Abstract: A strengthened glass having a stress profile that differs from error-function and parabolic profiles. Stress relaxation and thermal annealing/diffusion effects, which occur at longer ion exchange and/or anneal times increase the depth of compression of the surface layer. A method of achieving these effects is also provided.

Abstract: Embodiments of this disclosure pertain to a strengthened glass article including a first surface and a second surface opposing the first surface defining a thickness (t) of about less than about 1.1 mm, a compressive stress layer extending from the first surface to a depth of compression (DOC) of about 0.1·t or greater, such that when the glass article fracture, it breaks into a plurality of fragments having an aspect ratio of about 5 or less. In some embodiments, the glass article exhibits an equibiaxial flexural strength of about 20 kgf or greater, after being abraded with 90-grit SiC particles at a pressure of 25 psi for 5 seconds. Devices incorporating the glass articles described herein and methods for making the same are also disclosed.

Abstract: Embodiments of a glass-based article including a first surface and a second surface opposing the first surface defining a thickness (t) of about 3 millimeters or less (e.g., about 1 millimeter or less), and a stress profile, wherein all points of the stress profile between a thickness range from about 0·t up to 0.3·t and from greater than about 0.7·t up to t, comprise a tangent with a slope having an absolute value greater than about 0.1 MPa/micrometer, are disclosed. In some embodiments, the glass-based article includes a non-zero metal oxide concentration that varies along at least a portion of the thickness (e.g., 0·t to about 0.3·t) and a maximum central tension in the range from about 80 MPa to about 100 MPa. In some embodiments, the concentration of metal oxide or alkali metal oxide decreases from the first surface to a value at a point between the first surface and the second surface and increases from the value to the second surface. The concentration of the metal oxide may be about 0.

Abstract: An opaque gahnite-spinel glass ceramic is provided. The glass ceramic includes a first crystal phase including (MgxZn1-x)Al2O4 where x is less than 1 and a second crystal phase includes at least one of tetragonal ZrO2, MgTa2O6, mullite, and cordierite. The glass ceramic has a Young's modulus greater than or equal to 90 GPa, and has a hardness greater than or equal to 7.5 GPa. The glass ceramic may be ion exchanged. Methods for producing the glass ceramic are also provided.

Abstract: A black ?-spodumene lithium disilicate glass ceramic is provided. The glass ceramic includes at least one of magnetite, ?-quartz, cristobalite, and lithium phosphate as a minor crystal phase. The glass ceramic is characterized by the color coordinates: L*: 15.0 to 35.0, a*: ?3.0 to 3.0, and b*: ?5.0 to 5.0. The glass ceramic may be ion exchanged. Methods for producing the glass ceramic are also provided.

Abstract: A material system for a surface display unit that includes a first side (i.e., a proximal side) that faces a viewer of the surface display unit and a second side (i.e., a distal side) facing away from the viewer. The material system provides at least three appearance states, including a generally opaque first appearance state when the surface display unit is “off” (i.e., not used to display images), a second appearance state in which the material system is illuminated from the first (i.e., proximal) side to display a first image (e.g., information and/or decoration) that is perceptible to the viewer, and a third appearance state in which the material system is illuminated from the second (i.e., distal) side to display a second image (e.g., information and/or decoration) that is perceptible to the viewer. Surface display units, systems, and methods comprising the material system are also disclosed.

Abstract: Ion-exchanged glass ceramic articles described herein have a stress that decreases with increasing distance according to a substantially linear function from a depth of about 0.07 t to a depth of about 0.26 t from the outer surface of the ion-exchanged glass ceramic article from a compressive stress to a tensile stress. The stress transitions from the compressive stress to the tensile stress at a depth of from about 0.18 t to about 0.25 t from the outer surface of the ion-exchanged glass ceramic article. An absolute value of a maximum compressive stress at the outer surface of the ion-exchanged glass article is from 1.8 to 2.2 times an absolute value of a maximum central tension (CT) of the ion-exchanged glass article, and the glass ceramic article has a fracture toughness of 1 MPa?m or more as measured according to the double cantilever beam method.

