Abstract: A method for resistance spot welding comprising the following successive steps: —providing at least two steel sheets with thickness (th) comprised between 0.5 and 3 mm, at least one of the sheets being a zinc or zinc-alloy coated steel sheet (A) with a tensile strength (TS) higher than 800 MPa and a total elongation (TEL) such as (TS)×(TEL)>14000 MPa %, wherein the composition of the steel substrate of (A) contains, in weight: 0.05%?C?0.4%, 0.3%?Mn?8%, 0.010%?Al?3%, 0.010%?Si?2.09%, with 0.5%?(Si+Al)?3.5%, 0.001%?Cr?1.0%, 0.001%?Mo?0.5% and optionally: 0.005%?Nb?0.1%, 0.005%?V?0.2%, 0.005%?Ti?0.1%, 0.0003%?B?0.005%, 0.001%?Ni?1.0%, the remainder being Fe and unavoidable impurities, —performing resistance spot welding of the at least two steel sheets for producing a weld with an indentation depth (IDepth) on the surface of said steel sheet (A) such as: 100 ?m?(IDepth)?18.68 (Znsol)?55.1, wherein (IDepth) is in micrometers and wherein Znsol is the solubility of Zn in the steel of sheet (A) at 750° C.

Abstract: A pre-coated steel substrate coated with: a first pre-coating including titanium, the first coating having a thickness of 40 nm to 1200 nm, optionally, an intermediate pre-coating layer including at least 8% by weight nickel and at least 10% by weight chromium, the rest being iron or an intermediate pre-coating layer including Fe, Ni, Cr and Ti wherein the amount of Ti is above or equal to 5 wt. % and wherein the following equation is satisfied: 8 wt. %<Cr+Ti<40 wt. %, the balance being Fe and Ni, the intermediate pre-coating layer having a thickness between 2 and 30 nm a second pre-coating being a zinc-based coating and the steel substrate including above 0.05 wt. % of Si.

Abstract: A method for resistance spot welding comprising the following successive steps: —providing at least two steel sheets with thickness (th) comprised between 0.5 and 3 mm, at least one of the sheets being a zinc or zinc-alloy coated steel sheet (A) with a tensile strength (TS) higher than 800 MPa and a total elongation (TEL) such as (TS)×(TEL)>14000 MPa %, wherein the composition of the steel substrate of (A) contains, in weight: 0.05%?C?0.4%, 0.3%?Mn?8%, 0.010%?Al?3%, 0.010%?Si?2.09%, with 0.5%?(Si+Al)?3.5%, 0.001%?Cr?1.0%, 0.001%?Mo?0.5% and optionally: 0.005%?Nb?0.1%, 0.005%?V?0.2%, 0.005%?Ti?0.1%, 0.0003%?B?0.005%, 0.001%?Ni?1.0%, the remainder being Fe and unavoidable impurities, —performing resistance spot welding of the at least two steel sheets for producing a weld with an indentation depth (IDepth) on the surface of said steel sheet (A) such as: 100 ?m?(IDepth)?18.68 (Znsol)?55.1, wherein (IDepth) is in micrometers and wherein Znsol is the solubility of Zn in the steel of sheet (A) at 750° C.