Abstract: The present invention relates to a crosslinkable polymer composition comprising (A) a high density ethylene homo- or copolymer having a density, determined according to ISO 1183, of at least 930 kg/m3, and (B) a copolymer of ethylene with a silane groups-containing comonomer having a content of silane groups-containing comonomer of not more than 4.0 wt %, wherein the polymer composition passes the tracking resistance test, determined according to IEC60587 (2007), method 2A at 4.5 kV for 1 h and 4.75 kV for 1 h on compression molded plaques prepared according to ISO 11357. The present invention further relates to a track resistant wire or cable, preferably a power cable or an optical cable comprising at least one layer of the above polymer composition or to the use of the polymer composition in a wire or cable for increasing track resistance, and/or for increasing fire retardancy along the length of the wire or cable.

Abstract: An article comprising a layer element (LE) of at least two layers, first layer and second layer.

Abstract: The present invention relates to a polyolefin composition comprising a cross-linkable polyolefin with hydrolysable silane groups, an acidic silanol condensation catalyst, wherein the acidic silanol condensation catalyst is present in an amount of 0.0001 to 3 wt. % of the polyolefin composition, at least one UV stabilizer selected from the group consisting of phenols, benzophenones and/or combinations thereof, wherein component (C) is present in an amount of 0.0001 to 0.35 wt. % of the polyolefin composition, and/or at least one UV stabilizer selected from triazines, wherein component (D) is present in an amount of 0.0001 to 2.0 wt. % of the polyolefin composition. The present invention also relates to an article comprising such a composition, and to the use of such a composition for the production of an article.

Abstract: The present invention relates to a photovoltaic module comprising a solar cell element and an insulation material laminated to at least one side of the solar cell element wherein the insulation material comprises an olefin copolymer which comprises silane group-containing monomer units, to a process for the production of such a photovoltaic module, and to the use of an olefin copolymer which comprises silane group-containing monomer units for the production of an insulation layer of a photovoltaic module.

Abstract: The present invention relates to a polyolefin composition comprising a cross-linkable polyolefin with hydrolysable silane groups; an acidic silanol condensation catalyst, wherein the acidic silanol condensation catalyst (B) is present in an amount of 0.0001 to 3 wt. % of the polyolefin composition; at least one UV stabilizer selected from the group consisting of phenols, triazines, benzophenones, triazoles and/or combinations thereof; and at least one UV stabilizer of the hindered amine type (HALS) which is present in an amount of 0.0001 to 0.1 wt. % of the polyolefin composition. The present invention also relates to an article comprising such a composition, and to the use of such a composition for the production of an article.

Abstract: The invention relates to the use of a polyethylene composition comprising one or more ethylene copolymer(s) wherein the ethylene copolymer is a terpolymer containing monomer units with polar groups and monomer units with hydrolysable silane groups, wherein the monomer units with polar groups are present in an amount of more than 5 mol. % based on the total polyethylene composition, and a silanol condensation catalyst in an amount of 0.0001 to 5 wt. %, based on the total polyethylene composition for improving the adhesion between a layer of a cable comprising the polyethylene composition and a polyurethane resin.

Abstract: The present invention concerns a polyethylene composition comprising (A) an ethylene co-polymer containing monomer units with hydrolysable silane-groups, and (B) one or more ethylene co-polymers selected from the group of (B1) an ethylene co-polymer containing monomer units with hydroxyl groups, (B2) an ethylene co-polymer containing monomer units with (meth-)acrylate groups, and (B3) an ethylene co-polymer containing monomer units with hydroxyl groups and (meth-)acrylate groups, a cable comprising a layer (1) which comprises one or more ethylene copolymers selected from the group of (B1), (B2) and (B3) and to the use of one or more ethylene co-polymers selected from the group of (B1), (B2) and (B3) for improving the adhesion between a layer of a cable comprising the ethylene co-polymer(s) and a polyurethane resin.

Abstract: The present invention relates to a cross-linkable, grafted or non-grafted polymer composition comprising a cross-linkable copolymer containing hydrolysable silane groups. The invention further relates to a crosslinked polymer composition obtained by cross-linking the cross-linkable copolymer containing hydrolysable silane groups and an article comprising the same. The present invention also relates to the use of one or more cross-linking accelerators for accelerating the crosslinking of a cross-linkable copolymer containing hydrolysable silane groups.

Abstract: The invention is a polymer composition for film layer comprising less than 50 wt % of a copolymer of ethylene with silane group(s) containing units and at least 50 wt % of a thermoplastic polyolefine free from silane group(s) wherein the polymer composition has creep of less than 1 mm at 90° C., and an adhesion above 20 N/cm. The invention relates to a laminated article with at least one film layer of the polymer composition and a substrate.

Abstract: A polymer composition with a polymer of ethylene with a comonomer with silane group(s) containing units and an additive that is an organic compound with at least one amine moiety that has a gel content less than 10 wt % after 7 days at ambient conditions and a gel content of at least 15 wt % gel content after 14 days at 100° C. The film can be used in a laminate.

