Abstract: An object is to provide an adsorbent using activated carbon fiber, the adsorbent being suitable for motor vehicle canisters and enabling reduction in pressure loss. An activated carbon fiber sheet for a motor vehicle canister fulfils the following conditions (1) to (4). (1) The sheet has a specific surface area ranging from 1100 to 2300 m2/g. (2) The sheet has a density ranging from 0.010 to 0.200 g/cm3 or less. (3) The sheet has a thickness ranging from 0.1 to 100.00 mm. (4) The sheet has a fiber size of 13.0 ?m or larger.

Abstract: A problem to be solved by the present invention is to provide a new form of adsorbent suitable for a motor vehicle canister. An activated carbon fiber sheet satisfies one or two or more of conditions for indices, such as a specific surface area, a pore volume of pores having a given pore diameter, and a sheet density. An embodiment, for example, may have: a specific surface area ranging from 1400 to 2300 m2/g; a pore volume ranging from 0.20 to 0.70 cm3/g for pores having pore diameters of more than 0.7 nm and 2.0 nm or less; an abundance ratio R0.7/2.0, which is a ratio of a pore volume of micropores having pore diameters of 0.7 nm or less occupied in a pore volume of micropores having pore diameters of 2.0 nm or less, ranging from 5% to less than 25%, and a sheet density ranging from 0.030 to 0.200 g/cm3.

Abstract: An object is to provide a new form of adsorbent suitable for a high performance canister. An adsorbent including activated carbon is used as the adsorbent for the canister and satisfies the following conditions. P0.2/100 expressed by Equation 1: P0.2/100=X÷Y×100??(Equation 1) is 18% or more, in Equation 1, X represents an amount of adsorbed n-butane gas per 100 parts by weight of the adsorbent at 25° C. under an atmosphere where a gas pressure of n-butane gas is 0.2 kPa, and Y represents an amount of adsorbed n-butane gas per 100 parts by weight of the adsorbent at 25° C. under an atmosphere where a gas pressure of n-butane gas is 100 kPa.

Abstract: An object of the present invention is to provide a new form of adsorbent suitable for a motor vehicle canister. An activated carbon fiber sheet satisfies one or two or more of conditions for indices, such as a specific surface area, a pore volume of pores having a given pore diameter, and a sheet density. An embodiment, for example, may have: a specific surface area ranging from 1400 to 2200 m2/g; a pore volume ranging from 0.20 to 1.20 cm3/g for pores having pore diameters of more than 0.7 nm and 2.0 nm or less; and a sheet density ranging from 0.030 to 0.200 g/cm3.

Abstract: A problem to be solved by the present invention is to provide a new form of adsorbent suitable for a motor vehicle canister. An activated carbon fiber sheet satisfies one or two or more of conditions for indices, such as a specific surface area, a pore volume of pores having a given pore diameter, and a sheet density. An embodiment, for example, may have: a specific surface area ranging from 1400 to 2300 m2/g; a pore volume ranging from 0.20 to 0.70 cm3/g for pores having pore diameters of more than 0.7 nm and 2.0 nm or less; an abundance ratio R0.7/2.0, which is a ratio of a pore volume of micropores having pore diameters of 0.7 nm or less occupied in a pore volume of micropores having pore diameters of 2.0 nm or less, ranging from 5% to less than 25%, and a sheet density ranging from 0.030 to 0.200 g/cm3.

Abstract: An object is to provide a new form of adsorbent suitable for a high performance canister. An adsorbent including activated carbon is used as the adsorbent for the canister and satisfies the following conditions. P0.2/100 expressed by Equation 1: P0.2/100=X÷Y×100??(Equation 1) is 18% or more, in Equation 1, X represents an amount of adsorbed n-butane gas per 100 parts by weight of the adsorbent at 25° C. under an atmosphere where a gas pressure of n-butane gas is 0.2 kPa, and Y represents an amount of adsorbed n-butane gas per 100 parts by weight of the adsorbent at 25° C. under an atmosphere where a gas pressure of n-butane gas is 100 kPa.

Abstract: An object is to provide an adsorbent using activated carbon fiber, the adsorbent being suitable for motor vehicle canisters and enabling reduction in pressure loss. An activated carbon fiber sheet for a motor vehicle canister fulfils the following conditions (1) to (4). (1) The sheet has a specific surface area ranging from 1100 to 2300 m2/g. (2) The sheet has a density ranging from 0.010 to 0.200 g/cm3 or less. (3) The sheet has a thickness ranging from 0.1 to 100.00 mm. (4) The sheet has a fiber size of 13.0 ?m or larger.

Abstract: An object of the present invention is to provide a new form of adsorbent suitable for a motor vehicle canister. An activated carbon fiber sheet satisfies one or two or more of conditions for indices, such as a specific surface area, a pore volume of pores having a given pore diameter, and a sheet density. An embodiment, for example, may have: a specific surface area ranging from 1400 to 2200 m2/g; a pore volume ranging from 0.20 to 1.20 cm3/g for pores having pore diameters of more than 0.7 nm and 2.0 nm or less; and a sheet density ranging from 0.030 to 0.200 g/cm3.

Abstract: In this game system, a plurality of game devices are connected to a game parent station over a communication network, and an online game application may be executed on the game devices by means of the game parent station. In this game system, the game devices are provided with a personal information processing means that can exchange personal information with other players while the online game application is executed among the game devices. Therefore, personal information in the form of a business card may be exchanged with an opponent by means of the personal information processing means either after a game has ended or when a game begins.

Abstract: In this game system, a plurality of game devices 1 are connected to a game parent station 7 over a communication network 3, and an online game application may be executed on the game devices 1 by means of the game parent station 7. In this game system, the game devices 1 are provided with a personal information processing means 10 that can exchange personal information with other players while the online game application is executed among the game devices 1. Therefore, personal information in the form of a business card may be exchanged with an opponent by means of the personal information processing means 10 either after a game has ended or when a game begins.

Abstract: In this game system, a plurality of game devices 1 are connected to a game parent station 7 over a communication network 3, and an online game application may be executed on the game devices 1 by means of the game parent station 7. In this game system, the game devices 1 are provided with a personal information processing means 10 that can exchange personal information with other players while the online game application is executed among the game devices 1. Therefore, personal information in the form of a business card may be exchanged with an opponent by means of the personal information processing means 10 either after a game has ended or when a game begins.

Abstract: A gas diffusion electrode is manufactured by preparing a slurry containing an electrically conductive powder, carbon fibers, organic fibers and a resin in specific proportions, forming the slurry into a sheet, and heating and drying the sheet. The electrode has the volume resistivity, thermal conductivity and gas permeability required for use in fuel cells, exhibits a flexibility conducive to continuous production, and does not break under the application of pressure during electrode production or fuel cell assembly.