Abstract: Provided are an auxiliary alloy casting piece, a high-remanence and high-coercive force NdFeB permanent magnet, and preparation methods thereof. The method for preparing the auxiliary alloy casting piece includes the following steps: providing an auxiliary alloy material including, by mass percentage, 40% to 45% of Pr, 1% to 2% of Co, 0.5% to 1% of Ga, 0.6% to 0.8% of B, 0.1% to 0.2% of V, 0.3% to 0.7% of Ti, and a balance of Fe; smelting the auxiliary alloy material to obtain a smelted material; and subjecting the smelted material to a quick-setting casting to obtain the auxiliary alloy casting piece; where the quick-setting casting includes a refining and a casting in sequence.

Abstract: Provided are an auxiliary alloy casting piece, a high-remanence and high-coercive force NdFeB permanent magnet, and preparation methods thereof. The method for preparing the auxiliary alloy casting piece includes the following steps: providing an auxiliary alloy material including, by mass percentage, 40% to 45% of Pr, 1% to 2% of Co, 0.5% to 1% of Ga, 0.6% to 0.8% of B, 0.1% to 0.2% of V, 0.3% to 0.7% of Ti, and a balance of Fe; smelting the auxiliary alloy material to obtain a smelted material; and subjecting the smelted material to a quick-setting casting to obtain the auxiliary alloy casting piece; where the quick-setting casting includes a refining and a casting in sequence.

Abstract: A preparation method of improved sintered neodymium-iron-boron (Nd—Fe—B) casting strips includes the following steps: firstly nucleation assisted alloy particles used for sintered Nd—Fe—B casting strips are prepared, all elements are weighted as follows: 26.68-28% of Pr—Nd, 70-72.5% of Fe and 0.90-1% of B, and a Pr element in two elements of Pr—Nd accounts for 0-30 wt %; the compounded materials are smelted and poured to obtain alloy strips, then the alloy strips are crushed into particles with diameter of 1-10 mm; secondly, Nd—Fe—B casting strips are prepared: the prepared intermediate materials are smelted and melted into molten steel, and then are refined; after the intermediate materials are fully melted, the nucleation assisted alloy particles are added; and after the nucleation assisted alloy particles are added, smelting is performed for 3-15 minutes pouring is performed, and final Nd—Fe—B alloy casting strips are obtained.

Abstract: A preparation method of improved sintered neodymium-iron-boron (Nd—Fe—B) casting strips includes the following steps: firstly nucleation assisted alloy particles used for sintered Nd—Fe—B casting strips are prepared, all elements are weighted as follows: 26.68-28% of Pr—Nd, 70-72.5% of Fe and 0.90-1% of B, and a Pr element in two elements of Pr—Nd accounts for 0-30 wt %; the compounded materials are smelted and poured to obtain alloy strips, then the alloy strips are crushed into particles with diameter of 1-10 mm; secondly, Nd—Fe—B casting strips are prepared: the prepared intermediate materials are smelted and melted into molten steel, and then are refined; after the intermediate materials are fully melted, the nucleation assisted alloy particles are added; and after the nucleation assisted alloy particles are added, smelting is performed for 3-15 minutes pouring is performed, and final Nd—Fe—B alloy casting strips are obtained.

Abstract: A method for preparing a NdFeB permanent magnetic material may include providing a covered NdFeB magnetic powder by depositing heavy rare earth particles or high-melting particles onto a NdFeB magnetic powder by physical vapor deposition; and performing orientation molding and sintering on the covered NdFeB magnetic powder to provide the NdFeB permanent magnetic material.

Abstract: A method for preparing a NdFeB permanent magnetic material may include providing a covered NdFeB magnetic powder by depositing heavy rare earth particles or high-melting particles onto a NdFeB magnetic powder by physical vapor deposition; and performing orientation molding and sintering on the covered NdFeB magnetic powder to provide the NdFeB permanent magnetic material.