Abstract: The invention is a method of removing lithium from aluminum-lithium alloys. Aluminum-lithium alloys (64) and a metal halide flux (68) are fed into a rotary furnace (10) at a raised and cool end thereof. The temperature at the cool end is above that of the melting point of the flux (68) and below that of the melting point of the alloy (64). The flux is thus melted as it enters the furnace. It coats the solid alloy and the furnace refractory lining (46) to prevent contact between the refractories and the molten metal unitl the lithium content of the aluminum has been reduced to an acceptable level. A rotation of the furnace moves the alloy (64) and molten flux (68) toward a lower and hotter end at which the temperature is such to melt the aluminum. At this time the lithium is removed from the alloy (64) and is absorbed within the flux (68). The aluminum (70) is then drained from the furnace at its lower end.