Abstract: A self-lubricating, friction and wear reducing composite useful over a wide temperature range is described herein. The composite includes metal bonded chromium oxide dispersed in a metal binder having a substantial amount of nickel. The composite contains a fluoride of at least one Group I, Group II, or rare earth metal, and optionally a low temperature lubricant metal.

Abstract: A self lubricating, friction and wear reducing composite material useful over a wide temperature range of from cryogenic temperature up to about 900.degree. C. contains 60-80 wt. % of particulate Cr.sub.2 O.sub.3, dispersed in a metal binder of a metal alloy containing Cr and at least 50 wt. % of Ni, Cr or a mixture of Ni and Cr. It also contains 5-20 wt. % of a fluoride of at least one Group I, Group II, or rare earth metal and, optionally, 5-20 wt. % of a low temperature lubricant metal. Such as Ag, Au, Pt, Pd, Rh and Cu. This composite exhibits less oxidation instability and less abrasiveness than composites containing chromium carbide, is readily applied using plasma spray and can be ground and polished with a silicon carbide abrasive.

Abstract: A chill plate for continuous casting of high melting temperature metals. The chill plate is made from a copper substrate and subsequently coated by plasma spraying. The copper mold coating composition consists of a copper alloy, 10 to 20% by volume refractory powder having a mean particle size between about 5 to 250 microns, and 3 to 7% by volume of a flammable metal powder.