Abstract: Nanomaterials are an important class of materials for sunscreens. Conventional metal oxide nanoparticles are toxic in nature and leave white patches on skin after application. This disclosure provides a sunscreen composition containing biodegradable antimicrobial polymer nanoparticles as UV filter. The sunscreen composition comprising chitosan nanoparticles, at least one flavoring agent, at least one coloring agent, at least one stabilizer, and at least one preservative, in a defined form, wherein size of the chitosan nanoparticles is ranging from 200 to 900 nm. The size of the chitosan nanoparticles ranging from 200 to 400 nm for air medium, 500 to 700 nm for water medium and 700 to 900 nm for ethanol medium. The chitosan polymer is derived from chitin, a glucosamine polymer. The sunscreen composition is available in the defined form selected from a group consisting of a skin cream, a skin lotion, a powder, a gel, and a sprayable liquid.

Abstract: This disclosure relates generally to a sunscreen composition containing visibly transparent biocompatible ultraviolet blocking polymer nanoparticles. The sunscreen composition comprising polydimethylsiloxane (PDMS) nanoparticles, at least one flavoring agent, at least one coloring agent, at least one stabilizer, and at least one preservative, in a defined form, wherein size of the PDMS nanoparticles ranging from 200 to 1200 nm. The size of the PDMS nanoparticles ranging from 200 to 500 nm for air medium and from 800 to 1200 nm for water medium. The PDMS nanoparticles comprise a PDMS polymer having terminal functional group selected from alkyl, alkoxy, vinyl, hydroxyl, or a combination thereof. The sunscreen composition is available in the defined form selected from a group consisting of a skin cream, a skin lotion, a powder, a gel, and a sprayable liquid.

Abstract: Nanomaterials are an important class of materials for sunscreens. Conventional metal oxide nanoparticles are toxic in nature and leave white patches on skin after application. This disclosure provides a sunscreen composition containing biodegradable antimicrobial polymer nanoparticles as UV filter. The sunscreen composition comprising chitosan nanoparticles, at least one flavoring agent, at least one coloring agent, at least one stabilizer, and at least one preservative, in a defined form, wherein size of the chitosan nanoparticles is ranging from 200 to 900 nm. The size of the chitosan nanoparticles ranging from 200 to 400 nm for air medium, 500 to 700 nm for water medium and 700 to 900 nm for ethanol medium. The chitosan polymer is derived from chitin, a glucosamine polymer. The sunscreen composition is available in the defined form selected from a group consisting of a skin cream, a skin lotion, a powder, a gel, and a sprayable liquid.

Abstract: This disclosure relates generally to a sunscreen composition containing visibly transparent biocompatible ultraviolet blocking polymer nanoparticles. The sunscreen composition comprising polydimethylsiloxane (PDMS) nanoparticles, at least one flavoring agent, at least one coloring agent, at least one stabilizer, and at least one preservative, in a defined form, wherein size of the PDMS nanoparticles ranging from 200 to 1200 nm. The size of the PDMS nanoparticles ranging from 200 to 500 nm for air medium and from 800 to 1200 nm for water medium. The PDMS nanoparticles comprise a PDMS polymer having terminal functional group selected from alkyl, alkoxy, vinyl, hydroxyl, or a combination thereof. The sunscreen composition is available in the defined form selected from a group consisting of a skin cream, a skin lotion, a powder, a gel, and a sprayable liquid.

Abstract: Disclosed is a method for producing a coated substrate using a compact, easy to handle and automated coating apparatus that can prepare coated composite in a single batch process, with sufficient control over each portion of the coating apparatus. The coating apparatus may include a coating unit, a drying unit and a pressing unit sequentially arranged in a single line to produce the coated substrate.

Abstract: Present disclosure provides a process for the synthesis of visible light responsive doped titania photocatalysts. The process involves step a) milling a mixture containing titania and a precursor compound, the compound selected from the group consisting of chloroauric acid and a mixture containing chloroauric acid and silver nitrate, in the presence of water and oxide milling media, at a temperature in the range of 20 to 50° C. for a period of 60-120 minutes, to form a slurry, wherein the amount of water is in the range of 15 to 25% by weight of the total mixture; and b) filtering the slurry to separate the oxide milling media and obtain a filtrate containing doped titania nanoparticles.

Abstract: Present disclosure provides a process for the synthesis of doped titania nanoparticle having photocatalytic activity greater than 90% at 2 hours under sunlight irradiation. The process involves step a) milling a mixture containing anatase titania and a precursor compound, the compound selected from the group consisting of metal and non-metal salts, in the presence of water and oxide milling media, at a temperature in the range of 20 to 50° C. for a period of 60-120 minutes, to form a slurry, wherein the amount of water is in the range of 15 to 25% by weight of the total mixture; and b) filtering the slurry to separate the oxide milling media and obtain a filtrate containing doped titania nanoparticles.

Abstract: Present disclosure provides a process for the synthesis of visible light responsive doped titania photocatalysts. The process involves step a) milling a mixture containing titania and a precursor compound, the compound selected from the group consisting of chloroauric acid and a mixture containing chloroauric acid and silver nitrate, in the presence of water and oxide milling media, at a temperature in the range of 20 to 50° C. for a period of 60-120 minutes, to form a slurry, wherein the amount of water is in the range of 15 to 25% by weight of the total mixture; and b) filtering the slurry to separate the oxide milling media and obtain a filtrate containing doped titania nanoparticles.

Abstract: Disclosed is a method for producing a coated substrate using a compact, easy to handle and automated coating apparatus that can prepare coated composite in a single batch process, with sufficient control over each portion of the coating apparatus. The coating apparatus may include a coating unit, a drying unit and a pressing unit sequentially arranged in a single line to produce the coated substrate.

Abstract: Present disclosure provides a process for the synthesis of doped titania nanoparticle having photocatalytic activity greater than 90% at 2 hours under sunlight irradiation. The process involves step a) milling a mixture containing anatase titania and a precursor compound, the compound selected from the group consisting of metal and non-metal salts, in the presence of water and oxide milling media, at a temperature in the range of 20 to 50° C. for a period of 60-120 minutes, to form a slurry, wherein the amount of water is in the range of 15 to 25% by weight of the total mixture; and b) filtering the slurry to separate the oxide milling media and obtain a filtrate containing doped titania nanoparticles.