Abstract: The present invention relates to a polymer composition, which is a silanol condensation catalyst masterbatch, comprises a matrix, comprising a silane containing drying agent, and at least one silanol condensation catalyst, wherein each catalyst has a water content which is 0.

Abstract: The invention relates to a polyethylene having a melt flow rate at (2.16) kg loading (MFR2), determined according to method ISO1133-1:2011, which MFR2 is A g/10 min and A1?A?A2; wherein A1 is (0.5) and A2 is (1.70), and containing a total amount of vinyl groups which is B vinyl groups per (1000) carbon atoms, and B1?B, wherein B1 is (0.45), determined according to method ASTM D6248-98, a polymer composition, an article being e.g. a cable, e.g. a power cable, and processes for producing a polyethylene, a polymer composition and an article, and an article; useful in different end applications, such as wire and cable (W&C) applications.

Abstract: The present invention is directed to a polyolefin composition which has flame retardant and/or fire resistant properties and is suitable as flame retardant and/or fire resistant layer of a wire or cable. The polyolefin composition of the present invention comprises an polyolefin homo- or copolymer, a metal hydroxide in an amount of 30 to 60 wt % based on the weight of the polyolefin composition, and a borate in an amount of 5 to 25 wt %, based on the weight of the polyolefin composition. The present invention is further directed to a wire or cable comprising one or more layers, wherein at least one layer thereof is obtained from the polyolefin composition of the present invention. Finally, the present invention is further directed to the use of a polyolefin composition of the present invention as a flame retardant layer of a wire or cable.

Abstract: The present invention is directed to a polyolefin composition which has flame retardant and/or fire resistant properties and is suitable as flame retardant and/or fire resistant layer of a wire or cable. The polyolefin composition of the present invention comprises an polyolefin homo- or copolymer, ground magnesium hydroxide having particle size distribution D50 of 1.5 to 5.0 ?m in an amount of 30 to 65 wt % based on the weight of the polyolefin composition, and a silicone fluid or gum in an amount of 0.1 to 20 wt % based on the weight of the polyolefin composition. The present invention is further directed to a wire or cable comprising one or more layers, wherein at least one layer thereof is obtained from the polyolefin composition of the present invention. Finally, the present invention is further directed to the use of a polyolefin composition of the present invention as a flame retardant layer of a wire or cable.

Abstract: The invention is a polymer composition for film layer comprising less than 50 wt % of a copolymer of ethylene with silane group(s) containing units and at least 50 wt % of a thermoplastic polyolefine free from silane group(s) wherein the polymer composition has creep of less than 1 mm at 90° C., and an adhesion above 20 N/cm. The invention relates to a laminated article with at least one film layer of the polymer composition and a substrate.

Abstract: The present invention relates to low density polyethylene having a melt flow rate (MFR) according to ISO 1133 (190° C., 2.16 kg) which is higher than 4.0 g/10 min, a storage modulus G?, measured at a loss modulus G? of 5 kPa, which is above 3000 Pa and a vinylidene content which is at least 24/100 k C, compositions, a process for production of the low density polyethylene, a low density polyethylene which is obtainable by the process, a continuous ethylene polymerization method for introducing vinylidene in a low density polyethylene, a method for an extrusion coating process or an extrusion lamination process, an article, e.g. an extrusion article, an extrusion lamination article, film blowing article, film casting article, wire and cable extrusion article, injection moulding article, blow moulding article or pipe extrusion article, and uses of the low density polyethylene.

Abstract: The present invention relates to a wire or cable comprising a conductor coated with an insulation composition, wherein said insulation composition comprises: i) a polyethylene copolymer having a melting point of 105° C. or less; and ii) a hindered amine light stabiliser (HALS) comprising at least one 2,2,6,6-tetramethyl-piperidinyl group present in an amount of 0.5 to 1.5 wt %.

Abstract: A polymer composition with a polymer of ethylene with a comonomer with silane group(s) containing units and an additive that is an organic compound with at least one amine moiety that has a gel content less than 10 wt % after 7 days at ambient conditions and a gel content of at least 15 wt % gel content after 14 days at 100° C. The film can be used in a laminate.

Abstract: The present invention relates to a polymer composition, to a layer element, preferably to at least one layer element of a photovoltaic module, comprising the polymer composition and to an article which is preferably said at least one layer of a layer element, preferably of a layer element of a photovoltaic module.

Abstract: The present invention relates to a photovoltaic module comprising a solar cell element and an insulation material laminated to at least one side of the solar cell element wherein the insulation material comprises an olefin copolymer which comprises silane group-containing monomer units, to a process for the production of such a photovoltaic module, and to the use of an olefin copolymer which comprises silane group-containing monomer units for the production of an insulation layer of a photovoltaic module.