Abstract: A method for manufacturing grain-oriented electrical steel sheet includes: manufacturing a steel slab having at least one of 2 wt % to 7 wt % of Si, 0.03 wt % to 0.10 wt % of Sn, and 0.01 wt % to 0.05 wt % of Sb; hot-rolling the steel slab to produce a hot-rolled sheet; cold-rolling the hot-rolled sheet to produce a cold-rolled sheet; primary recrystallization-annealing the cold-rolled sheet; applying an annealing separator to the primary recrystallization-annealed cold-rolled sheet and drying the same; and secondary recrystallization-annealing the cold-rolled sheet on which the annealing separator is applied. The primary recrystallization-annealing is performed so that the thickness of an oxide layer formed on the surface of the cold-rolled sheet is 0.5 ?m to 2.5 ?m, and the oxygen amount of the oxide layer is 600 ppm or more after the primary recrystallization-annealing, and in which a forsterite (Mg2SiO4) film can be removed in the secondary recrystallization-annealing.

Abstract: An annealing separator for an oriented electrical steel sheet including: a first component includes a Mg oxide or a Mg hydroxide; and a second component including one kind among oxides and hydroxides of a metal selected from Al, Ti, Cu, Cr, Ni, Ca, Zn, Na, K, Mo, In, Sb, Ba, Bi, and Mn, or two or more kinds thereof.

Abstract: An annealing separator for an oriented electrical steel sheet includes: a first component including a Mg oxide or a Mg hydroxide; and a second component including one kind among oxides and hydroxides of a metal selected from Al, Ti, Cu, Cr, Ni, Ca, Zn, Na, K, Mo, In, Sb, Ba, Bi, and Mn, or two or more kinds thereof.

Abstract: Provided is an oriented electrical steel sheet including: a forsterite film formed on one side or both sides of an oriented electrical steel sheet substrate; and a ceramic layer formed on an entire or partial region of the forsterite film. Provided is a manufacturing method for an oriented electrical steel sheet including: preparing an oriented electrical steel sheet having a forsterite film formed on one surface or both surfaces thereof; and forming a ceramic layer by spraying ceramic powder on the forsterite film.

Abstract: The present invention relates to a soft high-silicon steel sheet, and more particularly, to a soft high-silicon steel sheet which has ductility even if the silicon content thereof is greater than 4%, and can thus be manufactured into a steel sheet having a high silicon content only by means of rolling without an additional siliconizing process. The soft high-silicon steel sheet may include a silicon content greater than 4 wt % and less than or equal to 7 wt % and 1 to 20% of chromium, or may include 5 to 7 wt % of Si+Al and 1 to 20 wt % of chromium.

Abstract: Provided is an oriented electrical steel sheet including: a forsterite film formed on one side or both sides of an oriented electrical steel sheet substrate; and a ceramic layer formed on an entire or partial region of the forsterite film. Provided is a manufacturing method for an oriented electrical steel sheet including: preparing an oriented electrical steel sheet having a forsterite film formed on one surface or both surfaces thereof; and forming a ceramic layer by spraying ceramic powder on the forsterite film.

Abstract: The present invention relates to a soft high-silicon steel sheet, and more particularly, to a soft high-silicon steel sheet which has ductility even if the silicon content thereof is greater than 4%, and can thus be manufactured into a steel sheet having a high silicon content only by means of rolling without an additional siliconizing process. The soft high-silicon steel sheet may include a silicon content greater than 4 wt % and less than or equal to 7 wt % and 1 to 20% of chromium, or may include 5 to 7 wt % of Si+Al and 1 to 20 wt % of chromium.

Abstract: A method for manufacturing grain-oriented electrical steel sheet comprises: manufacturing a steel slab comprising at least one of 2 wt % to 7 wt % of Si, 0.03 wt % to 0.10 wt % of Sn, and 0.01 wt % to 0.05 wt % of Sb; hot-rolling the steel slab to produce a hot-rolled sheet; cold-rolling the hot-rolled sheet to produce a cold-rolled sheet; primary recrystallization-annealing the cold-rolled sheet; applying an annealing separator to the primary recrystallization-annealed cold-rolled sheet and drying the same; and secondary recrystallization-annealing the cold-rolled sheet on which the annealing separator is applied. The primary recrystallization-annealing is performed so that the thickness of an oxide layer formed on the surface of the cold-rolled sheet is 0.5 ?m to 2.5 ?m, and the oxygen amount of the oxide layer is 600 ppm or more after the primary recrystallization-annealing, and in which a forsterite (Mg2SiO4) film can be removed in the secondary recrystallization-annealing.

Abstract: The present invention relates to an annealing separator for an oriented electrical steel sheet, an oriented electrical steel sheet, and a manufacturing method of an oriented electrical steel sheet. An annealing separator for an oriented electrical steel sheet including: a first component including a Mg oxide or a Mg hydroxide; and a second component including one kind among oxides and hydroxides of a metal selected from Al, Ti, Cu, Cr, Ni, Ca, Zn, Na, K, Mo, In, Sb, Ba, Bi, and Mn, or two or more kinds thereof, and of which Equation 1 below is satisfied, an oriented electrical steel sheet manufactured by using the same, and a manufacture method of an oriented electrical steel sheet, are provided. 0.05<[A]/[B]<10.5??[Equation 1] (In Equation 1, [A] is a content of the second component with respect to a total amount (100 wt %) of the annealing separator, and [B] is a content of the first component with respect to a total amount (100 wt %) of the annealing separator).

