Abstract: The invention relates to a composition and to a method for the production thereof, comprising quaternary amino-functional organosilicon compounds, in particular in the form of oligomers and polymers, which can be present ranging from partially hydrolyzed form to completely hydrolyzed form, and which are in particular soluble in water, have a low VOC content, and to the use thereof.

Abstract: Dispersion obtainable by reacting a) in 50 to 75 parts by weight of water b) 25 to 50 parts by weight of silica particles having a BET surface area of 30 to 500 m2/g and c) 100 to 300 ?g/m2 BET surface area of the silica particles from b) parts by weight of one or more aminofunctional, organosilicon compounds, the aminofunctional, organosilicon compound being a quaternary, aminofunctional, organosilicon compound which is obtainable by reacting at least one haloalkylfunctional silane as component A with a tertiary amine as component B in the presence of a defined amount of water and at least partly removing the resulting hydrolysis alcohol from the system.

Abstract: The invention relates to stabilized dispersions of precipitated silicon dioxide, to a process for production thereof and to the use thereof, especially for production of paper coatings for glossy photo paper for inkjet printing.

Abstract: The present invention relates to the use of a composition in coating agents, which is poor in volatile organic compounds (VOC) or essentially free of VOC, wherein the composition is at least partially based on one or more partially or fully hydrolyzed and optionally condensed or co-condensed aminoalkyl- and oligosilylated-aminoalkyl-, alkoxy- or hydroxy-functional silicon compounds and the alcohol is at least partially removed from the composition. The invention also relates to a composition containing aminoalkyl- or oligosilylated-aminoalkyl-, hydroxy- and optionally alkoxy-functional silicon compounds and to a method for producing such a composition.

Abstract: Process for preparing an aluminium oxide powder which is present in the form of aggregated primary particles and comprises at least 85% by weight of alpha-aluminium oxide, in which an aluminium oxide powder which a) is present in the form of aggregated primary particles, b) is selected from the group consisting of gamma-aluminium oxide, theta-aluminium oxide, delta-aluminium oxide and/or X-ray amorphous aluminium oxide, and c) has a tamped density of at least 250 g/l, is subject to a heat treatment at 13000C or more and subsequently milled. Aluminium oxide powder which can be obtained by this process. Aluminium oxide powder in the form of aggregated primary particles having a BET surface area of from 3 to 30 m2/g, in which the proportion of alpha-aluminium oxide is at least 85% by weight and the ratio dgo/dio of the weight distribution of the primary particles is at least 2.8. Use as constituent of fluorescent tubes.

Abstract: The invention relates to stabilized dispersions of precipitated silicon dioxide, to a process for production thereof and to the use thereof, especially for production of paper coatings for glossy photo paper for inkjet printing.

Abstract: An aqueous dispersion for use as a finishing agent for textiles, wherein the dispersion contains a pyrogenically produced, aggregated silicon dioxide powder and a cationic polymer which is soluble in the dispersion, wherein the cationic polymer is present in a quantity such that the particles of the silicon dioxide powder exhibit a positive zeta potential.

Abstract: Process for the production of an aqueous dispersion of pyrogenically produced metal oxide and metalloid oxide powders with a BET surface area of between 5 and 600 m2/g, with a metal oxide or metalloid oxide content in the dispersion of between 5 and 25 wt. %, comprising the following steps: water, which is optionally adjusted to pH values of between 2 and 4 by adding acids, is circulated from a receiving vessel via a rotor/stator machine, and metal oxide or metalloid oxide powder is introduced, using a feed device, into the shear zone between the slots in the rotor teeth and the stator slots, continuously or discontinuously and with the rotor/stator machine running, in a quantity such that a predispersion with a solids content of between 20 and 40 wt.

Abstract: An aqueous dispersion for use as a finishing agent for textiles, wherein the dispersion contains a pyrogenically produced, aggregated silicon dioxide powder and a cationic polymer which is soluble in the dispersion, wherein the cationic polymer is present in a quantity such that the particles of the silicon dioxide powder exhibit a positive zeta potential.

Abstract: Stable, pourable silicon dioxide dispersion, in which the average, number-related aggregate diameter of the silicon dioxide particles in dispersion is less than 200 nm, and which comprises at least 35 wt. % of a silicon dioxide powder, 3 to 35 wt. % of at least one polyol, 20 to 60 wt. % of water, 0 to 10 wt. % of an additive and a substance having an alkaline action in an amount such that a pH of 10<pH?12 is established. It can be prepared by a procedure in which silicon dioxide powder is introduced into water and a polyol in a rotor/stator machine, the pH being less than 5, and the mixture is dispersed until the current uptake of the rotor/stator machine is largely constant, and a substance having an alkaline action is subsequently added in an amount such that a pH of the dispersion of 10<pH?12 results, the substance having an alkaline reaction being added so rapidly that no gel formation takes place.

Abstract: Dispersion of aluminium oxide, characterised in that it contains 20 to 60 wt.-% of pyrogenically-produced aluminium oxide powder in form of aggregates of primary particles, wherein the powder has - a BET specific surface area of from 50 to 150 m2/g—a ratio Sears number/BET surface area which is from about 0.150 to 0.160, wherein the mean aggregate diameter in the dispersion is less than 200 nm.

