Abstract: A pre-oxidation heat-treatment method to heat treat nickel-base alloys containing, in weight percent, 1.8 wt. % minimum aluminum and 10 wt. % minimum chromium is disclosed that can provide an aluminum oxide scale having a thickness of at least 100 nanometers (nm) that contains little or no chromium oxide (Cr2O3), nickel oxide (NiO), titanium oxide (TiO2), silicon oxide (SiO2) or mixed oxides. The method involves heating a workpiece made from an alloy in a furnace containing a flowing argon atmosphere at a pressure of at least 500 microns, and at a temperature of 1400° F. to 2150° F. until a continuous scale of aluminum oxide (Al2O3) is formed on at least one surface of the workpiece. The flowing argon atmosphere in the pre-oxidation heat-treatment method should contain less than 0.1 vol. % oxygen content, and the gas flux is at least 1 mL/min·cm2.

Abstract: Techniques for carbon sequestration and storage site selection are presented.

Abstract: An alloy comprising about 0.5 weight percent to about 2 weight percent carbon, about 15 weight percent to about 30 weight percent chromium, about 4 weight percent to about 12 weight percent nickel, up to about 3 weight percent manganese, up to about 2.5 weight percent silicon, up to about 1 weight percent zirconium, up to about 3 weight percent molybdenum, up to about 3 weight percent tungsten, up to about 0.5 weight percent boron, up to about 0.5 weight percent impurities, and iron.

Abstract: A method for making an oxidation resistant article, including (a) depositing a layer of a Pt group metal on a substrate to form a platinized substrate; and (b) depositing on the platinized substrate layer of Pt group metal a layer of a reactive element selected from the group consisting of Hf, Y, La, Ce and Zr and combinations thereof to form a surface modified region thereon, wherein the surface modified region includes the Pt-group metal, Ni, Al and the reactive element in relative concentration to provide a ?-Ni+?-Ni3Al phase constitution.

Abstract: An alloy comprising about 0.5 weight percent to about 2 weight percent carbon, about 15 weight percent to about 30 weight percent chromium, about 4 weight percent to about 12 weight percent nickel, up to about 3 weight percent manganese, up to about 2.5 weight percent silicon, up to about 1 weight percent zirconium, up to about 3 weight percent molybdenum, up to about 3 weight percent tungsten, up to about 0.5 weight percent boron, up to about 0.5 weight percent impurities, and iron.

Abstract: A method for making an oxidation resistant article, including (a) depositing a layer of a Pt group metal on a substrate to form a platinized substrate; and (b) depositing on the platinized substrate layer of Pt group metal a layer of a reactive element selected from the group consisting of Hf, Y, La, Ce and Zr and combinations thereof to form a surface modified region thereon, wherein the surface modified region includes the Pt-group metal, Ni, Al and the reactive element in relative concentration to provide a ?-Ni+??-Ni3Al phase constitution.

Abstract: A method for making an oxidation resistant article, including (a) depositing a layer of a Pt group metal on a substrate to form a platinized substrate; and (b) depositing on the platinized substrate layer of Pt group metal a layer of a reactive element selected from the group consisting of Hf, Y, La, Ce and Zr and combinations thereof to form a surface modified region thereon, wherein the surface modified region includes the Pt-group metal, Ni, Al and the reactive element in relative concentration to provide a ?-Ni+??-Ni3Al phase constitution.

Abstract: A method for making an oxidation resistant article, including (a) depositing a layer of a Pt group metal on a substrate to form a platinized substrate; and (b) depositing on the platinized substrate layer of Pt group metal a layer of a reactive element selected from the group consisting of Hf, Y, La, Ce and Zr and combinations thereof to form a surface modified region thereon, wherein the surface modified region includes the Pt-group metal, Ni, Al and the reactive element in relative concentration to provide a ?-Ni+??-Ni3Al phase constitution.