Abstract: A glass pharmaceutical package having a glass composition of 68.00 mol % to 81.00 mol % SiO2, from 4.00 mol % to 11.00 mol % Al2O3, from 0.10 mol % to 16.00 mol % Li2O, from 0.10 mol % to 12.00 mol % Na2O, from 0.00 mol % to 5.00 mol % K2O, from 0.10 mol % to 8.00 mol % MgO, from 0.10 mol % to 5.00 mol % CaO, from 0.00 mol % to 0.20 mol % fining agent. The glass pharmaceutical package is delamination resistant, and has class 1 or class 2 chemical durability in acid, base, and water. The glass pharmaceutical package may be substantially free of B2O3, SrO, BaO, and ZrO2.

Abstract: Embodiments of glass ceramic articles and precursor glasses are disclosed. In one or more embodiments, the glass-ceramic articles are transparent and include a nepheline phase and a phosphate phase. The glass-ceramic articles are colorless and exhibit a transmittance of about 70% or greater across the visible spectrum. The glass-ceramic articles may optionally include a lithium aluminosilicate phase. The crystals of the glass-ceramic articles may have a major cross-section of about 100 nm or less.

Abstract: A strengthened glass having a stress profile that differs from error-function and parabolic profiles. Stress relaxation and thermal annealing/diffusion effects, which occur at longer ion exchange and/or anneal times increase the depth of compression of the surface layer. A method of achieving these effects is also provided.

Abstract: Embodiments of the present disclosure pertain to crystallizable glasses and glass-ceramics that exhibit a black color and are opaque. In one or more embodiments, the crystallizable glasses and glass-ceramics include a precursor glass composition that exhibits a liquidus viscosity of greater than about 20 kPa*s. The glass-ceramics exhibit less than about 20 wt % of one or more crystalline phases, which can include a plurality of crystallites in the Fe2O3—TiO2—MgO system and an area fraction of less than about 15%. Exemplary compositions used in the crystallizable glasses and glass-ceramics include, in mol %, SiO2 in the range from about 50 to about 76, Al2O3 in the range from about 4 to about 25, P2O5+B2O3 in the range from about 0 to about 14, R2O in the range from about 2 to about 20, one or more nucleating agents in the range from about 0 to about 5, and RO in the range from about 0 to about 20.

Abstract: Glass-based articles are provided that exhibit improved fracture resistance. The relationships between properties attributable to the glass composition and stress profile of the glass-based articles are provided that indicate improved fracture resistance.

Abstract: Crystallizable glasses, glass-ceramics, IXable glass-ceramics, and IX glass-ceramics are disclosed. The glass-ceramics exhibit ?-spodumene ss as the predominant crystalline phase. These glasses and glass-ceramics, in mole %, include: 62-75 SiO2; 10.5-18 Al2O3; 5-14 Li2O; 2-12 B2O3; and 0.4-2 Fe2O3. Additionally, these glasses and glass-ceramics can exhibit the following criteria: a ratio: [ Li 2 ? O + Na 2 ? O + K 2 ? O + MgO + ZnO ] [ Al 2 ? O 3 ] between 0.8 to 1.5. The glass-ceramics also exhibit colors at an observer angle of 10° and a CIE illuminant F02 determined with specular reflectance of a* between ?0.5 and 0.5, b* between ?2.5 and +2, and L* between 90 and 93.

Abstract: Embodiments of this disclosure pertain to a strengthened glass article including a first surface and a second surface opposing the first surface defining a thickness (t) of about less than about 1.1 mm, a compressive stress layer extending from the first surface to a depth of compression (DOC) of about 0.1·t or greater, such that when the glass article fracture, it breaks into a plurality of fragments having an aspect ratio of about 5 or less. In some embodiments, the glass article exhibits an equibiaxial flexural strength of about 20 kgf or greater, after being abraded with 90-grit SiC particles at a pressure of 25 psi for 5 seconds. Devices incorporating the glass articles described herein and methods for making the same are also disclosed.

