Abstract: In accordance with one aspect of the present disclosure, there is provided a steel material for a tailor-welded blank, including 0.04 to 0.06 wt % of carbon (C), 1.2 to 1.5 wt % of manganese (Mn), 0.01 to 0.10 wt % of titanium (Ti), 0.01 to 0.10 wt % of niobium (Nb), and the balance of iron (Fe) and inevitable impurities; having a tensile strength (TS) of 550 MPa or greater, a yield strength (YS) of 300 MPa or greater, and an elongation (EL) of 20% or greater; and having a dual-phase structure of ferrite and martensite.

Abstract: In accordance with one aspect of the present disclosure, there is provided a steel material for a tailor-welded blank, including 0.04 to 0.06 wt % of carbon (C), 1.2 to 1.5 wt % of manganese (Mn), 0.01 to 0.10 wt % of titanium (Ti), 0.01 to 0.10 wt % of niobium (Nb), and the balance of iron (Fe) and inevitable impurities; having a tensile strength (TS) of 550 MPa or greater, a yield strength (YS) of 300 MPa or greater, and an elongation (EL) of 20% or greater; and having a dual-phase structure of ferrite and martensite.

Abstract: A method for producing a molded article includes the steps of: preparing a first steel plate and a second steel plate. The first steel plate and the second steel plate are joined to each other, thereby preparing a joined steel plate. The joined steel plate is heated at a temperature between 910° C. and 950° C. The heated joined steel plate is then subjected to hot-press molding, thereby preparing an intermediate molded article; and cooling the intermediate molded article, wherein the first steel plate has a tensile strength (TS) higher than that of the second steel plate.

Abstract: A method for manufacturing a hot-stamped part includes reheating a steel slab at a temperature of 1,200° C. to 1,250° C., the steel slab including, by wt %, 0.20 to 0.50% carbon (C), 0.05 to 1.00% silicon (Si), 0.10 to 2.50% manganese (Mn), more than 0% and not more than 0.015% phosphorus (P), more than 0% and not more than 0.005% sulfur (S), 0.05 to 1.00% chromium (Cr), 0.001 to 0.009% boron (B), 0.01 to 0.09% titanium (Ti), and a balance of iron (Fe) and inevitable impurities; finish-rolling the reheated steel slab at a temperature of 880° C. to 950° C.; cooling the hot-rolled steel plate without using water, and coiling the cooled steel plate at a temperature of 680° C. to 800° C. to form a hot-rolled decarburized layer on a surface of the steel plate; pickling the coiled steel plate, followed by cold rolling; annealing the cold-rolled steel plate in a reducing atmosphere; plating the annealed steel plate; and hot-stamping the plated steel plate.

Abstract: In accordance with one aspect of the present disclosure, there is provided a steel material for a tailor-welded blank, including 0.04 to 0.06 wt % of carbon (C), 1.2 to 1.5 wt % of manganese (Mn), 0.01 to 0.10 wt % of titanium (Ti), 0.01 to 0.10 wt % of niobium (Nb), and the balance of iron (Fe) and inevitable impurities; having a tensile strength (TS) of 550 MPa or greater, a yield strength (YS) of 300 MPa or greater, and an elongation (EL) of 20% or greater; and having a dual-phase structure of ferrite and martensite.

Abstract: In accordance with one aspect of the present disclosure, there is provided a steel material for a tailor-welded blank, including 0.04 to 0.06 wt % of carbon (C), 1.2 to 1.5 wt % of manganese (Mn), 0.01 to 0.10 wt % of titanium (Ti), 0.01 to 0.10 wt % of niobium (Nb), and the balance of iron (Fe) and inevitable impurities; having a tensile strength (TS) of 550 MPa or greater, a yield strength (YS) of 300 MPa or greater, and an elongation (EL) of 20% or greater; and having a dual-phase structure of ferrite and martensite.

Abstract: A method for manufacturing a hot-stamped part includes reheating a steel slab at a temperature of 1,200° C. to 1,250° C., the steel slab including, by wt %, 0.20 to 0.50% carbon (C), 0.05 to 1.00% silicon (Si), 0.10 to 2.50% manganese (Mn), more than 0% and not more than 0.015% phosphorus (P), more than 0% and not more than 0.005% sulfur (S), 0.05 to 1.00% chromium (Cr), 0.001 to 0.009% boron (B), 0.01 to 0.09% titanium (Ti), and a balance of iron (Fe) and inevitable impurities; finish-rolling the reheated steel slab at a temperature of 880° C. to 950° C.; cooling the hot-rolled steel plate without using water, and coiling the cooled steel plate at a temperature of 680° C. to 800° C. to form a hot-rolled decarburized layer on a surface of the steel plate; pickling the coiled steel plate, followed by cold rolling; annealing the cold-rolled steel plate in a reducing atmosphere; plating the annealed steel plate; and hot-stamping the plated steel plate.

Abstract: A method for producing a molded article includes the steps of: preparing a first steel plate and a second steel plate. The first steel plate and the second steel plate are joined to each other, thereby preparing a joined steel plate. The joined steel plate is heated at a temperature between 910° C. and 950° C. The heated joined steel plate is then subjected to hot-press molding, thereby preparing an intermediate molded article; and cooling the intermediate molded article, wherein the first steel plate has a tensile strength (TS) higher than that of the second steel plate.