Abstract: A process for preparing catalytically active coatings for the synthesis of hydrogen cyanide on moulded items substantially consisting of aluminum oxide. The catalytically active coatings contain, as active components, at least one platinum group metal and a nitride waich are applied to the moulded item by means of a coating dispersion which contains the active components as finely divided solids. This means that the hitherto conventional production of aluminum nitride during the forming process is not required. The coatings therefore achieve their final activity level, which is well above that of conventional coatings, very rapidly. In addition, these catalysts can be started up under high load and have a lower operating temperature.

Abstract: A process for preparing catalytically active coatings for the synthesis of hydrogen cyanide on moulded items substantially consisting of aluminum oxide. The catalytically active coating contain, as active components, at least one platinum group metal and a nitrate which are applied to the moulded item by means of a coating dispersion which contains the active components as finely divided solids. This means that the hitherto conventional production of aluminum nitride during the forming process is not required. The coatings therefore achieve their final activity level, which is well above that of conventional coatings, very rapidly. In addition, these catalysts can be started up under high load and have a lower operating temperature.

Abstract: A process for the highly efficient production of hydrocyanic acid by reacting methane and ammonia to yield hydrocyanic acid in a reactor heated by the combustion of fuel gases and coated with a catalyst. The process is characterized in that the reactor consists of a monolithic arrangement of heating and reaction channels, wherein the fuel gas and a gas containing oxygen pass through the heating channels and the reactants pass through the reaction channels, the internal walls of which are coated with the catalyst. The fuel gas is burned in the heating channels. The monolithic structure of the reactor is such that the heating channels and reaction channels are in intimate contact. The cross-section of the channels and the wall thicknesses thereof may be reduced without any loss of mechanical stability. Wall thicknesses of 0.1 to 1 mm are completely adequate.