Abstract: Disclosed herein are glass-ceramics having crystalline phases including ?-spodumene ss and either (i) pseudobrookite or (ii) vanadium or vanadium containing compounds so as to be colored and opaque glass-ceramics having coordinates, determined from total reflectance—specular included—measurements, in the CIELAB color space of the following ranges: L*=from about 20 to about 45; a*=from about ?2 to about +2; and b*=from about ?12 to about +1. Such CIELAB color space coordinates can be substantially uniform throughout the glass-ceramics. In each of the proceeding, ?-quartz ss can be substantially absent from the crystalline phases. If present, ?-quartz ss can be less than about 20 wt % or, alternatively, less than about 15 wt % of the crystalline phases. Also Further crystalline phases might include spinel ss (e.g., hercynite and/or gahnite-hercynite ss), rutile, magnesium zinc phosphate, or spinel ss (e.g., hercynite and/or gahnite-hercynite ss) and rutile.

Abstract: Embodiments of thermally and chemically strengthened glass-based articles are disclosed. In one or more embodiments, the glass-based articles may include a first surface and a second surface opposing the first surface defining a thickness (t), a first CS region comprising a concentration of a metal oxide that is both non-zero and varies along a portion of the thickness, and a second CS region being substantially free of the metal oxide of the first CS region, the second CS region extending from the first surface to a depth of compression of about 0.17?t or greater. In one or more embodiments, the first surface is flat to 100 ?m total indicator run-out (TIR) along any 50 mm or less profile of the first surface. Methods of strengthening glass sheets are also disclosed, along with consumer electronic products, laminates and vehicles including the same are also disclosed.

Abstract: Embodiments of a glass-based article including a first surface and a second surface opposing the first surface defining a thickness (t) of about 3 millimeters or less (e.g., about 1 millimeter or less), and a stress profile, wherein all points of the stress profile between a thickness range from about 0·t up to 0.3·t and from greater than about 0.7·t up to t, comprise a tangent with a slope having an absolute value greater than about 0.1 MPa/micrometer, are disclosed. In some embodiments, the glass-based article includes a non-zero metal oxide concentration that varies along at least a portion of the thickness (e.g., 0·t to about 0.3·t) and a maximum central tension in the range from about 80 MPa to about 100 MPa. In some embodiments, the concentration of metal oxide or alkali metal oxide decreases from the first surface to a value at a point between the first surface and the second surface and increases from the value to the second surface. The concentration of the metal oxide may be about 0.

Abstract: A glass-ceramic article having one or more crystalline phases; a residual glass phase; a compressive stress layer extending from a first surface to a depth of compression (DOC); a maximum central tension greater than 70 MPa; a stored tensile energy greater than 22 J/m2; a fracture toughness greater than 1.0 MPa?m; and a haze less than 0.2.

Abstract: A glass ceramic article including a lithium disilicate crystalline phase, a petalite crystalline phased, and a residual glass phase. The glass ceramic article has a warp (?m)<(3.65×10?6/?m×diagonal2) where diagonal is a diagonal measurement of the glass ceramic article in ?m, a stress of less than 30 nm of retardation per mm of glass ceramic article thickness, a haze (%)<0.0994t+0.12 where t is the thickness of the glass ceramic article in mm, and an optical transmission (%)>0.91×10(2-0.03t) of electromagnetic radiation wavelengths from 450 nm to 800 nm, where t is the thickness of the glass ceramic article in mm.

Abstract: Embodiments of a glass-based article including a first surface and a second surface opposing the first surface defining a thickness (t) of about 3 millimeters or less (e.g., about 1 millimeter or less), and a stress profile, wherein all points of the stress profile between a thickness range from about 0·t up to 0.3·t and from greater than 0.7·t, comprise a tangent that is less than about ?0.1 MPa/micrometers or greater than about 0.1 MPa/micrometers, are disclosed. In some embodiments, the glass-based article includes a non-zero metal oxide concentration that varies along at least a portion of the thickness (e.g., 0·t to about 0.3·t). In some embodiments, the concentration of metal oxide or alkali metal oxide decreases from the first surface to a point between the first surface and the second surface and increases from the point to the second surface. The concentration of the metal oxide may be about 0.05 mol % or greater or about 0.5 mol % or greater throughout the thickness.