Abstract: A fire-resistant sheet-like molded article comprising a resin composition and having the relationship between the initial thickness t (mm) and temperature difference ?T(° C.) between one side and the reverse side after heating of said one side at 500° C. for 1 hour as represented by: ?T?0.015t4?0.298t3+1.566t2+30.151t, and having the initial bulk density at 25° C. of 0.8 to 8.0 g/cm3 and the bulk density after 1 hour of heating at 500° C. of 0.05 to 0.5 g/cm3 is provided along with a method of fabricating a fire-resistant structural steel and fire-resistant wall.

Abstract: A fire-resistant sheet-like molded article comprising a resin composition and having the relationship between the initial thickness t (mm) and temperature difference &Dgr;T(° C.) between one side and the reverse side after heating of said one side at 500° C.

Abstract: A fire-resistant sheet-like molded article having flame resistance and capable of producing good fire-resisting properties as the result of residues after combustion having sufficient shape-retaining property and, further, having good workability, a fire-resistant laminate for covering structural steels and a fire-resistant structural material for walls in which said molded article is used as well as a method of fabricating a fire-resistant structural steel and a fire-resistant wall. A fire resistant sheet-like molded article comprising a resin composition and having the-relationship between the initial thickness t (mm) and temperature difference &Dgr;T (° C.) between one side and the reverse side after heating of said one side at 500° C. for 1 hour as represented by: &Dgr;T≧0.015t4−0.298t3+1.566t2+30.151t, and having the initial bulk density at 25° C. of 0.8 to 2.0 g/cm3 and the bulk density after 1 hour of heating at 500° C. of 0.05 to 0.5 g/cm3.