Abstract: An alloy is provided. The alloy comprises (in % by weight): silicon 2.0%-4.5%, in particular 2.3%-3.9%, carbon 2.9%-4.0%, in particular 3.2%-3.7%, niobium 0.05%-0.7%, in particular 0.05%-0.6%, molybdenum 0.3%-1.5%, in particular 0.4%-1.0%, and optionally cobalt 0.1%-2.0%, in particular 0.1%-1.0%, manganese ?0.3%, in particular 0.15-0.30%, nickel ?0.5%, in particular ?0.3%, magnesium ?0.07%, in particular at least 0.03%, phosphorus ?0.05%, in particular 0.02%-0.035%, sulfur ?0.012%, in particular ?0.005%, chromium ?0.1%, in particular ?0.05%, antimony ?0.004%, in particular ?0.003%, and iron.

Abstract: Known cast iron alloys have use limits in respect of the temperature. An alloy (in a weight percentage) including silicon 2.0%-4.5%, carbon 2.9%-4.0%, niobium 0.05%-0.7%, molybdenum 0.3%-1.5%, optionally cobalt 0.1%-2.0%, manganese?0.3%, nickel?0.5%, magnesium?0.07%, phosphorus?0.05%, sulphur?0.012%, chromium?0.1%, antimony?0.004%, and, iron, is provided.

Abstract: The invention relates to a monotectic aluminium plain bearing alloy, comprising 5 to 20 wt. % bismuth, 3 to 20 wt. % zinc, 1 to 4 wt. % copper and additionally several of the components manganese, vanadium, niobium, nickel, molybdenum, cobalt, iron, tungsten, chromium, silver, calcium, scandium, cerium, beryllium, antimony, boron, titanium, carbon and zirconium in amounts up to 5 wt. % and aluminium to make 100 wt. %, produced by strip casting and during the subsequent production process for plain bearings, after rolling or roll-bonding, subjected to a heat treatment at ca. 270 to 400° C. Long bismuth particles or sheets, produced by rolling or roll-bonding can thus be recoagulated to give finely-distributed spherical drops with a size in the 20 ?m range and smaller.

Abstract: The invention relates to a copper alloy which is used for mechanically stressed components which, during operation, are subjected to vibrations and/or impacts to produce the same, and have particularly good mechanical damping properties. The composition of said copper alloy depends upon the utilisation temperature or working temperature of the component. Said copper alloy consists of 2-12 wt.-% manganese, 5-14 wt.-% aluminum and individually or in total 0-18 wt.-% of one or several elements, nickel, iron, cobalt, zinc, silicon, vanadium, niobium, molybdenum, chromium, tungsten, beryllium, lithium, yttrium, cerium, scandium, calcium, titanium, phosphorous, zirconium, boron, nitrogen, carbon, whereby each element does not contain more that 6% and 100 wt.-% copper.