Abstract: Disclosed is a microporous polyethylene film for a battery separator and a method of producing the same. The microporous polyethylene film comprises a resin mixture, which includes 100 parts by weight of composition containing 20-50 wt % polyethylene with a weight average molecular weight of 5×104-3×105 (component I) and 80-50 wt % diluent (component II), 0.1-2 parts by weight of peroxide (component III), and 0.05-0.5 parts by weight of anti-oxidant (component IV). The microporous polyethylene film has a puncture strength of 0.22 N/?m or more and a gas permeability (Darcy's permeability constant) of 1.3×10?5 Darcy or more. The present invention increases production efficiency of the microporous film, and improves performances and stability of the battery when the microporous polyethylene film is used in a battery separator.

Abstract: Disclosed is a microporous high density polyethylene film for a battery separator and a method of producing the same. The microporous high density polyethylene film includes high density polyethylene with a weight average molecular weight of 2×105?5×105, containing 5 wt % or less molecule with a molecular weight of 1×104 or less. The microporous high density polyethylene film has tensile strengths of 1,100 kg/cm2 or more in transverse and machine directions respectively, a puncture strength of 0.22 N/?m or more, a gas permeability (Darcy's permeability constant) of 1.3×10?5 Darcy or more, and shrinkages of 5% or less in machine and transverse directions, respectively. Particularly, the microporous high density polyethylene film has an excellent extrusion-compoundabiliy and stretchability and a high productivity, and can improve the performances and stability of a battery produced using the same.

Abstract: Disclosed is a microporous high density polyethylene film for a battery separator and a method of producing the same. The microporous high density polyethylene film includes high density polyethylene with a weight average molecular weight of 2×105-5×105, containing 5 wt % or less molecule with a molecular weight of 1×104 or less. The microporous high density polyethylene film has tensile strengths of 1,100 kg/cm2 or more in transverse and machine directions respectively, a puncture strength of 0.22 N/?m or more, a gas permeability (Darcy's permeability constant) of 1.3×10?5 Darcy or more, and shrinkages of 5% or less in machine and transverse directions, respectively. Particularly, the microporous high density polyethylene film has an excellent extrusion-compoundabiliy and stretchability and a high productivity, and can improve the performances and stability of a battery produced using the same.

Abstract: Disclosed in the present invention are a microporous polyethylene film and a method of manufacture thereof. The polyethylene microporous film manufactured according to the present invention may contribute to an increased productivity of stable products as its extrusion and stretching may be done readily. And thus manufactured product may be used for battery separators and various filters owing to its high gas permeability, superior puncture strength, and small ratio of shrinkage.

Abstract: The present invention discloses a microporous high-density polyethylene film for a battery separator, and process for preparing the same. The microporous high-density polyethylene film according to the present invention comprises of high-density polyethylene with weight average molecular weight of 2×105˜4×105, containing not more than 5 wt % of molecules with molecular weight of 1×104 or less and not more than 5 wt % of molecules with molecular weight of 1×106 or more, and has the properties of puncture strength of 0.22 N/?m or more, Darcy's permeability constant of 1.8×10?5 Darcy or more, and shrinkage of 4% or less in machine and transverse direction, respectively. Particularly, the microporous high-density polyethylene film has excellent extrusion-compoundability and stretchability with high productivity and enhances performances and stability of the battery using the film.

Abstract: Disclosed in the present invention are a microporous polyethylene film and a method of manufacture thereof. The polyethylene microporous film manufactured according to the present invention may contribute to an increased productivity of stable products as its extrusion and stretching may be done readily. And thus manufactured product may be used for battery separators and various filters owing to its high gas permeability, superior puncture strength, and small ratio of shrinkage.

Abstract: An air-permeable film is prepared by mono-axially drawing a composition comprising a linear low density polyethylene resin having a mw. distribution from 5 to 20, 1 to 100 parts by weight of propylene resin, 1 to 30 parts by weight of an ethylene-propylene copolymer, 1 to 30 parts by weight of a polyolefin resin which has a melt index of 12 or higher, and 50 to 200 parts by weight of an inorganic filler based on 100 parts by weight of total resin by 1.5 to 3 times.

Abstract: A plastic composition superior in both biodegradability and physical properties, comprises a matrix resin which is a blend of polyethylene and a biodegradable aliphatic polyester, starch, a coupling agent, a radical initiator, a starch plasticizer, a starch destructurizing agent and an autooxidizing agent, wherein the starch chemically binds to the matrix resin.