Abstract: Aqueous melamine resin dispersions comprise as discontinuous phase a melamine resin stabilized with a combination of a cationic protective colloid and an anionic protective colloid.

Abstract: An aqueous resin solution for the impregnation of paper webs contains 2-40 parts by weight of a polyurea composed of urea and of a polyamine per 100 parts by weight of a melamine/formaldehyde precondensate. The impregnated paper webs are suitable for coating woodbase materials, especially chipboard.

Abstract: 1,2-Dichloroethane is prepared by oxychlorination of ethylene in the presence of a catalyst which contains, on a conventional carrier, copper(II) chloride in a concentration such that the amount of copper ions is from 1 to 20% by weight, based on the total weight of the catalyst, by a process in which the catalyst is obtained by impregnating the carrier with an aqueous solution which contains copper(II) chloride and hydrogen chloride in amounts such that the weight ratio of copper ions to hydrogen chloride is from 13:1 to 130:1.

Abstract: A process for the manufacture of acicular magnetic iron oxide consisting of a core of gamma-iron(III) oxide and a ferrite shell which contains, based on the total amount of magnetic material, from 0.2 to 12 percent by weight of cobalt(II) ions and from 0.1 to 15 percent by weight of iron(II) ions, wherein a solution containing cobalt(II) hydroxide and iron(II) hydroxide is applied to acicular gamma-iron(III) oxide particles and the latter are heated at 100.degree.-220.degree. C.

Abstract: A process for the manufacture of acicular magnetic iron oxide consisting of core of gamma-iron(III) oxide and a ferrite shell which contains, based on the total amount of magnetic material, from 0.2 to 12 per cent by weight of cobalt(II) ions and from 0.1 to 15 per cent by weight of iron(II) ions, wherein a precipitate of cobalt(II) hydroxide and iron (II) hydroxide is applied to acicular gamma-iron(III) oxide particles and the latter are heated at 100.degree.-200.degree. C.

Abstract: A process for the manufacture of acicular magnetic iron oxides which consist of a core of gamma-iron(III) oxide and a shell of a magnetite modified with zinc(II) ions and/or manganese(II) ions and which contain, based on the total modified gamma-iron(III) oxide, from 0.1 to 20 percent by weight of iron(II) ions, from 0.1 to 10 percent by weight of zinc(II) ions and/or from 0.1 to 10 percent by weight of manganese(II) ions.

Abstract: A process for the manufacture of an acicular magnetic iron oxide containing from 0.5 to 10 percent by weight of cobalt and up to 24 percent by weight of divalent iron, each based on the amount of iron(III) oxide, wherein an aqueous suspension of gamma-iron(III) oxide, containing cobalt(II) and iron(II) ions, the suspension having a hydroxyl ion concentration of more than 3.6.times.10.sup.-6 moles/liter, is heated at from 50.degree. to 100.degree. C. for at least 15 minutes, and the resulting precipitate is filtered off, washed until neutral, dried at below 100.degree. C. and thereafter heated at from 100.degree. to 200.degree. C.The products thus obtained give, even when their cobalt content is low, a very high coercive force, while the effect of temperature on the coercive force and residual induction is very slight.

Abstract: A process for the manufacture of acicular ferromagnetic metal particles which essentially consist of iron and carry, on their surface, from 0.02 to 0.6% by weight of boron in the form of a borate, by reducing an acicular iron oxide with a gaseous reducing agent at from 250.degree. to 500.degree. C., wherein a compound selected from the group comprising boron oxyacids and their inorganic salts is precipitated on the said iron oxide before reduction.

Abstract: A method of preparing acicular ferromagnetic metal particles consisting essentially of iron and suitable for magnetic recording, said particles being modified at the surface with 0.02 to 0.2% by weight of carbon and with 0.5 to 1.9% by weight of phosphorus as phosphate, by reducing a finely divided acicular iron compound, wherein there are deposited on said iron compound, prior to reduction, (a) a hydrolysis-resistant substance selected from the group consisting of oxyacids of phosphorus, their esters and inorganic salts, and (b) a compound selected from the group consisting of aliphatic monobasic, dibasic and tribasic carboxylic acids of from 1 to 6 carbon atoms.