Abstract: Provided is a method for manufacturing a high silicon steel sheet having excellent producibility and magnetic properties. The method includes: casting a molten metal as a strip having a thickness of 5 mm or less, the molten metal comprising, by weight %, C: 0.05% or less (excluding 0%), N: 0.05% or less (excluding 0%), Si: 4% to 7%, Al: 0.5% to 3%, Si+Al: 4.5% to 8%, and the balance of Fe and inevitable impurities; hot-rolling the cast strip at a temperature of 800° C. or higher; annealing the hot-rolled strip at a temperature within a range of 900° C. to 1200° C.; cooling the annealed strip; warm-rolling the quenched strip at a temperature within a range of 300° C. to 700° C.; and finally annealing the warm-rolled strip at a temperature within a range of 800° C. to 1200° C.

Abstract: The present invention relates to a grain oriented electrical steel sheet having excellent core loss and to a method for manufacturing same. The electrical steel sheet according to one aspect of the present invention may have a composition comprising, by weight %, Si: 1.0 to 4.0%, Al: 0.1 to 4.0%, and a rare earth element: 0.0001 to 0.5% by the total content of the whole rare earth element.

Abstract: Provided is a grain-oriented electric steel sheet having superior magnetic property and to a grain-oriented electric steel sheet including 2.0 to 4.5 weight % of Si, 0.001 to 0.10 weight % of C, 0.010 weight % or lower of Al, 0.08 weight % or lower of Mn, 0.005 weight % or lower of N, 0.002 to 0.050 weight % of S, the remainder being Fe and other unavoidable impurities. The steel sheet having been subjected to secondary recrystallization using at least any one of grain boundary-segregated elementary S and an FeS precipitate as a grain growth inhibitor.

Abstract: The present invention relates to a grain oriented electrical steel sheet having excellent core loss and to a method for manufacturing same. The electrical steel sheet according to one aspect of the present invention may have a composition comprising, by weight %, Si: 1.0 to 4.0%, Al: 0.1 to 4.0%, and a rare earth element: 0.0001 to 0.5% by the total content of the whole rare earth element.

Abstract: The present invention relates to a grain oriented electrical steel sheet having excellent core loss and to a method for manufacturing same. The electrical steel sheet according to one aspect of the present invention may have a composition comprising, by weight %, Si: 1.0 to 4.0%, Al: 0.1 to 4.0%, and a rare earth element: 0.0001 to 0.5% by the total content of the whole rare earth element.

Abstract: The present invention relates to a soft high-silicon steel sheet, and more particularly, to a soft high-silicon steel sheet which has ductility even if the silicon content thereof is greater than 4%, and can thus be manufactured into a steel sheet having a high silicon content only by means of rolling without an additional siliconizing process. The soft high-silicon steel sheet may include a silicon content greater than 4 wt % and less than or equal to 7 wt % and 1 to 20% of chromium, or may include 5 to 7 wt % of Si+Al and 1 to 20 wt % of chromium.

Abstract: Provided is a grain-oriented electric steel sheet having superior magnetic property and to a grain-oriented electric steel sheet including 2.0 to 4.5 weight % of Si, 0.001 to 0.10 weight % of C, 0.010 weight % or lower of Al, 0.08 weight % or lower of Mn, 0.005 weight % or lower of N, 0.002 to 0.050 weight % of S, the remainder being Fe and other unavoidable impurities. The steel sheet having been subjected to secondary recrystallization using at least any one of grain boundary-segregated elementary S and an FeS precipitate as a grain growth inhibitor.

Abstract: Provided is a grain-oriented electric steel sheet and a method for manufacturing same, the steel sheet having superior magnetic properties. The method comprises heating a slab comprising 2.0 to 4.5 weight % of Si, 0.001 to 0.10 weight % of C, 0.010 weight % or lower of Al, 0.08 weight % or lower of Mn, 0.005 weight % or lower of N, 0.002 to 0.050 weight % of S, the remainder being Fe and other unavoidable impurities, performing hot-rolling of the heated slab, performing cold-rolling one time or two or more times including an intermediate annealing, performing decarbonization and re-crystallizing annealing, and performing secondary re-crystallizing annealing.

Abstract: The purpose of the present invention is to provide a high silicon steel sheet having excellent productivity and magnetic properties and a method for manufacturing the same.

Abstract: Provided is a grain-oriented electric steel sheet and a method for manufacturing same, the steel sheet having superior magnetic properties. The method comprises heating a slab comprising 2.0 to 4.5 weight % of Si, 0.001 to 0.10 weight % of C, 0.010 weight % or lower of Al, 0.08 weight % or lower of Mn, 0.005 weight % or lower of N, 0.002 to 0.050 weight % of S, the remainder being Fe and other unavoidable impurities, performing hot-rolling of the heated slab, performing cold-rolling one time or two or more times including an intermediate annealing, performing decarbonization and re-crystallizing annealing, and performing secondary re-crystallizing annealing.

Abstract: A method for manufacturing an oriented electrical steel sheet includes the step of preparing a steel slab composed of in weight %: 0.035-0.050% of C, 2.9-3.3% of Si, less than 0.016% of P, 0.011-0.017% of soluble Al, 0.0080-0.012% of N, less than 0.007% of S, 0.06-0.18% of Ni+Cr, less than 0.32% of Mn with an Mn/S ratio of 20 or more, less than 0.6% of Cu with a Cu/Mn ratio of 1.5 or more, and balance of Fe and other inevitable impurities. The steel slab is heated at a temperature of 1250.degree.-1320.degree. C., and then hot rolled. The hot rolled slab is then cold rolled in two stages to a final sheet thickness, with a decarburization annealing being carried out at an intermediate thickness. The decarburized cold rolled sheet is coated with an annealing separator containing MgO as the main ingredient and then a finish annealing treatment is conducted, thereby obtaining a magnetically superior oriented electrical steel sheet.