Abstract: A coated article is provided with an absorbing layer(s). The coating is, in certain example embodiments, designed so that significant changes in visible transmission can be made by adjusting thickness of the absorbing layer without significantly affecting certain other characteristics such as certain color values. Such coated articles may be used monolithically or in the context of insulating glass (IG) units in different embodiments of this invention, and may or may not be heat treated.

Abstract: A coated article that can be used in applications such as insulating glass (IG) units, so that resulting IG units can achieve high visible transmission of at least 70% (e.g., when using clear glass substrates from 1.0 to 3.5 mm thick), combined with at least one of: (a) SHGC no greater than about 0.45, more preferably no greater than about 0.40; (b) SC no greater than about 0.49, more preferably no greater than about 0.46; (c) chemical and/or mechanical durability; (d) neutral transmissive color such that transmissive a* is from ?5.0 to 0 (more preferably from ?3.5 to ?1.5), and transmissive b* is from ?2.0 to 4.0 (more preferably from 1.0 to 3.0); and (e) neutral reflective color from the exterior of the IG unit (i.e., Rg/Rout) such that reflective a* is from ?3.0 to 2.0 (more preferably from ?2.0 to 0.5), and reflective b* is from ?5.0 to 1.0 (more preferably from ?4.0 to ?1.0).

Abstract: A coated article is provided with an absorbing layer(s). The coating is, in certain example embodiments, designed so that significant changes in visible transmission can be made by adjusting thickness of the absorbing layer without significantly affecting certain other characteristics such as certain color values. Such coated articles may be used monolithically or in the context of insulating glass (IG) units in different embodiments of this invention, and may or may not be heat treated.

Abstract: A coated article that can be used in applications such as insulating glass (IG) units, so that resulting IG units can achieve high visible transmission of at least 70% (e.g., when using clear glass substrates from 1.0 to 3.5 mm thick), combined with at least one of: (a) SHGC no greater than about 0.45, more preferably no greater than about 0.40; (b) SC no greater than about 0.49, more preferably no greater than about 0.46; (c) chemical and/or mechanical durability; (d) neutral transmissive color such that transmissive a* is from ?5.0 to 0 (more preferably from ?3.5 to ?1.5), and transmissive b* is from ?2.0 to 4.0 (more preferably from 1.0 to 3.0); and (e) neutral reflective color from the exterior of the IG unit (i.e., Rg/Rout) such that reflective a* is from ?3.0 to 2.0 (more preferably from ?2.0 to 0.5), and reflective b* is from ?5.0 to 1.0 (more preferably from ?4.0 to ?1.0).

Abstract: A coated article that can be used in applications such as insulating glass (IG) units, so that resulting IG units can achieve high visible transmission of at least 70% (e.g., when using clear glass substrates from 1.0 to 3.5 mm thick), combined with at least one of: (a) SHGC no greater than about 0.45, more preferably no greater than about 0.40; (b) SC no greater than about 0.49, more preferably no greater than about 0.46; (c) chemical and/or mechanical durability; (d) neutral transmissive color such that transmissive a* is from ?5.0 to 0 (more preferably from ?3.5 to ?1.5), and transmissive b* is from ?2.0 to 4.0 (more preferably from 1.0 to 3.0); and (e) neutral reflective color from the exterior of the IG unit (i.e., Rg/Rout) such that reflective a* is from ?3.0 to 2.0 (more preferably from ?2.0 to 0.5), and reflective b* is from ?5.0 to 1.0 (more preferably from ?4.0 to ?1.0).

Abstract: A coated article is provided with an absorbing layer(s). The coating is, in certain example embodiments, designed so that significant changes in visible transmission can be made by adjusting thickness of the absorbing layer without significantly affecting certain other characteristics such as certain color values. Such coated articles may be used monolithically or in the context of insulating glass (IG) units in different embodiments of this invention, and may or may not be heat treated.

Abstract: A coated article is provided with an absorbing layer(s). The coating is, in certain example embodiments, designed so that significant changes in visible transmission can be made by adjusting thickness of the absorbing layer without significantly affecting certain other characteristics such as certain color values. Such coated articles may be used monolithically or in the context of insulating glass (IG) units in different embodiments of this invention, and may or may not be heat treated.

