Abstract: This method for recovering a valuable metal from a used LIB includes: a step of adding, to an electrode assembly taken out of a detoxified used LIB, metallic zinc in an excess amount relative to a mass of the electrode assembly; a step of heating a mixture of the electrode assembly and the metallic zinc to form a molten metal; a step of taking out the molten metal and separating the molten metal into an alloy metal and a slag; and a step of heating the alloy metal to volatilize zinc in the alloy metal, and thereby, recovering an alloy metal of a valuable metal.

Abstract: A method for immobilizing arsenic includes adding calcium arsenate to a glass-forming material containing iron, silica, and alkaline components so that an iron/silica weight ratio is in a range of 0.5 to 0.9 and an amount of alkaline components is in a range of 14 wt % to 26 wt %, and thereby incorporating the arsenic into a glass solidified body. For example, the method for immobilizing arsenic may include: adding an alkaline solution and an oxidizing agent to a copper-arsenic-containing substance, and thereby carrying out an oxidizing leaching; separating a leach residue by solid-liquid separation; adding calcium hydroxide to a recovered alkaline arsenate solution to generate calcium arsenate; and adding the glass-forming material to the recovered calcium arsenate so that the iron/silica weight ratio and the amount of alkaline components are in the above-mentioned ranges, and thereby incorporating the arsenic into the glass solidified body.

Abstract: A method for immobilizing arsenic includes adding calcium arsenate to a glass-forming material containing iron, silica, and alkaline components so that an iron/silica weight ratio is in a range of 0.5 to 0.9 and an amount of alkaline components is in a range of 14 wt % to 26 wt %, and thereby incorporating the arsenic into a glass solidified body. For example, the method for immobilizing arsenic may include: adding an alkaline solution and an oxidizing agent to a copper-arsenic-containing substance, and thereby carrying out an oxidizing leaching; separating a leach residue by solid-liquid separation; adding calcium hydroxide to a recovered alkaline arsenate solution to generate calcium arsenate; and adding the glass-forming material to the recovered calcium arsenate so that the iron/silica weight ratio and the amount of alkaline components are in the above-mentioned ranges, and thereby incorporating the arsenic into the glass solidified body.