Abstract: A process for transitioning molten glass in a glass furnace from one color to another color while minimizing the production of out-of-color specification transition glass. During the transition, a compensating agent is introduced into the molten glass to adjust the color of the molten glass being discharged from the furnace so that the discharged molten glass meets a target color specification, which effectively results in acceleration of the furnace color change compared to other conventional methods.

Abstract: A glass container and a process for forming an inorganic silica coating on an exterior surface of the glass container to improve one or more surface characteristics of the glass container. A sol-gel solution including a polysilazane and an organic solvent is applied to the exterior surface of the glass container to form a sol-gel coating thereon. The glass container and the sol-gel coating are then exposed to a water vapor-containing environment and heated at a temperature of between 150 degrees Celsius and 600 degrees Celsius to transform the sol-gel coating into an inorganic silica coating. The as-formed silica coating has a hardness of greater than 8.5 GPa and is bonded to the exterior surface of the glass container through a plurality of siloxane bonds.

Abstract: A soda-lime-silica glass-ceramic article having an amorphous matrix phase and a crystalline phase is disclosed along with a method of manufacturing a soda-lime-silica glass-ceramic article from a parent glass composition comprising 47-63 mol % SiO2, 15-22 mol % Na2O, and 18-36 mol % CaO. The crystalline phase of the glass-ceramic article has a higher concentration of sodium (Na) than that of the amorphous matrix phase.

Abstract: A process for forming coating on an interior surface of a glass container. A glass preform is formed at blank molding station from a gob of molten glass. Thereafter, a glass container is formed at a blow molding station from the glass preform. A coating material comprising a suspension of nanoparticles in a liquid medium is introduced into an interior of the glass preform or the glass container while the glass is still hot from being formed. Heat from the glass is transferred to the liquid medium to vaporize the liquid medium and form a coating on an interior surface of the glass preform or the glass container. Thereafter, the glass container is annealed.

Abstract: A glass container and related methods of manufacturing and coating glass containers. An exterior glass surface of a glass container is coated with a hybrid sol-gel and heated to cross-link the hybrid sol-gel. The resulting cross-linked hybrid sol-gel coating on the exterior glass surface of the glass container has greater than 90% silicate-based material by weight.

Abstract: A glass container and a process for forming an inorganic silica coating on an exterior surface of the glass container to improve one or more surface characteristics of the glass container. A sol-gel solution including a polysilazane and an organic solvent is applied to the exterior surface of the glass container to form a sol-gel coating thereon. The glass container and the sol-gel coating are then exposed to a water vapor-containing environment and heated at a temperature of between 150 degrees Celsius and 600 degrees Celsius to transform the sol-gel coating into an inorganic silica coating. The as-formed silica coating has a hardness of greater than 8.5 GPa and is bonded to the exterior surface of the glass container through a plurality of siloxane bonds.

Abstract: A soda-lime-silica glass-ceramic article having an amorphous matrix phase and a crystalline phase is disclosed along with a method of manufacturing a soda-lime-silica glass-ceramic article from a parent glass composition comprising 47-63 mol % SiO2, 15-22 mol % Na2O, and 18-36 mol % CaO. The crystalline phase of the glass-ceramic article has a higher concentration of sodium (Na) than that of the amorphous matrix phase.

Abstract: A soda-lime-silica glass-ceramic article having an amorphous matrix phase and a crystalline phase is disclosed along with a method of manufacturing a soda-lime-silica glass-ceramic article from a parent glass composition comprising 47-63 mol % SiO2, 15-22 mol % Na2O, and 18-36 mol % CaO. The crystalline phase of the glass-ceramic article has a higher concentration of sodium (Na) than that of the amorphous matrix phase.

Abstract: Latent colorant material compositions, soda-lime-silica glass compositions, and related methods of manufacturing color-strikable glass containers. The latent colorant material compositions may be introduced into a plurality of base glass compositions having redox numbers in the range of ?40 to +20 to produce color-strikable glass compositions and color-strikable glass containers. The latent colorant material compositions introduced into the base glass compositions include a mixture of cuprous oxide (Cu2O), stannous oxide (SnO), bismuth oxide (Bi2O3), and carbon (C). After formation, the color-strikable glass containers may be heat-treated to strike red or black therein.

Abstract: A glass container and a process for forming an inorganic silica coating on an exterior surface of the glass container to improve one or more surface characteristics of the glass container. A sol-gel solution including a polysilazane and an organic solvent is applied to the exterior surface of the glass container to form a sol-gel coating thereon. The glass container and the sol-gel coating are then exposed to a water vapor-containing environment and heated at a temperature of between 150 degrees Celsius and 600 degrees Celsius to transform the sol-gel coating into an inorganic silica coating. The as-formed silica coating has a hardness of greater than 8.5 GPa and is bonded to the exterior surface of the glass container through a plurality of siloxane bonds.

