Abstract: The strength properties of chemical cellulose pulp (particularly kraft pulp) are improved by substituting a cold impregnation soak for conventional impregnation procedures. After steaming, wood chips are soaked in an alkaline liquid at a temperature of about 80-110° C. (preferably 80-100° C., or 90-105° C.) for between one-half-72 hours (typically about 2-4 hours) at a pressure of about 0-15 bar (preferably about 1-5 bar), to dissolve at least about 8% of the wood (preferably about 10-20%) and at least about 15% of the lignin. The alkaline liquid used preferably contains sulfide (e.g. black liquor, green liquor, white liquor, or mixtures thereof), but almost any alkaline liquid having an alkali concentration of about 1.0 mole of NaOH/liter or less (typically about 0.75 m/l or less) is suitable. The wood chips are then raised to a cooking temperature of about 145-180° C. and cooked to produce the cellulose chemical pulp.

Abstract: The strength properties of chemical cellulose pulp (particularly kraft pulp) are improved by substituting a cold impregnation soak for conventional impregnation procedures. After steaming, wood chips are soaked in an alkaline liquid at a temperature of about 80-110° C. (preferably 80-100° C., or 90-105° C.) for between one-half-72 hours (typically about 2-4 hours) at a pressure of about 0-15 bar (preferably about 1-5 bar), to dissolve at least about 8% of the wood (preferably about 10-20%) and at least about 15% of the lignin. The alkaline liquid used preferably contains sulfide (e.g. black liquor, green liquor, white liquor, or mixtures thereof), but almost any alkaline liquid having an alkali concentration of about 1.0 mole of NaOH/liter or less (typically about 0.75 m/l or less) is suitable. The wood chips are then raised to a cooking temperature of about 145-180° C. and cooked to produce the cellulose chemical pulp.

Abstract: The strength properties of chemical cellulose pulp (particularly kraft pulp) are improved by substituting a cold impregnation soak for conventional impregnation procedures. After steaming, wood chips are soaked in an alkaline liquid at a temperature of about 80-110° C. (preferably 80-100° C., or 90-105° C.) for between one-half-72 hours (typically about 2-4 hours) at a pressure of about 0-15 bar (preferably about 1-5 bar), to dissolve at least about 8% of the wood (preferably about 10-20%) and at least about 15% of the lignin. The alkaline liquid used preferably contains sulfide (e.g. black liquor, green liquor, white liquor, or mixtures thereof), but almost any alkaline liquid having an alkali concentration of about 1.0 mole of NaOH/liter or less (typically about 0.75 m/l or less) is suitable. The wood chips are then raised to a cooking temperature of about 145-180° C. and cooked to produce the cellulose chemical pulp.

Abstract: The strength properties of chemical cellulose pulp (particularly kraft pulp) are improved by substituting a cold impregnation soak for conventional impregnation procedures. After steaming, wood chips are soaked in an alkaline liquid at a temperature of about 80-110° C. (preferably 80-100° C., or 90-105° C.) for between one-half-72 hours (typically about 2-4 hours) at a pressure of about 0-15 bar (preferably about 1-5 bar), to dissolve at least about 8% of the wood (preferably about 10-20%) and at least about 15% of the lignin. The alkaline liquid used preferably contains sulfide (e.g. black liquor, green liquor, white liquor, or mixtures thereof), but almost any alkaline liquid having an alkali concentration of about 1.0 mole of NaOH/liter or less (typically about 0.75 m/l or less) is suitable. The wood chips are then raised to a cooking temperature of about 145-180° C. and cooked to produce the cellulose chemical pulp.

Abstract: The strength properties of chemical cellulose pulp (particularly kraft pulp) are improved by substituting a cold impregnation soak for conventional impregnation procedures. After steaming, wood chips are soaked in an alkaline liquid at a temperature of about 80-110° C. (preferably 80-100° C., or alternatively 90-105° C.) for between one-half-72 hours (typically about 2-4 hours) at a pressure of about 0-15 bar (preferably about 1-5 bar), to dissolve at least about 8% of the wood (preferably about 10-20%) and at least about 15% of the lignin. The alkaline liquid used preferably contains sulfide (e.g. black liquor, green liquor, white liquor, or mixtures thereof), but almost any alkaline liquid having an alkali concentration of about 1.0 mole of NaOH/liter or less (typically about 0.75 m/l or less) is suitable. The wood chips are then raised to a cooking temperature of about 145-180° C. and cooked to produce the cellulose chemical pulp.