Abstract: An inorganic material that consists of at least two elementary spherical particles, each of said spherical particles comprising metal nanoparticles that are between 1 and 300 nm in size and a mesostructured matrix with an oxide base of at least one element X that is selected from the group that consists of aluminum, titanium, tungsten, zirconium, gallium, germanium, tin, antimony, lead, vanadium, iron, manganese, hafnium, niobium, tantalum, yttrium, cerium, gadolinium, europium and neodymium is described, whereby said matrix has a pore size of between 1.5 and 30 nm and has amorphous walls with a thickness of between 1 and 30 nm, said elementary spherical particles having a maximum diameter of 10 ?m. Said material can also contain zeolitic nanocrystals that are trapped within said mesostructured matrix.

Abstract: A mesostructured aluminosilicate material is described, constituted by at least two spherical elementary particles, each of said spherical particles being constituted by a matrix based on silicon oxide and aluminium oxide, having a pore size in the range 1.5 to 30 nm, a Si/Al molar ratio of at least 1, having amorphous walls with a thickness in the range 1 to 20 nm, said spherical elementary particles having a maximum diameter of 10 ?m. A process for preparing said material and its application in the fields of refining and petrochemistry are also described.

Abstract: A material with a hierarchical porosity is described, constituted by at least two spherical elementary particles, each of said spherical particles comprising zeolitic nanocrystals having a pore size in the range 0.2 to 2 nm and a matrix based on silicon oxide, which is mesostructured, having a pore size in the range 1.5 to 30 nm and having amorphous walls with a thickness in the range 1 to 20 nm, said spherical elementary particles having a maximum diameter of 10 ?m. the matrix based on silicon oxide may contain aluminium. The preparation of said material is also described.