Abstract: A method of manufacturing a low-core-loss oriented electrical steel sheet. Thread-like grooves are formed in a cold-rolled grain oriented electrical steel sheet having a final thickness of about 0.27 mm or less in a direction within the range of about 30.degree. from the direction perpendicular to the rolling direction. The grooves and sheet satisfy the equationlog d.gtoreq.0.6 Ra+0.4where d is the groove depth (.mu.m), and Ra is the mean surface roughness of the steel sheet cold-rolled to final gauge. The steel sheet is thereafter decarburization annealed and final texture annealed.

Abstract: A low-iron loss grain oriented electromagnetic steel sheet subjected to final finishing annealing has a plurality of linear grooves formed on surface of the steel sheet in a direction across the rolling direction, so as to improve the magnetic characteristics of the steel sheet. The linear grooves have a substantially rectangular cross-sectional shape in which the angle of a groove side wall to the direction of the thickness of the sheet is about 60.degree. or less. Projections are present at a bottom portion of the groove, and the depth at the top of the projection at the groove bottom is at least about 1/2 of the maximum groove depth. The steel sheet maintains a low iron loss even after stress relief annealing. The present invention provides a method of stably producing the steel sheet.

Abstract: A method of producing a grain oriented silicon steel sheet is adapted to lower the iron loss. A silicon steel slab, containing about 2.0 to 4.0 weight % of Si and an inhibitor-forming amount of S, or Se, or both, is hot rolled. After the hot rolled steel sheet is annealed when necessary, the steel sheet is cold rolled into a cold rolled steel sheet having a final thickness by performing cold rolling either one time or a plurality of times with intermediate annealing therebetween, the cold rolled steel sheet then being subjected to decarburization, coating of the surface of the steel sheet with an annealing separation agent mainly comprising MgO, secondary recrystallization annealing, and purification annealing. In the cold rolling step, an oxide layer exists on the surface of the steel sheet. Specifically, in the cold rolling step, rolling oil is supplied only at the entrance of the rolling mill used, and an oxide layer having a thickness of about 0.05 to 5 .mu.m is generated.

Abstract: Method of manufacturing a grain oriented silicon steel sheet. An annealing separating agent mainly composed of MgO is coated on a surface of a decarburized silicon steel sheet. The silicon steel sheet is subjected to secondary recrystallization annealing and then purification annealing. The annealing separating agent contains Ti oxide or a Ti compound which can be oxidized by heating. The purification annealing is conducted in steps. A non-oxidizing atmosphere having a high nitrogen concentration is present in one step. A hydrogen atmosphere having a low nitrogen concentration is present in a subsequent step.

Abstract: The iron loss is reduced by irradiating plasma flame to the surface of the grain oriented silicon steel sheet, wherein the irradiation interval (l) of plasma flame is controlled so as to satisfy the following equation (1):22-2.5D.ltoreq.l.ltoreq.36-2.5D (1)(D is an average secondary recrystallized grain size of the steel sheet).

Abstract: A process and an apparatus for improving iron loss of electromagnetic steel sheet or amorphous material are disclosed. In this case, the steel sheet or amorphous material is subjected to an irradiation of plasma flame under specified conditions.

Abstract: A process and an apparatus for improving iron loss of electromagnetic steel sheet or amorphous material are disclosed. In this case, the steel sheet or amorphous material is subjected to an irradiation of plasma flame under specified conditions.