at least one additive that improves the flame retardant properties of the composition.

Abstract: The use of a heat stabilized calcium hypophosphite as a filler to increase the mechanical properties of a polyamide composition is described. The composition can also involve reinforcing and/or bulking filler and/or impact modifier agents. Using such a filler one can obtain a polyamide composition having very good mechanical performance with the calcium hypophosphite having a low degree of phoshpine generation.

Abstract: A process for stabilizing hypophosphite salt is provided, which comprises the following steps: a) washing the hypophosphite salt at least one time under a controlled pH value of 4-11, preferably 5-8, as the said hypophosphite salt in an aqueous solution and/or in a solid state; and b) drying the said hypophosphite salt under reduced pressure to remove the volatiles. The process can prevent or minimize the formation of a dangerous quantity of phosphine from hypophosphite salts, more particularly in the flame retardant of the application. The flame retardant polymer composition is also provided, which comprises a polymer and the hypophosphite salt stabilized by the above process.

Abstract: The current invention relates to a process for stabilizing a hypophosphite salt, comprising the step of heating the hypophosphite salt at a temperature of between 150 and 370° C. during a sufficient period of time to prevent the formation of a dangerous quantity of phosphine in their application as FR in polymers and a flame retardant polymer composition comprising a polymer and 0.1 to 30 weight percent based on the total weight of the composition of the hypophosphite salt thermally stabilized by the above process.