Abstract: Some examples of a method for manufacturing an electrode material for electrolytic hydrogen generation are described. Tungsten salt and nickel salt are mixed in a determined molar ratio on a carbon support by effectively controlling synthesis temperature and composition. Water and adsorbed oxygen, produced by mixing the tungsten salt and nickel salt are removed. Then, methane gas is flowed over the mixture resulting in the electrode material. The electrode material is suitable for use as a catalyst in electrolytic hydrogen generation processes, for example, at an industrial scale, to produce large quantities of hydrogen.

Abstract: Some examples of a method for manufacturing an electrode material for electrolytic hydrogen generation are described. Tungsten salt and nickel salt are mixed in a determined molar ratio on a carbon support by effectively controlling synthesis temperature and composition. Water and adsorbed oxygen, produced by mixing the tungsten salt and nickel salt are removed. Then, methane gas is flowed over the mixture resulting in the electrode material. The electrode material is suitable for use as a catalyst in electrolytic hydrogen generation processes, for example, at an industrial scale, to produce large quantities of hydrogen.

Abstract: Some examples of a method for manufacturing an electrode material for electrolytic hydrogen generation are described. Tungsten salt and nickel salt are mixed in a determined molar ratio on a carbon support by effectively controlling synthesis temperature and composition. Water and adsorbed oxygen, produced by mixing the tungsten salt and nickel salt are removed. Then, methane gas is flowed over the mixture resulting in the electrode material. The electrode material is suitable for use as a catalyst in electrolytic hydrogen generation processes, for example, at an industrial scale, to produce large quantities of hydrogen.

Abstract: Some examples of a method for manufacturing an electrode material for electrolytic hydrogen generation are described. Tungsten salt and nickel salt are mixed in a determined molar ratio on a carbon support by effectively controlling synthesis temperature and composition. Water and adsorbed oxygen, produced by mixing the tungsten salt and nickel salt are removed. Then, methane gas is flowed over the mixture resulting in the electrode material. The electrode material is suitable for use as a catalyst in electrolytic hydrogen generation processes, for example, at an industrial scale, to produce large quantities of hydrogen.