Abstract: An aqueous dispersion that can be used in the coating of glass, ceramics and metal surfaces is prepared by placing, in water, an aggregated titanium dioxide powder having a specific surface area of from 20 to 150 m2/g in such an amount that the desired dispersion contains at least 20 wt. % titanium dioxide, and at least one amino alcohol having from 1 to 6 carbon atoms, and at least one carboxylic acid selected from dibasic carboxylic acids and/or hydroxycarboxylic acids having from 2 to 6 carbon atoms. A pre-dispersion is produced by introducing energy in an amount of less than 200 kJ/m3. Then a dispersion is produced in which the aggregated titanium dioxide powder has a mean, volume-related aggregate diameter of less than 150 nm by grinding the pre-dispersion with a high-energy mill at a pressure of at least 500 bar.

Abstract: Aluminium oxide powder produced by flame hydrolysis and consisting of aggregates of primary particles, having a BET surface area of from 100 to 250 m2/g, a dibutyl phthalate absorption of from 50 to 450 g/100 g of aluminium oxide powder, which powder shows only crystalline primary particles in high-resolution TEM pictures.

Abstract: Ink jet ink containing at least one pigment and at least one oxidized carbon black. The ink jet ink is prepared in a process wherein the pigment is dispersed in at least one solvent, followed by addition of the oxidized carbon black and renewed dispersing. The ink jet ink can be used for printing textiles, metal, foil, film, sheet, glass and paper.

Abstract: An aqueous dispersion for use as a finishing agent for textiles, wherein the dispersion contains a pyrogenically produced, aggregated silicon dioxide powder and a cationic polymer which is soluble in the dispersion, wherein the cationic polymer is present in a quantity such that the particles of the silicon dioxide powder exhibit a positive zeta potential.

Abstract: Preparation for producing refractory materials, characterized in that it comprises one or more particulate, refractory components and one or more binders, where—the particulate, refractory component has a mean particle diameter of >0.3 m and—the binder is selected from among—from 0.05 to 50% by weight of a very finely particulate binder having a mean particle diameter of from 10 nm to 0.3 m selected from the group consisting of aluminium oxide, titanium dioxide, zirconium dioxide and/or mixed oxides of the abovementioned oxides, —from 0 to 20% by weight of an inorganic binder, from 0 to 20% by weight of a hydraulically setting binder, —from 0 to 15% by weight of an organic, silicon-free binder—and the preparation additionally contains from 0 to 35% by weight of water, where—the proportion of the particulate, refractory component is equal to 100 and the percentages of the further materials in the preparation are based on the particulate component.

Abstract: Aqueous dispersion which comprises hydrophobized silicon dioxide powder with a content of between 5 and 50 wt. % and which comprises at least one compound of the general formula R & supl; —COO—(CH2-CH(Ph)—O)a-(CnH2n-xR2x-O)b-R3 (I). It is prepared by dispersing the hydrophobic silicon dioxide powder, dispersing agent and optionally pH-regulating substances and further additives in an aqueous medium. It can be employed as an additive to waterborne fillers in the automobile industry, as a coating constituent in can and coil coating processes, as an additive in water-based UV-curable formulations e.g. for wood preservation and as a constituent of protective lacquer films.

Abstract: Stable, pourable silicon dioxide dispersion, in which the average, number-related aggregate diameter of the silicon dioxide particles in dispersion is less than 200 nm, and which comprises at least 35 wt. % of a silicon dioxide powder, 3 to 35 wt. % of at least one polyol, 20 to 60 wt. % of water, 0 to 10 wt. % of an additive and a substance having an alkaline action in an amount such that a pH of 10<pH<12 is established. It can be prepared by a procedure in which silicon dioxide powder is introduced into water and a polyol in a rotor/stator machine, the pH being less than 5, and the mixture is dispersed until the current uptake of the rotor/stator machine is largely constant, and a substance having an alkaline action is subsequently added in an amount such that a pH of the dispersion of 10<pH<12 results, the substance having an alkaline reaction being added so rapidly that no gel formation takes place.

Abstract: A method and device for producing a finely divided dispersion of solids having a mean particle size of 10 nm to 10 µm, in which at least two flows of a predispersion are sprayed by means of pumps, preferably high-pressure pumps, through one nozzle each into a grinding chamber enclosed by a reactor housing onto a collision point, wherein the grinding chamber is flooded with the predispersion and the finally divided dispersion is removed from the grinding chamber by the overpressure of the predispersion continuing to flow into the grinding chamber.

Abstract: An aqueous dispersion containing pyrogenically prepared oxide particles of titanium, zinc, iron or cerium with an average particle size, expressed as the median, in the dispersion of less than 250 nm, that the particle sizes of the oxide particles in the dispersion are not distributed symmetrically and the dispersion contains, as a dispersant, at least one compound of the formula (I) and/or a maleic anhydride/acrylate copolymer of the general formula (IIa) and/or a maleate/acrylate copolymer of the general formula (IIb). It is prepared by dispersing a predispersion stream by means of a high energy mill. It can be used in sunscreen formulations.