Abstract: The invention relates to carbon aerogels with particle sizes less than 1 ?m. The carbon aerogels are prepared by (A)reacting a mono- and/or polyhydroxybenzene, an aldehyde and a catalyst in a reactor at a reaction temperature T in the range from 75-200° C. at a pressure of 80-2400 kPa, (B) then spraying the reaction mixture from process step (A) into an acid, (C) drying the resulting product from process step (B) and (D) carbonizing it. The carbon aerogels according to the invention can be used as filler, reinforcing filler, UV stabilizer, electrode material, sound absorbents, thermal insulating material, catalyst, catalyst support, conductivity additive, absorbent for gas and/or liquid preparation or pigment.

Abstract: The invention relates to carbon aerogels with particle sizes less than 1 ?m. The carbon aerogels are prepared by (A)reacting a mono- and/or polyhydroxybenzene, an aldehyde and a catalyst in a reactor at a reaction temperature T in the range from 75-200° C. at a pressure of 80-2400 kPa, (B) then spraying the reaction mixture from process step (A) into an acid, (C) drying the resulting product from process step (B) and (D) carbonizing it. The carbon aerogels according to the invention can be used as filler, reinforcing filler, UV stabilizer, electrode material, sound absorbents, thermal insulating material, catalyst, catalyst support, conductivity additive, absorbent for gas and/or liquid preparation or pigment.

Abstract: Silicon dioxide powder in the form of aggregated primary particles has a specific pore length L of 2.5×105 to 4×105 m/?g, where L is defined as the quotient formed from the square of the BET surface area and the cumulative 2-50 nm pore volume determined using the BJH method, as per the formula L=(BET×BET)/BJH volume. A silanized silicon dioxide powder in the form of aggregated primary particles has a specific pore length L of 2.5×105 to 3.5×105 m/?g, and in it the surface area of the aggregates or parts thereof is occupied by chemically bound silyl groups. A thermal insulant comprises the silicon dioxide powder and/or the silanized silicon dioxide powder.

Abstract: The invention relates to a process for producing nanostructured silicon-carbon composites, comprising the (A) introduction of at least one of components (a1) mono- and/or polyhydroxyaromatic compound, and (a2) an aldehyde, and (a3) a catalyst, into a reactor to obtain a composition in which the components react with one another in the presence of the catalyst at a reaction temperature T of 75 to 200° C., and at a pressure of 80 to 2400 kPa, and over a period to of 0.

Abstract: The invention relates to carbon aerogels with particle sizes less than 1 ?m, The carbon aerogels are prepared by (A) reating a mono- and/or polyhydroxybenzene, an aldehyde and a catalyst in a reactor at a reaction temperature T in the range from 75-200° C. at a pressure of 80-2400 kPa, (B) then spraying the reaction mixture from process step (A) into an acid, to drying the resulting product from process step (B) and (D) carbonizing it. The carbon aerogels according to the invention can be used as filler, reinforcing filler, UV stabilizer, electrode material, sound absorbents, thermal insulating material, catalyst, catalyst support, conductivity additive, absorbent for as and/or liquid preparation or pigment.