Abstract: Disclosed are a thermoplastic elastomer resin composition, and a molded article produced therefrom. The thermoplastic elastomer resin composition includes styrene-based synthetic rubber having a melt index in a range of 30 g/10 min to 100 g/10 min which is measured at a temperature of 190° C. and a load of 2.16 kg, a propylene-ethylene copolymer having a melt index in a range of 60 g/10 min to 150 g/10 min which is measured at a temperature of 230° C. and a load of 2.16 kg, cross-linked rubber, oil, an inorganic filler, and a lubricant in appropriate amounts.

Abstract: Provided is a polypropylene resin composition which imparts excellent impact resistance by comprising polypropylene resin, a thermoplastic elastomer, and a wool-like inorganic filler, and simultaneously imparts dimensional stability through control of low shrinkage and orientation, and also has very excellent scratch resistance.

Abstract: Disclosed is a thermoplastic elastomer composition having a superior low-temperature flexibility is provided. The thermoplastic elastomer composition may include an amount of about 10 to 15 wt % of a polypropylene-ethylene copolymer; an amount of about 70 to 85 wt % of a thermoplastic elastomer including an olefin-based thermoplastic elastomer and a styrene-based thermoplastic elastomer; an amount of about 5 to 10 wt % of a softener; an amount of about 3 to 5 wt % of a reinforcing agent; and an amount of about 1 wt % or less but greater than 0 wt % of a UV stabilizer based on the total weight of the thermoplastic elastomer composition.

Abstract: The present disclosure relates to a fiber-reinforced polypropylene composite resin composition with reduced odor for interior parts of vehicles which includes an inorganic deodorant with excellent effects of reducing odors so as to improve indoor air quality, and includes a mixture of a polypropylene polymer, a thermoplastic elastomer, a fiber-shaped filler, a coupling agent, a slip agent and a UV stabilizer. Interior parts of vehicles molded from the fiber-reinforced polypropylene composite resin composition according to the present disclosure deodorize unpleasant gas generated during the production process and have excellent mechanical properties, thus providing pleasant environments for drivers.

Abstract: Provided is a polypropylene resin composition which imparts excellent impact resistance by comprising polypropylene resin, a thermoplastic elastomer, and a wool-like inorganic filler, and simultaneously imparts dimensional stability through control of low shrinkage and orientation, and also has very excellent scratch resistance.

Abstract: Disclosed is a thermoplastic elastomer composition having a superior low-temperature flexibility is provided. The thermoplastic elastomer composition may include an amount of about 10 to 15 wt % of a polypropylene-ethylene copolymer; an amount of about 70 to 85 wt % of a thermoplastic elastomer including an olefin-based thermoplastic elastomer and a styrene-based thermoplastic elastomer; an amount of about 5 to 10 wt % of a softener; an amount of about 3 to 5 wt % of a reinforcing agent; and an amount of about 1 wt % or less but greater than 0 wt % of a UV stabilizer based on the total weight of the thermoplastic elastomer composition.

Abstract: The present disclosure relates to a fiber-reinforced polypropylene composite resin composition with reduced odor for interior parts of vehicles which includes an inorganic deodorant with excellent effects of reducing odors so as to improve indoor air quality, and includes a mixture of a polypropylene polymer, a thermoplastic elastomer, a fiber-shaped filler, a coupling agent, a slip agent and a UV stabilizer. Interior parts of vehicles molded from the fiber-reinforced polypropylene composite resin composition according to the present disclosure deodorize unpleasant gas generated during the production process and have excellent mechanical properties, thus providing pleasant environments for drivers.

Abstract: Compositions of high-rigid polypropylene composite resin are provided herein. Such compositions having excellent tactile sensation and dimensional stability, and more particularly, the compositions of polypropylene composite resin having excellent tactile sensation such as thermoplastic rubber, excellent impact strength and rigidity, and low shrinkage anisotropy. The compositions of polypropylene composite resin provided herein also have excellent impact strength and rigidity as well as excellent tactile sensation such as a thermoplastic rubber and low shrinkage anisotropy. Thus, they exhibit excellent moldability and the compositions can be molded into a vehicle component. Furthermore, the compositions of polypropylene composite resin have excellent tactile sensation and can be used as a high-quality material that does not require separate painting and maintains excellent physical properties and dimensional stability as a vehicle component.

Abstract: A composition of polypropylene composite resin having high impact strength and high adhesion is provided. The composition of polypropylene composite resin having high impact strength and high adhesion can largely enhance base adhesion and impact resistance due to a high friction coefficient while providing a similar mechanical property to the related art. The compositions provided herein include mixing a polypropylene polymer, a polyethylene resin composition, and a thermoplastic elastomer, a silane-based propylene polymer, and an inorganic filler as main components at a specific content ratio. The compositions have advantages including process simplification, cost reduction, and eco-friendly without a separate adhering process. Such compositions can be used for interior components such as sun visors, door trims, pillar trims of vehicles and various other industrial components and materials.

Abstract: A composition of polypropylene composite resin having high impact strength and high adhesion is provided. The composition of polypropylene composite resin having high impact strength and high adhesion can largely enhance base adhesion and impact resistance due to a high friction coefficient while providing a similar mechanical property to the related art. The compositions provided herein include mixing a polypropylene polymer, a polyethylene resin composition, and a thermoplastic elastomer, a silane-based propylene polymer, and an inorganic filler as main components at a specific content ratio. The compositions have advantages including process simplification, cost reduction, and eco-friendly without a separate adhering process. Such compositions can be used for interior components such as sun visors, door trims, pillar trims of vehicles and various other industrial components and materials.