Abstract: The invention relates to a method for producing a hot-rolled strip composed of a bainitic multi-phase steel and having a Zn—Mg—Al coating, comprising the following steps: melting a steel melt containing (in weight percent): C: 0.04-0.11, Si: <=0.7, Mn: 1.4-2.2, Mo: 0.05-0.5, Al: 0.015-0.1, P: up to 0.02, S: up to 0.01, B: up to 0.006, and at least one element from the group Nb, V, Ti in accordance with the following condition: 0.02<=Nb+V+Ti<=0.20, the remainder being iron including unavoidable steel-accompanying elements resulting from the melting process, casting the steel melt into a preliminary material, in particular a slab or a block or a thin slab, hot rolling the preliminary material into a hot-rolled strip having a final rolling temperature in the range of 800 to 950° C., cooling the hot-rolled strip to a winding temperature less than 650° C., winding the hot-rolled strip at a winding temperature less than 650° C.

Abstract: The invention relates to a method for producing a hot-rolled strip composed of a bainitic multi-phase steel and having a Zn—Mg—Al coating, comprising the following steps: melting a steel melt containing (in weight percent): C: 0.04-0.11, Si: <=0.7, Mn: 1.4-2.2, Mo: 0.05-0.5, Al: 0.015-0.1, P: up to 0.02, S: up to 0.01, B: up to 0.006, and at least one element from the group Nb, V, Ti in accordance with the following condition: 0.02<=Nb+V+Ti<=0.20, the remainder being iron including unavoidable steel-accompanying elements resulting from the melting process, casting the steel melt into a preliminary material, in particular a slab or a block or a thin slab, hot rolling the preliminary material into a hot-rolled strip having a final rolling temperature in the range of 800 to 950° C., cooling the hot-rolled strip to a winding temperature less than 650° C., winding the hot-rolled strip at a winding temperature less than 650° C.

Abstract: The invention relates to a method for producing a hot-rolled strip composed of a bainitic multi-phase steel and having a Zn—Mg—Al coating, comprising the following steps: melting a steel melt containing (in weight percent): C: 0.04-0.11, Si: <=0.7, Mn: 1.4-2.2, Mo: 0.05-0.5, Al: 0.015-0.1, P: up to 0.02, S: up to 0.01, B: up to 0.006, and at least one element from the group Nb, V, Ti in accordance with the following condition: 0.02<=Nb+V+Ti<=0.20, the remainder being iron including unavoidable steel-accompanying elements resulting from the melting process, casting the steel melt into a preliminary material, in particular a slab or a block or a thin slab, hot rolling the preliminary material into a hot-rolled strip having a final rolling temperature in the range of 800 to 950° C., cooling the hot-rolled strip to a winding temperature less than 650° C., winding the hot-rolled strip at a winding temperature less than 650° C.