Abstract: A surface-modified member in which a surface-modifying layer is laminated over at least a part of a resin member containing a thermosetting resin, the surface-modified member containing: a mixed layer that the resin member and the surface-modifying layer are mixed between the resin member and the surface-modifying layer, in which the mixed layer has a thickness of 250 nm to 10 ?m.

Abstract: A surface-modifying sheet contains a release sheet and a surface-modifying layer, the surface-modifying layer has a 160° C. storage modulus of 5.0×103 to 1.0×107 Pa, and the surface-modifying layer has a surface tension of 38 mN/m or higher.

Abstract: The present invention relates to a method for manufacturing a laminate, including: a laminating step of laminating a side of a thermal transfer layer of a thermal transfer sheet having a release sheet and the thermal transfer layer on at least a part of a surface of a resin member by heat bonding, in which the release sheet has no yield points, and has an elongation at break of 100% to 600% in a stress-strain curve measured by a tensile test at a molding temperature T?° C. in the laminating step.

Abstract: The present invention relates to a method for manufacturing a laminate, including a laminating step of laminating a side of a thermal transfer layer of a thermal transfer sheet having a release sheet and the thermal transfer layer on at least a part of a surface of a resin member by heat bonding, in which the release sheet has a thermal expansion coefficient ? of ?15%???+7.5% at a molding temperature T?° C. in the laminating step.

Abstract: The present invention relates to a surface-modifying sheet including a release sheet and a surface-modifying layer, the surface-modifying layer having an average thickness of 0.1 ?m to 50 ?m, and the difference between the maximum value and the minimum value of the thickness of the surface-modifying layer being less than twice the average thickness; and a surface-modified member, a coated article and a method for producing a coated article, using the surface-modifying sheet.

Abstract: The present invention relates to a surface-modifying sheet including a release sheet and a surface-modifying layer, and the surface-modifying layer containing a component that reacts with a thermosetting resin; a surface-modified member, a coated article, a printed article and a joined body, using the surface-modifying sheet; and a method for producing a surface-modified member.

Abstract: Polylactic acid film or sheet having tear strength so as not to break or tear during, for example, production or processing of the film or sheet or winding thereof into a roll, and causing neither melt nor deformation at high temperatures more than 100° C. In the polylactic acid film or sheet, the tear strength is not less than 100 N/mm when the film or sheet is torn at least in a flow direction (MD), a rate of dimensional change due to heating is not more than ±3% in the flow direction (MD) and a transverse direction (TD), and a rate of dimensional change due to loaded heating is not more than ±3% in the flow direction (MD).

Abstract: A film for a pressure-sensitive adhesive tape is a film for a pressure-sensitive adhesive tape, including a non-pressure-sensitive adhesive layer on one surface of a plastic film, where the non-pressure-sensitive adhesive layer includes a mixed layer of a silicone and a (meth)acrylic polymer; and the (meth)acrylic polymer has a calculated Tg of 10° C. or more.

Abstract: The present invention provides a polylactic acid film or sheet having tear strength so as not to break or tear during, for example, production or processing of the film or sheet or winding thereof into a roll, and causing neither melt nor deformation at high temperatures more than 100° C. In the polylactic acid film or sheet according to the present invention, the tear strength is not less than 100 N/mm when the film or sheet is torn at least in a flow direction (MD), a rate of dimensional change due to heating is not more than ±3% in the flow direction (MD) and a transverse direction (TD), and a rate of dimensional change due to loaded heating is not more than ±3% in the flow direction (MD).

Abstract: The present invention provides a separator including a separator substrate composed of a polylactic acid film or sheet having tear strength so as not to break or tear during production or processing of the separator. The separator is a separator including a separator substrate and a removable pressure-sensitive adhesive layer on at least one surface of the separator substrate, wherein the separator substrate is composed of a polylactic acid film or sheet comprising polylactic acid (A) wherein the tear strength of the film or sheet is not less than 100 N/mm when the film or sheet is torn at least in a flow direction (MD), a rate of dimensional change due to heating is not more than ±3% in the flow direction (MD) and a transverse direction (TD), and a rate of dimensional change due to loaded heating is not more than ±3% in the flow direction (MD).

Abstract: The present invention provides a protection film including a substrate composed of a polylactic acid film or sheet having tear strength so as not to break or tear during production or processing of the protection film. The protection film according to the present invention is a protection film including a substrate and a removable pressure-sensitive adhesive layer on at least one surface of the substrate, wherein the substrate is composed of a polylactic acid film or sheet comprising polylactic acid (A) wherein the tear strength is not less than 100 N/mm when the film or sheet is torn at least in a flow direction (MD), a rate of dimensional change due to heating is not more than ±3% in the flow direction (MD) and in a transverse direction (TD), and a rate of dimensional change due to loaded heating is not more than ±3% in the flow direction (MD).

Abstract: Provided is the following film for a pressure-sensitive adhesive tape in which a non-pressure-sensitive adhesive layer is provided on a base material film. In the case where dicing or the like is performed by performing adsorption fixation to a fixing base with a negative pressure, the occurrence of excessive close adhesion due to, for example, the heat generation of the base can be effectively suppressed. In addition, the non-pressure-sensitive adhesive layer is provided on the base material film, and hence blocking in a roll shape is effectively suppressed, the film for a pressure-sensitive adhesive tape does not tear or break upon its unwinding from the roll shape, conformity between the non-pressure-sensitive adhesive layer and the base material film is good, and followability to a deformation such as stretching is good. Also provided is a pressure-sensitive adhesive tape including such film for a pressure-sensitive adhesive tape.

Abstract: Disclosed is a polylactic acid-based film or sheet as a resin film or sheet including a polylactic acid (A). The film or sheet has a melt endotherm ?Hc? of 10 J/g or more, where ?Hc? is of a region crystallized upon film formation and specified by following Expression (1): ?Hc?=?Hm??Hc??(1) wherein ?Hc represents an exotherm (J/g) associated with crystallization of the film or sheet in a temperature rise process after film formation; and ?Hm represents an endotherm (J/g) associated with subsequent melting of the film or sheet, each determined by DSC. The film or sheet has a tear strength of 2.5 N/mm or more both in a machine direction (MD) and a transverse direction (TD). The polylactic acid-based resin film or sheet is resistant to melting and deformation even at an elevated temperature higher than 100° C. and is resistant to breaking and tearing during winding into a roll.