Abstract: A coated article is provided with an absorbing layer(s). The coating is, in certain example embodiments, designed so that significant changes in visible transmission can be made by adjusting thickness of the absorbing layer without significantly affecting certain other characteristics such as certain color values. Such coated articles may be used monolithically or in the context of insulating glass (IG) units in different embodiments of this invention, and may or may not be heat treated.

Abstract: A coated article that can be used in applications such as insulating glass (IG) units, so that resulting IG units can achieve high visible transmission of at least 70% (e.g., when using clear glass substrates from 1.0 to 3.5 mm thick), combined with at least one of: (a) SHGC no greater than about 0.45, more preferably no greater than about 0.40; (b) SC no greater than about 0.49, more preferably no greater than about 0.46; (c) chemical and/or mechanical durability; (d) neutral transmissive color such that transmissive a* is from ?5.0 to 0 (more preferably from ?3.5 to ?1.5), and transmissive b* is from ?2.0 to 4.0 (more preferably from 1.0 to 3.0); and (e) neutral reflective color from the exterior of the IG unit (i.e., Rg/Rout) such that reflective a* is from ?3.0 to 2.0 (more preferably from ?2.0 to 0.5), and reflective b* is from ?5.0 to 1.0 (more preferably from ?4.0 to ?1.0).

Abstract: A coated article that can be used in applications such as insulating glass (IG) units, so that resulting IG units can achieve high visible transmission of at least 70% (e.g., when using clear glass substrates from 1.0 to 3.5 mm thick), combined with at least one of: (a) SHGC no greater than about 0.45, more preferably no greater than about 0.40; (b) SC no greater than about 0.49, more preferably no greater than about 0.46; (c) chemical and/or mechanical durability; (d) neutral transmissive color such that transmissive a* is from ?5.0 to 0 (more preferably from ?3.5 to ?1.5), and transmissive b* is from ?2.0 to 4.0 (more preferably from 1.0 to 3.0); and (e) neutral reflective color from the exterior of the IG unit (i.e., Rg/Rout) such that reflective a* is from ?3.0 to 2.0 (more preferably from ?2.0 to 0.5), and reflective b* is from ?5.0 to 1.0 (more preferably from ?4.0 to ?1.0).

Abstract: A coated article that can be used in applications such as insulating glass (IG) units, so that resulting IG units can achieve high visible transmission of at least 70% (e.g., when using clear glass substrates from 1.0 to 3.5 mm thick), combined with at least one of: (a) SHGC no greater than about 0.45, more preferably no greater than about 0.40; (b) SC no greater than about 0.49, more preferably no greater than about 0.46; (c) chemical and/or mechanical durability; (d) neutral transmissive color such that transmissive a* is from ?5.0 to 0 (more preferably from ?3.5 to ?1.5), and transmissive b* is from ?2.0 to 4.0 (more preferably from 1.0 to 3.0); and (e) neutral reflective color from the exterior of the IG unit (i.e., Rg/Rout) such that reflective a* is from ?3.0 to 2.0 (more preferably from ?2.0 to 0.5), and reflective b* is from ?5.0 to 1.0 (more preferably from ?4.0 to ?1.0).

Abstract: A coated article that can be used in applications such as insulating glass (IG) units, so that resulting IG units can achieve high visible transmission of at least 70% (e.g., when using clear glass substrates from 1.0 to 3.5 mm thick), combined with at least one of: (a) SHGC no greater than about 0.45, more preferably no greater than about 0.40; (b) SC no greater than about 0.49, more preferably no greater than about 0.46; (c) chemical and/or mechanical durability; (d) neutral transmissive color such that transmissive a* is from ?5.0 to 0 (more preferably from ?3.5 to ?1.5), and transmissive b* is from ?2.0 to 4.0 (more preferably from 1.0 to 3.0); and (e) neutral reflective color from the exterior of the IG unit (i.e., Rg/Rout) such that reflective a* is from ?3.0 to 2.0 (more preferably from ?2.0 to 0.5), and reflective b* is from ?5.0 to 1.0 (more preferably from ?4.0 to ?1.0).