Abstract: Provided in this disclosure is an ethylene interpolymer composition. The ethylene interpolymer composition includes a first ethylene interpolymer, a second ethylene interpolymer, and a third ethylene interpolymer. Further, the ethylene interpolymer composition has a density of at least 0.945 g/cm3; an environmental stress crack resistance (ESCR), measured according to ASTM D1693, Condition B, 10% IGEPAL CO-360, of at least 90 hours; and an Izod impact strength of at least 80 J/m, as measured according to ASTM D256.

Abstract: High density polyethylene compositions having a high flow index and a bimodal composition provides an outstanding combination of processability, stiffness and ductility in rotomolded articles. The compositions have a low relative elasticity (G?/G?, measured at 0.05 rad/sec) of less than 0.03.

Abstract: A rotomolding composition comprises a blend of two polyethylenes: 1) a well stabilized polyethylene; and 2) a poorly stabilized polyethylene having a very low flow rate. The poorly stabilized polyethylene is further characterized by having a large particle size (from 500 to 3000 microns). Rotomolded parts prepared from the composition have a rough inner surface. Polyurethane foam adheres well to this rough surface.

Abstract: An interpolymer product comprising: a first ethylene interpolymer comprising ethylene and an ?-olefin having a weight-average molecular weight (Mw) of greater than 250,000 and a density of less than 0.930 g/cm3, and a second ethylene interpolymer comprising ethylene and an ?-olefin wherein the second ethylene interpolymer comprises a Mw of less than 70,000 and a density of greater than 0.930 g/cm3; and wherein the interpolymer product comprises an environmental stress crack resistance (ESCR), measured according to ASTM D1693, Condition B, 10% IGEPAL CO-630, of greater than 90 hours. The interpolymer product may be manufactured in a continuous solution polymerization process utilizing at least two reactors employing at least one single site catalyst formulation and at least one heterogeneous catalyst formulation.

Abstract: A dual reactor solution process gives high density polyethylene compositions containing a first ethylene copolymer and a second ethylene copolymer and which have good processability, toughness, and environmental stress crack resistance. The polyethylene compositions are suitable for the preparation of rotomolded parts.

Abstract: A polyethylene composition having a high flow index and a bimodal composition provides an outstanding combination of environmental stress crack resistance (ESCR) and ductility in rotomolded articles. The composition is easy to process/mold.

Abstract: Rotomolded articles, especially flexible rotomolded articles are made from an ethylene interpolymer product having a melt index, I2 of from 2.5 to 8.0 g/10 min, a density of from 0.905 to 0.920 g/cm3; and a Dilution Index, Yd, greater than 0. The ethylene interpolymer product comprises: (I) a first ethylene interpolymer; (II) a second ethylene interpolymer, and; (III) optionally a third ethylene interpolymer.

Abstract: Rotomolded articles, especially flexible rotomolded articles are made from an ethylene interpolymer product having a melt index, I2 of from 2.5 to 8.0 g/10 min, a density of from 0.905 to 0.920 g/cm3; and a Dilution Index, Yd, greater than 0. The ethylene interpolymer product comprises: (I) a first ethylene interpolymer; (II) a second ethylene interpolymer, and; (III) optionally a third ethylene interpolymer.

Abstract: The present disclosure provides high density polyethylene resins having good low temperature impact resistance. The resins are suitable for use in rotomolding application for large parts. The resin is a bi- or trimodal resin produced using solution phase polymerization in the presence of a single site catalyst.

Abstract: The present disclosure provides high density polyethylene resins having good low temperature impact resistance. The resins are suitable for use in rotomolding application for large parts. The resin is a bi- or trimodal resin produced using solution phase polymerization in the presence of a single site catalyst.

Abstract: This disclosure relates to rotomolded articles, having a wall structure, where the wall structure contains at least one layer containing an ethylene interpolymer product, or a blend containing an ethylene interpolymer product and an ethylene polymer, where the ethylene interpolymer product has a Dilution Index (Yd) greater than 0 and improved Environmental Stress Crack Resistance (ESCR). The ethylene interpolymer product has a melt index from about 0.5 to about 15 dg/minute, a density from about 0.930 to about 0.955 g/cm3, a polydispersity (Mw/Mn) from about 2 to about 6 and a CDBI50 from about 50% to about 98%. Further, the ethylene interpolymer products are a blend of at least two ethylene interpolymers; where one ethylene interpolymer is produced with a single-site catalyst formulation and at least one ethylene interpolymer is produced with a heterogeneous catalyst formulation.

Abstract: The present disclosure provides high density polyethylene resins having good low temperature impact resistance. The resins are suitable for use in rotomolding application for large parts. The resin is a bi- or trimodal resin produced using solution phase polymerization in the presence of a single site catalyst.

Abstract: This disclosure relates to rotomolded articles, having a wall structure, where the wall structure contains at least one layer containing an ethylene interpolymer product, or a blend containing an ethylene interpolymer product and an ethylene polymer, where the ethylene interpolymer product has a Dilution Index (Yd) greater than 0 and improved Environmental Stress Crack Resistance (ESCR). The ethylene interpolymer product has a melt index from about 0.5 to about 15 dg/minute, a density from about 0.930 to about 0.955 g/cm3, a polydispersity (Mw/Mn) from about 2 to about 6 and a CDBI50 from about 50% to about 98%. Further, the ethylene interpolymer products are a blend of at least two ethylene interpolymers; where one ethylene interpolymer is produced with a single-site catalyst formulation and at least one ethylene interpolymer is produced with a heterogeneous catalyst formulation.

