Abstract: The invention relates to an aluminum alloy strip with improved surface optics, which is fabricated via hot and/or cold rolling, and consists of a type AA 3xxx, AA 5xxx, AA 6xxx or AA 8xxx aluminum alloy. The object of proposing an aluminum alloy strip that is suitable for attractive and precious surface optics despite the elevated percentage of alloy constituents is achieved in that, after degreasing, the finish-rolled aluminum alloy strip exhibits an increase in the luminance value L*(?L) in relation to the rolled-greasy state of more than 5 while measuring the color of the surface in the CIE L*a*b* color space using a standard illuminant D65 and a normal observation angle of 10°, excluding direct reflection in 45°/0° geometry.

Abstract: The invention relates to an aluminum alloy strip with improved surface optics, which is fabricated via hot and/or cold rolling, and consists of a type AA 3xxx, AA 5xxx, AA 6xxx or AA 8xxx aluminum alloy. The object of proposing an aluminum alloy strip that is suitable for attractive and precious surface optics despite the elevated percentage of alloy constituents is achieved in that, after degreasing, the finish-rolled aluminum alloy strip exhibits an increase in the luminance value L*(?L) in relation to the rolled-greasy state of more than 5 while measuring the color of the surface in the CIE L*a*b* color space using a standard illuminant D65 and a normal observation angle of 10°, excluding direct reflection in 45°/0° geometry.

Abstract: A method for the production of an absorber plate for solar collectors from a strip of metal, in particular of aluminum or an aluminum alloy, includes coating the strip using a coil coating process with a highly selective coating, which has very good absorptive properties for sunlight and ensures very little heat emission.

Abstract: Method for making an absorber coating for solar heating and a coating as such to be applied on a metal substrate, in particular a coating to be applied on a thin aluminium metal sheet. The coating is of the sol-gel type based on a metal oxide precursor where pigment particles are intimately mixed into the precursor followed by application of the mixed sol lacquer on the substrate and thereafter reaction in humid air at a required temperature to obtain the sol-gel coating. The precursor may preferably be a CeO2 (NO3) based sol with preferably 20% CeO2 having a particle size of 10-20 nm and a pH of 1.5. Further the pigment may be a manganese ferrite black spinel, Mn3Cu2FeO8.

Abstract: A method for the production of an absorber plate for solar collectors from a strip of metal, in particular of aluminum or an aluminum alloy, includes coating the strip using a coil coating process with a highly selective coating, which has very good absorptive properties for sunlight and ensures very little heat emission.