Abstract: A lithium-rich oxide positive electrode material. At least one unit lattice parameter (a, b, c) of the material decreases as the temperature increases at a temperature between 50 to 350 degrees. After treatment for 0.5 to 10 hours under the condition of 150 to 350° C., the degree of ordering of the material structure is increased, and the material has a higher discharge specific capacity and a higher discharge voltage when applied to a positive electrode of a lithium ion battery.

Abstract: A lithium-rich manganese-based positive electrode material represented by formula (I). In an X-ray diffraction pattern of the lithium-rich manganese-based positive electrode material, a ratio of a diffraction peak intensity of a Bragg angle near 18.7° to a diffraction peak intensity of a Bragg angle near 44.6° is 1.10 to 1.24. A method for preparing the lithium-rich manganese-based positive electrode material comprises: mixing a lithium-rich manganese-based compound with a lithium remover; and under the effect of the lithium remover, removing part of Li2O from Li2MnO3 in the lithium-rich manganese-based compound, so as to obtain the lithium-rich manganese-based positive electrode material. Due to the reduction of the irreversible product Li2O, the initial coulombic efficiency is improved; because of existence of lithium vacancy and oxygen vacancy, the lithium-rich manganese-based positive electrode material has good rate performance and cycle performance.

Abstract: A lithium-rich manganese-based positive electrode material represented by formula (I). In an X-ray diffraction pattern of the lithium-rich manganese-based positive electrode material, a ratio of a diffraction peak intensity of a Bragg angle near 18.7° to a diffraction peak intensity of a Bragg angle near 44.6° is 1.10 to 1.24. A method for preparing the lithium-rich manganese-based positive electrode material comprises: mixing a lithium-rich manganese-based compound with a lithium remover; and under the effect of the lithium remover, removing part of Li2O from Li2MnO3 in the lithium-rich manganese-based compound, so as to obtain the lithium-rich manganese-based positive electrode material.