Abstract: This disclosure relates to rotomolded articles, having a wall structure, where the wall structure contains at least one layer containing an ethylene interpolymer product, or a blend containing an ethylene interpolymer product, where the ethylene interpolymer product has: a Dilution Index (Yd) greater than ?1.0; total catalytic metal ?3.0 ppm; ?0.03 terminal vinyl unsaturations per 100 carbon atoms. The ethylene interpolymer products have a melt index from about 0.5 to about 15 dg/minute, a density from about 0.930 to about 0.955 g/cm3, a polydispersity (Mw/Mn) from about 2 to about 6 and a CDBI50 from about 50% to about 98%. Further, the ethylene interpolymer products are a blend of at least two ethylene interpolymers; where one ethylene interpolymer is produced with a single-site catalyst formulation and at least one ethylene interpolymer is produced with a heterogeneous catalyst formulation.

Abstract: The present disclosure provides high density polyethylene resins having good low temperature impact resistance. The resins are suitable for use in rotomolding application for large parts. The resin is a bi- or trimodal resin produced using solution phase polymerization in the presence of a single site catalyst.

Abstract: The present disclosure provides a resin suitable for use in rotational molding having an environmental stress crack resistance of greater than 1000 hours. The resin has a density from 0.937 to 0.942 g/cm3, a melt index I2 determined according to ASTM D 1238 (2.16 kg/190° C.—I2) from 4.0 to 7.0 g/10 min, an I21 determined according to ASTM D 1238 (21.6 kg/190° C.—I21) from 160 to 200 g/10 min, an I21/I2 from 30 to 40 and a terminal vinyl unsaturation greater than 0.06, per 1000 carbon atoms; and a primary structure parameter (PSP2) of from 4 to 7, and an overall Mw/Mn from 2.7 to 3.5 comprising from 2 to 5 weight % of one or more C4-8 alpha olefin comonomers.

Abstract: This disclosure relates to rotomolded articles, having a wall structure, where the wall structure contains at least one layer containing an ethylene interpolymer product, or a blend containing an ethylene interpolymer product, where the ethylene interpolymer product has: a Dilution Index (Yd) greater than ?1.0; total catalytic metal ?3.0 ppm; ?0.03 terminal vinyl unsaturations per 100 carbon atoms. The ethylene interpolymer products have a melt index from about 0.5 to about 15 dg/minute, a density from about 0.930 to about 0.955 g/cm3, a polydispersity (Mw/Mn) from about 2 to about 6 and a CDBI50 from about 50% to about 98%. Further, the ethylene interpolymer products are a blend of at least two ethylene interpolymers; where one ethylene interpolymer is produced with a single-site catalyst formulation and at least one ethylene interpolymer is produced with a heterogeneous catalyst formulation.

Abstract: Resins suitable for rotomolded articles comprise a bimodal polyethylene copolymer comprising from 0.1 to 5 weight % of one or more C6-8 alpha olefins and the balance ethylene, comprising from 20 to 50 weight % of a higher molecular weight polymer component having an Mw greater than 120,000 and correspondingly from 80 to 50 weight % of a lower molecular weight polymer component having an Mw less than 100,000 having a density greater than 0.942 g/cc [but less than 0.965 g/cc] and a bent strip ESCR as determined by ASTM D 1693 in 100% Igepal® CO-630 (ethoxylated nonylphenols) for conditions A and B of greater than 1000 hours. The resulting articles have a very good balance of properties and significant ESCR.

Abstract: The present disclosure provides a resin suitable for use in rotational molding having an environmental stress crack resistance of greater than 1000 hours. The resin has a density from 0.937 to 0.942 g/cm3, a melt index I2 determined according to ASTM D 1238 (2.16 kg/190° C.—I2) from 4.0 to 7.0 g/10 min, an I21 determined according to ASTM D 1238 (21.6 kg/190° C.—I21) from 160 to 200 g/10 min, an I21/I2 from 30 to 40 and a terminal vinyl unsaturation greater than 0.06, per 1000 carbon atoms; and a primary structure parameter (PSP2) of from 4 to 7, and an overall Mw/Mn from 2.7 to 3.5 comprising from 2 to 5 weight % of one or more C4-8 alpha olefin comonomers.

Abstract: Resins suitable for rotomolded articles comprise a bimodal polyethylene copolymer comprising from 0.1 to 5 weight % of one or more C6-8 alpha olefins and the balance ethylene, comprising from 20 to 50 weight % of a higher molecular weight polymer component having an Mw greater than 120,000 and correspondingly from 80 to 50 weight % of a lower molecular weight polymer component having an Mw less than 100,000 having a density greater than 0.942 g/cc [but less than 0.965 g/cc] and a bent strip ESCR as determined by ASTM D 1693 in 100% Igepal® CO-630 (ethoxylated nonylphenols) for conditions A and B of greater than 1000 hours. The resulting articles have a very good balance of properties and significant ESCR.