Abstract: Firing of ceramic cores (1) is important in order to achieve manufacturing processes. These ceramic cores (1) are generally formed in a “green” state which has limited mechanical strength and may be distorted during the firing process by non-uniform thermal effects, etc. By providing a tube or containment 2 which is located on a saggar base 3 and surrounded by firing media 4, it is possible to achieve an initial pre-firing step whereby the “green” state core 1 is located through a stem 1a in an initial partial depth 5 of firing media 4 in the tube or containment 2 until it achieves a sufficient mechanical strength to enable positional adjustment. Thus, the green core will be pre-fired in a kiln solely supported through the stem 1a and then the core adjusted using a tool such as an engineering rule.

Abstract: Firing of ceramic cores (1) is important in order to achieve manufacturing processes. These ceramic cores (1) are generally formed in a “green” state which has limited mechanical strength and may be distorted during the firing process by non-uniform thermal effects, etc. By providing a tube or containment 2 which is located on a saggar base 3 and surrounded by firing media 4, it is possible to achieve an initial pre-firing step whereby the “green” state core 1 is located through a stem 1a in an initial partial depth 5 of firing media 4 in the tube or containment 2 until it achieves a sufficient mechanical strength to enable positional adjustment. Thus, the green core will be pre-fired in a kiln solely supported through the stem 1a and then the core adjusted using a tool such as an engineering rule.