Abstract: A curable, high temperature, carbonaceous, cement paste composition comprising a catalyst; a carbon filler present in an amount of about 20 to about 60 wt. %; a polymerizable monomeric system present in an amount of about 7 to about 30 wt. % comprising a dialkyl ester of an aromatic tetracarboxylic acid, an aromatic diamine, and a monoalkyl ester of an acid selected from the group consisting of 5-norbornene-2,3-dicarboxylic acid and phthalic acid; and a furan solvent present in an amount of about 20 to about 60 wt. %. The most preferred embodiment comprising a monomeric system comprising a dimethyl ester of 3,3′,4,4′-benzophenonetetracarboxylic acid, 2,2′-bis (4-[4-aminophenoxyl]phenyl)propane and a monomethyl ester of 5-norbornene-2,3-dicarboxylic acid with furfuryl alcohol and a catalytic solution of about 50% ZnCl2, has a glass transition temperature of about 280° C. after curing by heating at about 2° C./minute to about 240° C. and holding for about 2 hours.