Abstract: A soda-lime-silica glass-ceramic article having an amorphous matrix phase and a crystalline phase is disclosed along with a method of manufacturing a soda-lime-silica glass-ceramic article from a parent glass composition comprising 47-63 mol % SiO2, 15-22 mol % Na2O, and 18-36 mol % CaO. The crystalline phase of the glass-ceramic article has a higher concentration of sodium (Na) than that of the amorphous matrix phase.

Abstract: A soda-lime-silica glass container and related methods of manufacturing. A black-strikable glass composition having a base glass portion and a latent colorant portion is prepared. The base glass portion includes soda-lime-silica glass materials and one or more blue colorant materials, and the latent colorant portion includes cuprous oxide (Cu2O), stannous oxide (SnO), bismuth oxide (Bi2O3), and carbon (C). Glass containers may be formed from the black-strikable glass composition, and these glass containers may be heated to a temperature greater than 600 degrees Celsius to strike black therein. The glass containers formed from the black-strikable glass composition may be inspected—before or after striking—by infrared inspection equipment.

Abstract: A process for forming coating on an interior surface of a glass container. A glass preform is formed at blank molding station from a gob of molten glass. Thereafter, a glass container is formed at a blow molding station from the glass preform. A coating material comprising a suspension of nanoparticles in a liquid medium is introduced into an interior of the glass preform or the glass container while the glass is still hot from being formed. Heat from the glass is transferred to the liquid medium to vaporize the liquid medium and form a coating on an interior surface of the glass preform or the glass container. Thereafter, the glass container is annealed.

Abstract: A glass container and related methods of manufacturing a glass container. A solution having a composition including a silane, a solvent, a catalyst, and water, is applied to an exterior glass surface of the glass container, at an application temperature between 5 and 40 degrees Celsius, such that the solution at least partially fills the surface imperfections to provide a room-temperature-curable cold-end coating on the glass container. Then, the applied solution is allowed to cure on the exterior glass surface of the glass container, at a curing temperature between 5 and 40 degrees Celsius.

Abstract: Latent colorant material compositions, soda-lime-silica glass compositions, and related methods of manufacturing color-strikable glass containers. The latent colorant material compositions may be introduced into a plurality of base glass compositions having redox numbers in the range of ?40 to +20 to produce color-strikable glass compositions and color-strikable glass containers. The latent colorant material compositions introduced into the base glass compositions include a mixture of cuprous oxide (Cu2O), stannous oxide (SnO), bismuth oxide (Bi2O3), and carbon (C). After formation, the color-strikable glass containers may be heat-treated to strike red or black therein.

Abstract: Latent colorant material compositions, soda-lime-silica glass compositions, and related methods of manufacturing color-strikable glass containers. The latent colorant material compositions may be introduced into a plurality of base glass compositions having redox numbers in the range of ?40 to +20 to produce color-strikable glass compositions and color-strikable glass containers. The latent colorant material compositions introduced into the base glass compositions include a mixture of cuprous oxide (Cu2O), stannous oxide (SnO), bismuth oxide (Bi2O3), and carbon (C). After formation, the color-strikable glass containers may be heat-treated to strike red or black therein.

Abstract: A glass container that includes a microwave susceptor coating on an exterior surface thereof, and a process for healing flaws in an exterior portion of the glass container. When the glass container is exposed to microwave radiation, the microwave susceptor coating generates heat and selectively and locally provides a major portion of such heat to regions of glass in the exterior portion of the glass container that are in close proximity to the flaws. These regions of glass in the exterior portion of the glass container may be selectively and locally heated so that the glass therein can flow and thereby fill-in the flaws in the exterior portion of the glass container. This process can be used to heal flaws in an exterior portion of a glass container without impairing the structural integrity of the glass container.

Abstract: A glass container and related methods of manufacturing a glass container. A solution having a composition including a silane, a solvent, a catalyst, and water, is applied to an exterior glass surface of the glass container, at an application temperature between 5 and 40 degrees Celsius, such that the solution at least partially fills the surface imperfections to provide a room-temperature-curable cold-end coating on the glass container. Then, the applied solution is allowed to cure on the exterior glass surface of the glass container, at a curing temperature between 5 and 40 degrees Celsius.

Abstract: A process for cullet beneficiation by precipitation. A mass of cullet is melted to form a body of molten glass having a heavy metal con ration of greater than 100 ppm. A precipitate agent is introduced into the body of molten glass to form a heavy metal-containing precipitate phase and a liquid beneficiated glass phase within the body of molten glass. The precipitate phase may have a density greater than that of the liquid beneficiated glass phase. Thereafter, the liquid beneficiated glass phase is physically separated from the precipitate phase. The separated liquid beneficiated glass phase has a reduced concentration of heavy metals, as compared to the concentration of heavy metals in the body of molten glass.

Abstract: A glass container and related methods of manufacturing a glass container. A solution having a composition including a silane, a solvent, a catalyst, and water, is applied to an exterior glass surface of the glass container, at an application temperature between 5 and 40 degrees Celsius, such that the solution at least partially fills the surface imperfections to provide a room-temperature-curable cold-end coating on the glass container. Then, the applied solution is allowed to cure on the exterior glass surface of the glass container, at a curing temperature between 5 and 40 degrees Celsius.