Abstract: In a method for preparing a nickel-based alloy, an electrode is produced by VIM, VOF or VLF, heat-treated in a furnace between 500 and 1300° C. for 10 to 336 hours to reduce stresses and aging, the heat-treatment being conducted for at least 10 hours and at most 48 hours at 1000° C. to 1300° C., and cooled to between room temperature and less than 900° C., then remelted using ESR at 3.0 to 10 kg/minute to form an ESR block which is cooled to between room temperature and less than 900° C., and remelted again using VAR at 3.0 to 10 kg/minute and a remelting rate fluctuation range of less than 15%, preferably 10%, ideally 5%; the remelted VAR block is heat-treated between 500 and 1250° C. for 10 to 336 hours, then shaped into the desired product shape and dimension by hot or cold forming.

Abstract: In a method for preparing a nickel-based alloy, an electrode is produced by VIM, VOF or VLF, heat-treated in a furnace between 500 and 1300° C. for 10 to 336 hours to reduce stresses and aging, the heat-treatment being conducted for at least 10 hours and at most 48 hours at 1000° C. to 1300° C., and cooled to between room temperature and less than 900° C., then remelted using ESR at 3.0 to 10 kg/minute to form an ESR block which is cooled to between room temperature and less than 900° C., and remelted again using VAR at 3.0 to 10 kg/minute and a remelting rate fluctuation range of less than 15%, preferably 10%, ideally 5%; the remelted VAR block is heat-treated between 500 and 1250° C. for 10 to 336 hours, then shaped into the desired product shape and dimension by hot or cold forming.

Abstract: The invention relates to creep-resistant iron-nickel alloys with a low thermal expansion coefficient that contain (in weight %) 0.008 to 0.12 C, 0.05 to 0.30% Mn, 0.05 to 0.30% Si, 0.2 to 0.9% Mo, 0.1 to 0.3% Cr, 0.03 to 0.15% Nb, a maximum content of 0.5% Co as well as a content of 36.0 to 36.5% Ni, and a balance of iron and production-related impurities. The alloys have a thermal expansion coefficient of less than 2.0×10−6/K in the temperature range of 20 to 100° C.