Abstract: Lithium silicate materials are described which can be easily processed by machining to dental products without undue wear of the tools.

Abstract: The invention relates to glass ceramics and glasses with a europium content, containing the following components: Component wt.-% SiO2 30.0 to 75.0 Al2O3 10.0 to 45.0 Europium, calculated as Eu2O3 0.05 to 5.0? and which are suitable in particular for the production of restorations, the fluorescence properties of which largely correspond to those of natural teeth.

Abstract: The invention relates to multi-layer oxide ceramic bodies and in particular to presintered multi-layer oxide ceramic blanks and oxide ceramic green bodies suitable for dental applications. These bodies can be thermally densified by further sintering without distortion and are thus particularly suitable for the manufacture of dental restorations. The invention also relates to a process for the manufacture of such multi-layer oxide ceramic bodies as well as to a process for the manufacture of dental restorations using the multi-layer oxide ceramic bodies.

Abstract: Lithium silicate-low quartz glass ceramics are described which are characterized by a combination of very good mechanical and optical properties and can therefore be used in particular as restoration material in dentistry.

Abstract: The invention relates to glass ceramics and glasses with a europium content, containing the following components: Component wt.-% SiO2 30.0 to 75.0 Al2O3 10.0 to 45.0 Europium, calculated as Eu2O3 0.05 to 5.0 and which are suitable in particular for the production of dental restorations, the fluorescence properties of which largely correspond to those of natural teeth.

Abstract: Lithium silicate materials are described which can be easily processed by machining to dental products without undue wear of the tools.

Abstract: Lithium silicate-low quartz glass ceramics are described which are characterized by a combination of very good mechanical and optical properties and can therefore be used in particular as restoration material in dentistry.

Abstract: A glazing material for producing a glazed ceramic body, in which at a first temperature T1, the glazing material has a viscosity of more than 102.5 Pa·s, in particular more than 104.0 Pa·s, preferably more than 105.6 Pa·s and particularly preferably more than 107.0 Pa·s, and, which at a second temperature T2, which is higher than the first temperature, a viscosity of less than 109 Pa·s, in particular less than 107 Pa·s and preferably less than 105.6 Pa·s. The glazing material can be used for glazing a non-densely sintered substrate material.

Abstract: A process for the production of a dental shaped body, such as a dental blank or a dental restoration, in which a suspension of a zirconium oxide starting material is gelled by means of a gelling agent, and the use of a suspension of a zirconium oxide starting material as dental material, the suspension containing a gelling agent.

Abstract: A process for producing a glazed ceramic body, in which a glazing material is applied to a non-densely sintered substrate material and the substrate material and the glazing material are subjected to a heat treatment in order to obtain the glazed body.

Abstract: A method for layer-wise additive manufacturing of a shaped body made up of slices of processed layers, including the steps: creating a layer of a slurry, the slurry including binder, a dispersing medium and a particulate filler material, solidifying the slurry layer, directing electromagnetic radiation to the solidified layer for processing it by debinding and/or sintering, and repeating the above-mentioned steps to successively build the shaped body. A laser induced forward transfer (LIFT) process utilizing a laser to direct laser beam pulses acts on a coating of slurry on a carrier to transfer droplets of slurry to a receptor surface to create the slurry layer which is then processed further by above-mentioned steps of solidifying, and debinding and/or sintering.

Abstract: Glass ceramics having SiO2 as main crystal phase and precursors thereof are described which are characterized by very good mechanical and optical properties and in particular can be used as restoration material in dentistry.

Abstract: Lithium silicate materials are described which can be easily processed by machining to dental products without undue wear of the tools.

Abstract: Glass ceramics having SiO2 as main crystal phase and precursors thereof are described which are characterized by very good mechanical and optical properties and in particular can be used as restoration material in dentistry.

Abstract: Lithium silicate materials are described which can be easily processed by machining to dental products without undue wear of the tools and which subsequently can be converted into lithium silicate products showing high strength.

Abstract: The invention relates to a method for the preparation of a glass ceramic or a glass, which comprise cerium ions and are suitable in particular for the preparation of dental restorations, the fluorescence properties of which largely correspond to those of natural teeth. The invention also relates to a glass ceramic and a glass which can be obtained using the method according to the invention, the use thereof as dental material and in particular for the preparation of dental restorations, as well as a glass-forming composition which is suitable for use in the method according to the invention.

Abstract: The present invention is directed to a porous pre-densified CeO2-stabilized ZrO2 ceramic having a density of 50.0 to 95.0%, relative to the theoretical density of zirconia, and an open porosity of 5 to 50% as well as to a densified CeO2-stabilized ZrO2 ceramic having a density of 97.0 to 100.0%, relative to the theoretical density of zirconia, and wherein the grains of the ceramic have an average grain size of 50 to 1000 nm, methods for the preparation of the pre-densified and densified ceramics and their use for the manufacture of dental restorations.

Abstract: Lithium silicate materials are described which can be easily processed by machining to dental products without undue wear of the tools and which subsequently can be converted into lithium silicate products showing high strength.

Abstract: Lithium silicate materials are described which can be easily processed by machining to dental products without undue wear of the tools.

Abstract: The invention relates to glass ceramics and glasses with a europium content, containing the following components: Component wt.-% SiO2 30.0 to 75.0 Al2O3 10.0 to 45.0 Europium, calculated as Eu2O3 0.05 to 5.0? and which are suitable in particular for the production of restorations, the fluorescence properties of which largely correspond to those of natural teeth.