Abstract: Disclosed is a method for manufacturing a large-area thin-film solid oxide fuel cell, the method including: preparing an anode support slurry, an anode functional layer slurry, an electrolyte slurry, and a buffer layer slurry for tape casting; preparing an anode support green film, an anode functional layer green film, an electrolyte green film, and a buffer layer green film by tape casting the slurries onto carrier films; staking the green films, followed by hot press and warm iso-static press (WIP), to prepare a laminated body; and co-sintering the laminated body.

Abstract: Disclosed is a method for manufacturing a large-area thin-film solid oxide fuel cell, the method including: preparing an anode support slurry, an anode functional layer slurry, an electrolyte slurry, and a buffer layer slurry for tape casting; preparing an anode support green film, an anode functional layer green film, an electrolyte green film, and a buffer layer green film by tape casting the slurries onto carrier films; staking the green films, followed by hot press and warm iso-static press (WIP), to prepare a laminated body; and co-sintering the laminated body.

Abstract: Provided is an interconnect for a solid oxide fuel cell including ferritic stainless steel dispersed with nano-CeO2 and Nb2O5. The interconnect for the solid oxide fuel cell of the present disclosure includes nano-CeO2 and Nb2O5 having specific particle sizes in specific contents, thereby suppressing the formation of the insulating layer SiO2 and exhibiting an excellent improvement effect of high-temperature characteristics such as oxidation resistance and sheet resistance.